Skimming tool
A skimmer and micropowder technology, which is applied to blast furnace parts, blast furnaces, furnace types, etc., can solve the problems of lower labor productivity, poor operating environment, and influence on punctual tapping, so as to improve labor productivity, reduce the cost per ton of iron, The effect of prolonging the service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] Dense corundum or brown corundum: 45%, silicon carbide: 31%, spherical pitch: 2.5%, pure calcium aluminate cement: 3%, α-Al 2 o 3 Micropowder: 9%, uf-SiO 2 Micropowder: 2%, metal aluminum powder: 1%, metal silicon powder: 2%, composite additive: 0.5%, water: 4%. After the material is prepared according to the above ratio, it is directly poured into the mold, and then fired to form a prefabricated skimmer that can be used directly, and the user does not need to ram before the furnace when using it. And in the case of achieving a better effect than the original, its thickness is much smaller than the original, saving raw material resources.
[0012] The volume of the blast furnace generally has various specifications such as 150m3, 300m3, 450m3, 700m3, etc. The volume of the skimmer should correspond to the volume of the blast furnace. increased, but the weight percentages of the various components remained the same.
[0013] Among them, dense corundum or brown corund...
Embodiment 2
[0020] Dense corundum or brown corundum: 43%, silicon carbide: 33%, spherical pitch: 3%, pure calcium aluminate cement: 2.7%, α-Al 2 o 3 Micropowder: 9.8%, uf-SiO 2 Micropowder: 2%, metal aluminum powder: 0.5%, metal silicon powder: 1%, compound additive: 0.3%, water: 4.7%. After the material is prepared according to the above ratio, it is directly poured into the mold, and then fired to form a prefabricated skimmer that can be used directly. The user does not need to ram before the furnace when using it. And in the case of achieving a better effect than the original, its thickness is much smaller than the original, saving raw material resources.
Embodiment 3
[0022] Dense corundum or brown corundum: 48%, silicon carbide: 29%, spherical pitch: 2%, pure calcium aluminate cement: 2.5%, α-Al 2 o 3 Micropowder: 8%, uf-SiO 2 Micropowder: 2.5%, metal aluminum powder: 1.5%, metal silicon powder: 2.6%, composite additive: 0.4%, water: 3.5%. After the material is prepared according to the above ratio, it is directly poured into the mold, and then fired to form a prefabricated skimmer that can be used directly. The user does not need to ram before the furnace when using it. And in the case of achieving a better effect than the original, its thickness is much smaller than the original, saving raw material resources.
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
flexural strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com