Locally reinforced heating method and device for hot rolling steel billet before discharging

A technology of local strengthening and heating method, which is applied in the field of hot-rolled billet reheating, can solve problems affecting steel rolling production, biting difficulties, quality problems, etc., to improve product rolling quality, improve rolling temperature uniformity, and reduce waste products rate effect

Inactive Publication Date: 2004-02-11
SHANGHAI INST OF TECH
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such a temperature difference will cause rolling quality problems for steel types (silicon steel, etc.) that require high rolling temperature uniformity, and even difficulty in biting (such as when rolling wire rods), which will affect the rolling production.
At present, there is still no method and device that can solve this problem.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Locally reinforced heating method and device for hot rolling steel billet before discharging
  • Locally reinforced heating method and device for hot rolling steel billet before discharging
  • Locally reinforced heating method and device for hot rolling steel billet before discharging

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] This method is based on the calculation of the temperature distribution requirements of the steel billet out of the furnace and the calculation of the time for the local intensive heating of the steel billet in the furnace. The details are as follows:

[0023] 1. Calculation of temperature distribution requirements of the furnace

[0024] The temperature distribution requirements of the steel billet can be obtained by numerical calculation according to the following heat transfer model: λ ∂ 2 T ∂ X 2 - ϵσ b 1 ( T 4 - T ∞ 4 ) = ρc ∂ ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The local heating process for reinforced heating rolled steel billet includes the following steps: calculating the temperature distribution of discharged steel billet; calculating the reinforced heating time for the steel billet inside the furnace; establishing local reinforced heating area or chamber in the last end of the heating furnace based on the calculated data and heating the local 200-300 mm long areas in two ends of the steel billet at the temperature 80-120 deg.c higher than the average furnace temperature for 20-30 sec. The local heating apparatus features its at least one pair of burning nozzles installed on two side walls or top of the local heating area for the reinforced heating. The present invention can reduce the surface temperature difference in the steel billet to be rolled, raise the rolling temperature homogeneity and raise rolling quality.

Description

technical field [0001] The invention relates to a reheating of a hot-rolled steel slab, in particular to a method and device for locally intensified heating of a hot-rolled steel slab before being discharged from the furnace. Background technique [0002] The steel billet needs to be heated before hot rolling. According to the existing technology, it is hoped that the temperature of the steel billet should be heated as uniformly as possible before the heating ends. However, the steel slab with uniform temperature out of the furnace is transported to the rolling mill through the roller table, and due to heat dissipation, the original steel slab with uniform temperature becomes uneven. In this phenomenon, the longer the conveying distance, the greater the cooling intensity of the surrounding environment of the roller table, and the more uneven the temperature of the billet when it enters the rolling mill. figure 1 , figure 2 It is the measured surface temperature distributi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/34C21D9/70
Inventor 郑跃伟苑安民
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap