Manufacturing method of ceramic ornament inlaid with metal structure

A manufacturing method and metal structure technology, applied in decorative structures, ceramic molding machines, manufacturing tools, etc., can solve the problems of poor use feeling of ceramic ornaments, and achieve the effects of high aesthetics, enhanced structure, and long service life

Pending Publication Date: 2022-07-22
福建省德化县泉艺陶瓷有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a method for making ceramic ornaments inlaid with metal structures, mainly to solve the problems caused by the existing ordinary ceramic ornaments due to their material, time, temperature and maintenance methods. The influence of service life and appearance makes ceramic ornaments extremely poor for people to use and cannot meet people's requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of ceramic ornament inlaid with metal structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] refer to figure 1 , a method for making a ceramic ornament inlaid with a metal structure, comprising the following steps:

[0037] S1: Prepare materials, take porcelain stone from the mining area, crush it manually with a hammer to the size of an egg, and then use a water masher to beat it into powder, wash it out, remove impurities, and make a brick-shaped mud block after precipitation. Then mix the mud with water;

[0038] S2: Pull the blank, throw the mud ball on the center of the turntable of the reel car, and pull out the shape of the blank with the flexion and extension of the technique, and complete the first process of forming;

[0039] S3: printing blank, the shape of the stamping die is formed by rotating according to the inner shape of the blank, cover the semi-dry blank on the mold, press the outer wall of the blank evenly, and then demould;

[0040] S4: Inlay, after demolding is completed, insert the metal to be inlaid into the embryo. The metal structure...

Embodiment 2

[0050] refer to figure 1 , a method for making a ceramic ornament inlaid with a metal structure, comprising the following steps:

[0051] S1: Prepare materials, take porcelain stone from the mining area, crush it manually with a hammer to the size of an egg, and then use a water masher to beat it into powder, wash it out, remove impurities, and make a brick-shaped mud block after precipitation. Then mix the mud with water;

[0052] S2: Pull the blank, throw the mud ball on the center of the turntable of the reel car, and pull out the shape of the blank with the flexion and extension of the technique, and complete the first process of forming;

[0053] S3: printing blank, the shape of the stamping die is formed by rotating according to the inner shape of the blank, cover the semi-dry blank on the mold, press the outer wall of the blank evenly, and then demould;

[0054] S4: Inlay, after demolding is completed, insert the metal to be inlaid into the embryo. The metal structure...

Embodiment 3

[0064] refer to figure 1 , a method for making a ceramic ornament inlaid with a metal structure, comprising the following steps:

[0065] S1: Prepare materials, take porcelain stone from the mining area, crush it manually with a hammer to the size of an egg, and then use a water masher to beat it into powder, wash it out, remove impurities, and make a brick-shaped mud block after precipitation. Then mix the mud with water;

[0066] S2: Pull the blank, throw the mud ball on the center of the turntable of the reel car, and pull out the shape of the blank with the flexion and extension of the technique, and complete the first process of forming;

[0067] S3: printing blank, the shape of the stamping die is formed by rotating according to the inner shape of the blank, cover the semi-dry blank on the mold, press the outer wall of the blank evenly, and then demould;

[0068] S4: Inlay, after demolding is completed, insert the metal to be inlaid into the embryo. The metal structure...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic manufacturing, and discloses a manufacturing method of a ceramic ornament inlaid with a metal structure, which comprises the following steps: S1, preparing materials: taking chinastone from a mining area, firstly, manually breaking the chinastone into blocks in the size of an egg by using a hammer, pounding the chinastone into powder by using a water-powered hammer, washing, removing impurities, precipitating, and then manufacturing into brick-shaped mud blocks, then blending mud blocks with water; s2, throwing the blank, namely throwing the mud pie to the center of a turntable of a windlass, and drawing the mud pie into a pattern of the blank along with the flexion, extension, retraction and release of a technique, so as to complete a first process of forming; by means of the method, the ceramic ornament can be more stereoscopic and attractive, the service life of the ceramic ornament can be longer, new and featured works can be created, the ceramic ornament can have more distinctive personality, the shadow effect can be improved by means of various different technologies, and the effect of the ceramic ornament can be improved. And the stereoscopic impression of the ornamentation is highlighted.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a manufacturing method of a ceramic ornament inlaid with a metal structure. Background technique [0002] Ceramics are materials and various products made of clay as the main raw material and various natural minerals through crushing, kneading, molding and calcining. People call a kind of clay made of clay and fired at high temperature in a special kiln called ceramics, which is a general term for pottery and porcelain. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. [0003] Ceramic ornaments are more and more popular because of their exquisiteness and high ornamental value, but ordinary ceramic ornaments will affect their service life and appearance due to their material, time, temperature and maintenance methods. The ceramic ornaments give people a very poor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B44C3/04B44C1/26B44C1/22B28B1/02B28B11/00B28B11/24
CPCB44C3/04B44C1/26B44C1/225B28B1/02B28B11/001B28B11/243
Inventor 张泉德
Owner 福建省德化县泉艺陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com