Use of pre-coated mat for preparing gypsum board

a technology of gypsum board and fiber mat, which is applied in the field of use of pre-coated fiber mat for making fiber matfaced gypsum board, can solve the problems of insufficient strength of the board to satisfy the supporting function, insufficient tensile strength of the board, and inability to meet the requirements of the supporting function

Inactive Publication Date: 2009-04-02
SMITH RUSSELL +1
View PDF101 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this construction the flow of gypsum into the mat during preparation of the board is unimpeded.
If the bond does not have a sufficient strength, the board is not strong enough to satisfy its supporting function.
Indeed, the board of this published application has not been used in such situations and the bond between the pre-coated mat and the gypsum core in the disclosed board would not inherently have the necessary tensile strength for such uses.
As described, if too much glass mat is exposed such that the gypsum cannot cover it entirely, the application speculates that the resultant board is unacceptable.
Conversely, if not enough glass fibers are left exposed, the '079 application indicates that the resulting board also is not acceptable.
The '079 application does not address the situation where the gypsum board in intended to be used in circumstances where it is required to support a substrate such as tiles, insulating material or other exterior finishing materials.
In particular, unless the extent of coating penetration in the pre-coated mat is controlled within a much smaller window and the process conditions for subsequently making the gypsum board are properly observed, the resulting bond between the pre-coated glass mat and the gypsum core does not have the required tensile strength for supporting tiles, insulating material or other construction materials, such as exterior finishing materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Use of pre-coated mat for preparing gypsum board
  • Use of pre-coated mat for preparing gypsum board
  • Use of pre-coated mat for preparing gypsum board

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0094]Pre-coated fibrous mats have been prepared by first preparing the following coating composition.

IngredientsAmounts, wt. %Aqueous acrylic latex (45% solids)18.7(NeoCar ® 820)Limestone65.3(GFP 102 from Global Stone Filler Products)Ethyl hydroxyethyk cellulose thickener / stabilizer0.04Bermocoll 230FQAcrylate thickeners0.19, 0.19Paragum 501, 109Colorant0.47Englehard W 1241Ammonia0.37Added water14.74

[0095]The aqueous coating composition has been applied to Johns Manville 7594 fiberglass mat at application rates of about 30 grams per square foot (about 66 pounds per 1000 square feet). The wet coating composition was dried. The dried basis weight of the coating was about 22 grams per square foot (about 48 pounds per 1000 square feet).

example 2

[0096]Pre-coated fiberglass mat obtained in the manner of Example 1 was used to prepare gypsum board panels. The pre-coated mat had a thickness of about 35 mils and a porosity of about 10 seconds.

[0097]Continuous length boards were made from a gypsum slurry containing about 55% percent by weight of gypsum hemi-hydrate and the pre-coated mats on a conventional wallboard machine. The slurry was deposited on one continuous sheet of the coated mat, which was advanced at a rate of about 185 linear feet per minute, sufficient to form ⅝th inch thick boards, while a continuous sheet of Johns Manville 8802 fibrous mat was deposited onto the opposite surface of the gypsum slurry. Drying of the gypsum boards was accelerated by heating the composite structures in an oven at about 600° F. for about thirty minutes and until the boards are almost dry and then at about 250° F. for about fifteen minutes until they are dried completely. The densities of the coated mat-faced boards were determined to ...

example 3

[0099]Selected gypsum boards made with pre-coated mats were tested to assess the bond strength between the pre-coated mat facer and the gypsum core.

[0100]In order to support tiles, insulating material or other construction materials, such as exterior finishing materials from the pre-coated mat surface of the board, the bond between the gypsum core and the mat facer must have a sufficient strength. In particular, it has been determined that the tensile strength of that bond should be at least 16 psi when tested in accordance with the following procedure.

[0101]A 5.5 inch square sample for testing is prepared from a gypsum board. An expanded polystyrene board (EPS) then is adhered to the gypsum board sample. An EPS board, nominal 2 pound, one inch thick (typical of EPS insulation), cut into a 3.5 inch square, is suitable. A suitable adhesive is a 1:1 mixture of Type I Portland cement and Dryvit Primus adhesive mixed with water to a suitable consistency for applying it to EPS board. Thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
wt. %aaaaaaaaaa
Login to View More

Abstract

A gypsum board which comprises a set gypsum core sandwiched between and faced with fibrous mats, wherein a free surface of one of said mats is pre-coated with a combination of a mineral pigment, optionally an inorganic adhesive binder and an organic binder, preferably a hydrophobic, UV resistant polymer latex adhesive binder applied to said surface as an aqueous coating composition, said aqueous coating composition upon drying and setting providing a pre-coated mat satisfying certain morphology requirements.

Description

FIELD OF THE INVENTION[0001]This invention relates to the use of a pre-coated fiber mat for making fiber mat-faced gypsum board, for example, a gypsum board faced with a glass fiber mat. The invention more particularly relates to the fiber mat-faced gypsum board that is prepared with the pre-coated fiber mat. The coating on the pre-coated mat comprises a dried aqueous mixture of a mineral pigment or filler, an organic binder, preferably comprised of a hydrophobic, UV-resistant polymer latex adhesive; and, optionally a second binder comprised of an inorganic adhesive, wherein the dried coating satisfies certain coating morphology requirements.[0002]The present invention is based on the discovery that in order to obtain a gypsum board with certain desired physical strength characteristics, the pre-coated mat used to prepare the gypsum board product must satisfy a particular set of structural properties and the process for making the board must produce the proper interface between the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): D21H13/40D21H17/63D21H17/60D21H17/61D21H17/36D21H17/59B28B19/00B28B23/00B32B13/14C03C25/28D06N3/00D06N7/00E04C2/04
CPCB28B19/0092B28B23/0006B32B13/14C03C25/1095D06N3/0063E04C2/043Y10T428/24992D06N2209/1678D06N3/0022D06N3/042D06N2205/023Y10T428/25D06N2209/142Y10T442/623Y10T442/2992Y10T442/665Y10T442/361Y10T428/249921Y10T428/249932Y10T442/2066Y10T442/645Y10T442/3797Y10T442/699Y10T442/2008B32B17/02B32B2307/7265B32B2419/00B32B2260/044B32B2260/021
Inventor SMITH, RUSSELLRANDALL, BRIAN
Owner SMITH RUSSELL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com