Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Spandex-containing polyester foam tackifying spinning two-dimensional hollow fiber and process

A fiber technology, spandex technology, applied in the direction of fiber chemical characteristics, hollow filament manufacturing, textiles and papermaking, etc., can solve the problems of poor hygroscopicity of hollow fibers, single raw material, high production cost, etc., to improve water absorption performance, improve softness, Improve the effect of high elasticity

Pending Publication Date: 2022-05-13
扬州天富龙科技纤维有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the two-dimensional hollow fiber in the existing market is produced by bottle flakes, and the raw material is single, which not only leads to poor hygroscopicity of the hollow fiber, but also high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A polyester foam viscosity-spun two-dimensional hollow fiber containing spandex, including a hygroscopic melt made of spandex and a hygroscopic agent, the hygroscopic melt and modified PET are compositely sprayed to obtain a finished two-dimensional hollow fiber;

[0024] The hygroscopic melt includes, measured in parts by weight: 70 parts of spandex chips, 15 parts of magnesium sulfate micropowder;

[0025] The modified PET includes the following parts by weight: 70 parts of terephthalic acid, 34 parts of ethylene glycol, 1.8 parts of titanium dioxide, 1.4 parts of catalyst, 2.1 parts of stabilizer, 20 parts of sodium benzoic acid-3,5-disulfonate part, 20 parts of polyethylene glycol.

[0026] The catalyst is one or more of antimony trioxide, antimony ethylene glycol or antimony acetate, and the stabilizer is one or more of triphenyl phosphate, trimethyl phosphate or trimethyl phosphate.

[0027] A kind of spandex-containing polyester foam viscosity-increasing spinnin...

Embodiment 2

[0036] A polyester foam viscosity-spun two-dimensional hollow fiber containing spandex, including a hygroscopic melt made of spandex and a hygroscopic agent, the hygroscopic melt and modified PET are compositely sprayed to obtain a finished two-dimensional hollow fiber;

[0037] The hygroscopic melt includes, measured in parts by weight: 75 parts of spandex chips, 25 parts of magnesium sulfate micropowder;

[0038]The modified PET includes the following parts by weight: 75 parts of terephthalic acid, 41 parts of ethylene glycol, 1.85 parts of titanium dioxide, 1.5 parts of catalyst, 2.3 parts of stabilizer, 25 parts of sodium benzoic acid-3,5-disulfonate Parts, 25 parts of polyethylene glycol. Wherein, the catalyst is one or more of antimony trioxide, ethylene glycol antimony or antimony acetate, and the stabilizer is one or more of triphenyl phosphate, trimethyl phosphate or trimethyl phosphate kind.

[0039] A kind of spandex-containing polyester foam viscosity-increasing ...

Embodiment 3

[0046] A polyester foam viscosity-spun two-dimensional hollow fiber containing spandex, including a hygroscopic melt made of spandex and a hygroscopic agent, the hygroscopic melt and modified PET are compositely sprayed to obtain a finished two-dimensional hollow fiber;

[0047] The hygroscopic melt includes, measured in parts by weight: 85 parts of spandex chips, 30 parts of magnesium sulfate micropowder;

[0048] The modified PET includes the following parts by weight: 85 parts of terephthalic acid, 48 parts of ethylene glycol, 1.9 parts of titanium dioxide, 1.7 parts of catalyst, 2.5 parts of stabilizer, 30 parts of sodium benzoic acid-3,5-disulfonate part, 30 parts of polyethylene glycol. Wherein, the catalyst is one or more of antimony trioxide, ethylene glycol antimony or antimony acetate, and the stabilizer is one or more of triphenyl phosphate, trimethyl phosphate or trimethyl phosphate kind.

[0049] A kind of spandex-containing polyester foam viscosity-increasing s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
number of curlsaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spandex-containing polyester foam tackifying spun two-dimensional hollow fiber and a process, belongs to the technical field of chemical fibers, and solves the problems of poor water absorption, poor softness and weak rebound resilience of a composite fiber in the prior art, and the spandex-containing polyester foam tackifying spun two-dimensional hollow fiber comprises a moisture absorption melt prepared from spandex and a moisture absorbent, the moisture absorption melt and modified PET are subjected to composite spinning to obtain the finished product two-dimensional hollow fiber. Through the composite spinning assembly, the spandex melt and the modified PET melt are made into the hollow two-dimensional composite fiber, and the physical properties of high elasticity, high strength, wear resistance, corrosion resistance and the like of the composite fiber are improved; the moisture absorbent is added and matched with the fiber cavity, so that the requirements of the fiber for rapidly absorbing, diffusing and volatilizing moisture are met, the water absorption performance of the fiber is remarkably improved, the softness of the fiber is improved by using the flexible group, and the comfort degree of the fiber in contact with skin is improved; the whole process is simple, melt viscosity is tackified and homogenized, spandex is effectively utilized to keep elasticity, and the rebound resilience of the fiber is guaranteed.

Description

technical field [0001] The invention belongs to the technical field of chemical fibers, and in particular relates to a two-dimensional hollow fiber and a process for viscosifying polyester foam containing spandex. Background technique [0002] With the rapid development of science and technology and the continuous improvement of people's living standards, people's requirements for the practical functions of clothing are not only to protect the body from the cold, but also in many ways: from comfort to health care, from safety to hygiene, from convenience for storage and It can be processed to suit different climates and environments, from adapting to the rhythm of life of modern people to adapting to the way of life of modern people. Especially in recent years, climate change is impermanent, and the daily difference of temperature is bigger, and people often because change clothes not in time, and cause the frequent outbreak of many diseases, this has just proposed higher re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01F8/16D01F1/08D01F1/10
CPCD01F8/14D01F8/16D01F1/08D01F1/10
Inventor 殷峥潘道东夏军缪兴江
Owner 扬州天富龙科技纤维有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com