TiC/AI high-damp composite material and preparing method thereof
A composite material and preparation technology, which is applied in the field of high-damping composite materials and its preparation technology, can solve the problems of small contribution to the strength of graphite particle materials and the inability to realize the effective combination of structure and function materials, and achieve good wear resistance , low expansion coefficient, high specific strength effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] The preparation composition is Cu5.3%, Ti0.15%, Mn0.3%, Cd0.25%, V0.3%, Zr0.2%, B0.06%, of which TiC0.1%, and the rest is Al for high damping Composite materials, the process is as follows:
[0019] After the aluminum ingot is melted, add KCl, NaCl, Na 3 AlF 6 Cover with covering agent, melt temperature reaches 900°C, add high-damping composite material prefabricated blocks that have been heat-preserved and dried at 250°C for 2 hours, and after the prefabricated blocks are completely melted, use a stirring device to stir at 400rpm for 10 minutes at a stirring temperature of 900°C . After adding Cu, Al-Ti, Al-Mn, Cd, V, Zr, B to adjust the chemical composition, after standing at 780°C for 10 minutes, pour it into the ingot mold to obtain the TiC / Al high damping composite material. The obtained composite material was cut into a damping sample of 50 mm × 5 mm × 1 mm, and the damping value Q of the prepared in-situ self-generated TiC / Al high damping composite material wa...
Embodiment 2
[0021] The preparation composition is Cu4.8%, Ti0.35%, Mn1%, wherein TiC10%, the rest is Al high damping composite material, the process is as follows:
[0022] After the aluminum ingot is melted, add KF and MgCl 2 Covered with KCl covering agent, the melt temperature reaches 790°C, add high damping composite material prefabricated blocks that have been heat-preserved and dried at 200°C for 3.5 hours, and after the prefabricated blocks are completely melted, stir with a stirring device at a stirring speed of 300rpm for 20min at a stirring temperature of 790°C. After adding Cu, Al-Ti, Al-Mn alloys to adjust the chemical composition, after standing at 730°C for 20 minutes, pour it into the ingot mold to obtain the in-situ self-generated TiC / Al high damping composite material. The obtained composite material was cut into a damping sample of 50 mm × 5 mm × 1 mm, and the damping value Q of the prepared high damping composite material was measured by DMTA -1 =9×10 -3 ~48×10 -3 ;...
Embodiment 3
[0024] The preparation composition is Cu4%, Ti0.2%, Mn0.6%, wherein TiC20%, the rest is Al high damping composite material, the process is as follows:
[0025] Add MgCl after the aluminum ingot is melted 2 、Na 2 SiF 6 , NaF covering agent, and the melt temperature reaches 680°C. Add high-damping composite material prefabricated blocks that have been heat-preserved and dried at 150°C for 5 hours. After the prefabricated blocks are completely melted, use a stirring device to stir at a speed of 200rpm for 30 minutes. The stirring temperature is 680°C. After adding Cu, Al-Ti, Al-Mn alloy to adjust the chemical composition, after standing at 680°C for 30 minutes, pour it into the ingot mold to obtain the TiC / Al high damping composite material. The obtained composite material was cut into a damping sample of 50 mm × 5 mm × 1 mm, and the damping value Q of the prepared high damping composite material was measured by DMTA -1 =10×10 -3 ~49×10 -3 ; Tensile strength at room tempera...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com