Molten steel composite refining agent

A compound refining agent and refining agent technology, applied in the field of molten steel compound refining agent, can solve the problems of ineffective reduction of smelting cost, high price, unfavorable environmental protection, etc. effect of the problem

Inactive Publication Date: 2006-11-08
CHONGQING UNIV
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, some refining agents contain quartz CaF 2 ingredients, not conducive to environmental protection
Some refining agents are relatively expensive and cannot effectively reduce the cost of smelting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The molten steel composite refining agent of the present invention is composed of a variety of deoxidizing alloys and refining agent base materials. The deoxidizing alloy is composed of Ca, Si, Ba, Al, and C; the proportions of the deoxidizing alloy are as follows: Ca8-18%, Si35-45% , Ba7~17%, Al10~25%, C15~35%; refining agent base material consists of the following materials, CaO, AL 2 O 3 , SiO 2 , MgO, the ratio of each component is as follows: CaO50~65%, Al 2 O 3 30~45%, SiO 2 2~6%, MgO5~10%. The ratio of deoxidizing alloy to refining agent base material is as follows, deoxidizing alloy: refining agent base material is 0.75-3:1, and the weight ratio of deoxidizing alloy is generally 40-80%.

[0015] The production process of the molten steel composite refining agent of the present invention:

[0016] Deoxidizing alloy: broken, grain size 1~5mm.

[0017] Refining agent base material: pre-melted, broken. The particle size is 1~5mm.

[0018] Finished product: Deoxidizing a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The composite molten steel refining agent consists of deoxidizing alloy and refining agent base material in the weight ratio of 0.75-3 to 1. The deoxidizing alloy consists of Ca 8-18%, Si 35-45%, Ba 7- 17%, Al 10-25% and C 15-35%; and the refining agent base material consists of CaO 50-65%, Al2O3 30-45%, SiO 6-22% and MgO 5-10%. The composite molten steel refining agent of the present invention may be used as the pre-deoxidizing agent or cinder pushing modifier, can avoid the formation of SiO2, AL2O3 and other high smelting point solid deoxidizing products, and is favorable to the formation of low smelting point composite compounds. The present invention has high deoxidizing effect, low deoxidizing cost, and no fluorine content resulting in environment friendship.

Description

Technical field [0001] The invention relates to an auxiliary additive material used in the steelmaking process of the metallurgical industry, in particular to a molten steel composite refining agent used as a pre-deoxidizer or top slag modifier added to a ladle during steel tapping. Background technique [0002] With the increase in the quality requirements of molten steel, especially the widespread use of high-performance and high-quality steel, higher requirements are put forward for auxiliary materials in the steelmaking process. The invented molten steel composite refining agent is a new type of metallurgical auxiliary material that integrates the refining functions of molten steel, steel slag deoxidation, and adsorption of inclusions. It is added into the ladle when steel is tapped, which can play the role of alloy deoxidation. Adding to the slag surface of the ladle can deoxidize and modify the slag of the converter and electric furnace, and effectively change a series of q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/06
Inventor 唐萍文光华李万绪
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com