Solar to electric energy conversion device

a technology of solar energy and conversion device, which is applied in the direction of electrolytic capacitor manufacture, final product manufacturing, sustainable manufacturing/processing, etc., can solve the problems of low efficiency, failure to achieve liquid-semiconductor hetero junction cells, and successful approaches to improve efficiency

Inactive Publication Date: 2011-02-10
MIGUEZ HERNAN +1
View PDF6 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0012]The present invention features a solar-to-electric energy conversion device based on a light absorbing electrode coupled to a nanoparticle based one dimensional photonic crystal. The function of the latter is to localize the incident light within the electrode thus enhancing the optical absorption and the power conversion efficiency of dye-sensitized, organic (polymer based or hybrid) devices. The photonic crystal comprises alternating layers possessing different index of refraction and can be easily integrated into the cell. The alternation of layers of different refractive index provides the structure with one-dimensional photonic crystal properties necessary to efficiently localize the incident light within the absorbing layer. Each layer in the multilayer photonic crystal is made of nanoparticles and its porosity allows the electrolytes and the absorbing compounds to flow through the multilayer. This ensures good electrical contact with the rest of the components, while not affecting the charge transport through the cell.
[0027]D′) depositing a multilayer having high porosity and photonic crystal properties on the polymer or polymer-fullerene blend layer deposited in step (b), thus forming a structure of alternated nanoparticle layers of controlled thickness, so that a periodic or quasi-periodic spatial modulation of a refractive index across the multilayer is achieved;

Problems solved by technology

Although stability is improved, lower values of efficiency are achieved.
Unfortunately, some of the most successful approaches developed for silicon photovoltaic devices to improve the LHE, which are based on the implementation of highly reflecting distributed Bragg reflectors, surface gratings, or a combination of both, cannot be easily realized for liquid-semiconductor hetero junction cells due to the following reasons:1. The need of electrical contact between the electrolyte and the sensitized semiconductor slab in the latter forces any potential back reflector to be porous to allow a proper flow of the liquid conductor through it.2. The processing of these cells involves deposition of solid layers from colloidal suspensions, which complicates the implementation of optical quality components within the device.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solar to electric energy conversion device
  • Solar to electric energy conversion device
  • Solar to electric energy conversion device

Examples

Experimental program
Comparison scheme
Effect test

example 1

Fabrication of the Dye-Sensitized Solar Cell 1

[0082]Dye-Sensitized Solar Cell Coupled to a 1-Dimensional Photonic Crystal with Lattice Parameter of 180±10 nm (95±5 nm SiO2-85±5 nm nc-TiO2) Presenting its Reflectance Maximum at 600 nm

[0083]A 350 nm thick transparent titanium dioxide electrode is deposited by doctor-blading onto a previously cleaned 25 mm×25 mm conducting substrate (fluorine-doped SnO2 conducting glass, Hartford Glass). The anatase particle paste the electrodes are made of was purchased from Solaronix (Ti-Nanoxide HT, Solaronix). The TiO2 layer coated glass so prepared is heated to 450° C. during 30 minutes under oxygen for sintering. On the other hand, nanocrystalline TiO2 particles are synthesised by using a procedure reported by Burnside et al, based on the hydrolysis of titanium isopropoxide followed by a peptization process under hydrothermal conditions. In our case, 20 ml of titanium isopropoxide (97% Aldrich) are added to 36 ml of Milli-Q water and stirred for ...

example 2

Fabrication of the Dye-Sensitized Solar Cell 2

[0084]Dye-Sensitized Solar Cell Coupled to a 1-Dimensional Photonic Crystal with Lattice Parameter of 140±10 nm (55±5 nm SiO2-85±5 nm nc-TiO2) Presenting its Reflectance Maximum at 450 nm

[0085]The same fabrication procedure mentioned in Example 1 is employed to build the dye-sensitized solar cell 2. In this case, the six layer periodic stack is made from silica (2 wt. % precursor solution) and titania (5 wt. % precursor solution) nanoparticles. The precursor suspensions for the spin-coating process are obtained by suspending TiO2 or SiO2 nanoparticles in a mixture of water (21 vol. %) and methanol (79 vol. %), and the rotation speed is kept at 100 rps during the spin-coating process. The IV curve corresponding to this dye-sensitized solar cell is presented in FIG. 3 (blue squares). The IV curve corresponding to a reference dye-sensitized solar cell is also shown in this graph (black circles). For this comparison, the same electrode thick...

example 3

Fabrication of the Dye-Sensitized Solar Cell

[0086]Dye-Sensitized Solar Cell Coupled to a 1-Dimensional Photonic Crystal with Lattice Parameter of 195±15 nm (110±10 nm SiO2-85±5 nm nc-TiO2) Presenting its Reflectance Maximum at 520 nm

[0087]The same fabrication procedure mentioned in Example 1 is employed to build the dye-sensitized solar cell 3. In this case, the six layer periodic stack is made from silica (3 wt. % precursor solution) and titania (5 wt. % precursor solution) nanoparticles. The precursor suspensions for the spin-coating process are obtained by suspending TiO2 or SiO2 nanoparticles in a mixture of water (21 vol. %) and methanol (79 vol. %), and the rotation speed is kept at 100 rps during the spin-coating process. The IV curve and the specular reflectance spectrum corresponding to this dye-sensitized solar cell are presented in FIG. 6a (circles) and 6b, respectively. In FIG. 6b is also plotted the absorption spectrum of the ruthenium based dye (black solid line, in ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention features a solar-to-electric energy conversion device based on a light absorbing electrode coupled to a one-dimensional nanoparticle based photonic crystal. The function of the latter is to localize the incident light within the electrode thus enhancing the optical absorption and the power conversion efficiency of the so called dye-sensitized and organic (polymer based or hybrids) cell. The photonic crystal comprises alternating layers possessing different index of refraction and can be easily integrated into the cell.

Description

FIELD OF THE INVENTION[0001]The present invention relates to a solar-to-electric energy conversion device having a light absorbing electrode coupled to a porous photonic crystal or multilayer Bragg reflector. The porous reflecting element is used to enhance the power conversion efficiency of the solar cell device by selectively increasing the optical absorption in the electrode.BACKGROUND OF THE INVENTION[0002]The research on different solar-to-electric energy conversion devices made of materials alternative to silicon has been boosted in recent years for a number of reasons such as the search for lower cost processes or added value features, such as transparency. Among them, one of the devices that have shown higher efficiency is dye-sensitized solar cells (DSSC), also known as Grätzel cells, U.S. Pat. No. 5,084,365. The DSSC combine a solid wide band gap semiconductor with a liquid ionic conductor. The former usually consists of one electrode made of a layer of a few micrometers o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01L31/0232H01L31/18
CPCH01G9/2031H01G9/2036H01G9/2059H01L51/426Y02E10/542H01G9/209H01L51/0086Y02P70/50H10K85/344H01G9/0029
Inventor MIGUEZ, HERNANCOLODRERO, SILVIA
Owner MIGUEZ HERNAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com