Laminate film

一种层合膜、透明层的技术，应用在涂层、分层产品、合成树脂层状产品等方向，能够解决难以确保涂层特性和意匠性、加工性和意匠性降低、排列混乱等问题，达到优异涂层特性和意匠性、仿形性优异、耐冲击性优异的效果

Inactive Publication Date: 2005-09-14
นิปปอน เพนท์ ออโตโมทีฟ โคทติ้งส์ โค แอลทีดี
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, in the conventional laminated films mentioned above, it is difficult to ensure processability and originality while ensuring the above-mentioned coating properties.
That is to say, conventional laminated films have the following problems: if the focus is on ensuring the coating properties, the workability and originality will be reduced, and if the workability is emphasized, it will be difficult to ensure the coating properties and the originality
However, if emphasis is placed on flexibility as mentioned above, it is difficult to ensure the coating properties of the laminated film
In addition, there is a problem that it is difficult to ensure the originality of the laminated film due to the disorder in the arrangement of the glossy material, etc.
[0010] Therefore, conventionally, there has been a problem that, if the workability of the object to be coated with a laminated film is to be secured, it is impossible to obtain a coating of a level higher than that achieved by the above-mentioned spray coating method, dip coating method, etc. Character and originality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0118] Hereinafter, the present invention will be described with reference to examples and comparative examples, but the present invention is not limited thereto.

[0119] In addition, the measurement of the weight-average molecular weight Mw, the calculation of the glass transition temperature, the calculation of the hydroxyl value (OHV), the evaluation of the transparent layer (B), the evaluation of the laminated film, the acrylic polymer (B1 ) manufacture.

[0120] [Measurement of weight average molecular weight Mw]

[0121] The weight-average molecular weight Mw of each polymer was measured in terms of standard polystyrene using gel permeation chromatography. And, use Gelpack R400, R450, R400M (all from Hitachi Chemical Industry Co., Ltd.) as a column, use tetrahydrofuran as an eluent, measure with Hitachi L6000 type high-speed liquid chromatography, use Hitachi L3350 type differential refractometer as Detector. In addition, the measurement conditions are: column temper...

manufacture example

[0171]

[0172] In the reaction vessel, add the solvent (I) in the ratio shown in Table 1 and Table 2 respectively, and heat to 110°C while stirring under a nitrogen atmosphere. Then, under the temperature condition of 110 DEG C, in the above-mentioned solvent (I) of reaction container, add dropwise as shown in table 1, the unsaturated compound (B1a ), a mixed solution (II) of 2,3-epoxypropyl methacrylate, an unsaturated compound (B1b), and parbutill (registered trademark) ○ (manufactured by NOF Corporation). After the dropwise addition was completed, the reaction was carried out at a temperature of 110° C. for 1 hour, and then the mixed solvent (III) containing various solvents in proportions shown in Table 1 and Table 2 was added dropwise within 1 hour. Then, heat to 145°C, react for another 2 hours, then cool to below 110°C, add the solvent (IV) in the proportion shown in Table 1 and Table 2, and obtain the precursor as the epoxy group-containing copolymer (B1c). Body (1...

Embodiment 1～13

[0184]

[0185] In a container equipped with a stirrer, the resins (1) to (12) produced in the above manner and the urethane oligomer (B2 ) UV7200B (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., solid weight fraction 70%). Next, 100 g of Irgacure (IRGACURE)-819 (IRGACURE)-819 ( Chiba Special Chemical Co., Ltd., solid weight fraction 100%) 3 g, Chiba Bin 400 (manufactured by Chiba Special Chemical Chemical Co., Ltd., solid weight fraction 100%) as an ultraviolet absorber (UVA) 2 g, As an agent (HALS), 1 g of Chiubin 292 (manufactured by Chiba Specialty Chemicals Co., Ltd., solid weight fraction: 100%) was added, and 100 g of methyl isobutyl ketone (hereinafter referred to as MIBK) was added. These ingredients were stirred for 30 minutes to obtain a clearcoat solution. When preparing the clear paint solution, the compatibility of each component of the clear paint composition was evaluated. The results are shown in Table 6.

[0186]

[0187] In a container...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The laminating film has a clear layer (B) comprising an acrylic polymer (B1). The acrylic polymer (B1) has long-side-chain double bonds derived from a long-chain unsaturated carboxylic acid having a molecular weight of at least 150 and short-side-chain double bonds derived from a short-chain unsaturated carboxylic acid having a molecular weight of below 150. The weight-average molecular weight of the acrylic polymer (B1) is in the range of 50,000 to 500,000. To provide a laminating film which has design properties and coating film performances at least equivalent to those realized by e.g., spraying or dipping, exhibits a high ability to follow the shape of a molding, and realizes good decoration on the molding.

Description

field of invention [0001] The present invention relates to a laminated film used when modifying a shaped article by a film modification method. Background of the invention [0002] Molded products such as metal products, plastic products, inorganic products, and wood products are sometimes subjected to a finishing treatment to form a coating on the surface of the molded product for the purpose of imparting durability and artistic characteristics including color. Since the material and shape of the finished molded article (hereinafter referred to as the object to be painted) are various, in order to form a coating on the concave part and gap of the object to be painted easily, spraying method and dip coating method can be obtained. a wide range of applications. [0003] In general, many coating layers formed by coating an object to be coated are laminated films obtained by laminating a plurality of layers. For example, the above-mentioned laminated film is composed of a bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/02B32B27/00B32B27/06B32B27/30B32B27/40C08J7/043C08J7/046
CPCC08J7/042Y10T428/31573Y10T428/31855Y10T428/31909Y10T428/31551C08J2433/14Y10T428/31554C09D133/14C08J7/043C08J7/046
Inventor 长谷高和齐藤芳彦高桥孝一小岛靖新谷健一滨田启司
Owner นิปปอน เพนท์ ออโตโมทีฟ โคทติ้งส์ โค แอลทีดี
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com