Wind power blade ice melting and inhibiting agent based on exothermic reaction and preparation method thereof

A technology of wind power blades and exothermic reaction, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of slow deicing speed, poor deicing effect, and difficulty in spraying the surface of blades on a large area

Pending Publication Date: 2022-01-18
XIAN THERMAL POWER RES INST CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the technical problem that the anti-icing agent in the prior art has poor deicing effect under severe icing conditions, it will corrode the surface coating of the blade, the deicing speed is slow, and it is difficult to spray on the surface of the blade in a large area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] An ice-melting and deicing agent for wind power blades based on an exothermic reaction and a preparation method thereof. The deicing and deicing agent comprises the following components: a solid component A and a liquid component B, wherein the solid component A contains sodium hydroxide and activated carbon Powder; Liquid Component B contains acetic acid and ethylene glycol (glycerol).

[0027] In the solid component A, the sodium hydroxide content is 10 parts, and the purity is more than 96%;

[0028] In the solid component A, the content of activated carbon is 20-30 parts; the particle size range is 100-180um;

[0029] In the liquid component B, the content of acetic acid is 15 parts, and its concentration is above 99%;

[0030] In the liquid component B, the content of ethylene glycol (glycerol) is 5-10 parts;

[0031] A self-heating material-based wind power blade surface deicing agent and a preparation method thereof, the steps are as follows:

[0032] (1) Weig...

Embodiment 1

[0036] An ice-melting and deicing agent for wind power blades based on an exothermic reaction and a preparation method thereof. The deicing and deicing agent comprises the following components: a solid component A and a liquid component B, wherein the solid component A contains sodium hydroxide and activated carbon Powder; Liquid Component B contains acetic acid and ethylene glycol (glycerol).

[0037] In the solid component A, the sodium hydroxide content is 10 parts, and the purity is more than 96%;

[0038] In the solid component A, the activated carbon content is 20 parts; the particle size range is 180um;

[0039] In the liquid component B, the content of acetic acid is 15 parts, and its concentration is above 99%;

[0040] In the liquid component B, the content of ethylene glycol is 5 parts;

[0041] A self-heating material-based wind power blade surface deicing agent and a preparation method thereof, the steps are as follows:

[0042] (1) Weigh solid component A sodi...

Embodiment 2

[0046] An ice-melting and deicing agent for wind power blades based on an exothermic reaction and a preparation method thereof. The deicing and deicing agent comprises the following components: a solid component A and a liquid component B, wherein the solid component A contains sodium hydroxide and activated carbon Powder; Liquid Component B contains acetic acid and ethylene glycol (glycerol).

[0047] In the solid component A, the sodium hydroxide content is 10 parts, and the purity is more than 96%;

[0048] In the solid component A, the activated carbon content is 30 parts; the particle size range is 100um;

[0049] In the liquid component B, the content of acetic acid is 15 parts, and its concentration is above 99%;

[0050] In the liquid component B, the glycerol content is 10 parts;

[0051] A self-heating material-based wind power blade surface deicing agent and a preparation method thereof, the steps are as follows:

[0052] (1) Weigh the solid component A sodium hydr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wind power blade ice-melting and ice-inhibiting agent based on exothermic reaction and a preparation method thereof. The ice-melting and ice-inhibiting agent comprises a solid component A and a liquid component B. The solid component A comprises sodium hydroxide powder and activated carbon; the liquid component B comprises acetic acid and ethylene glycol (glycerol). Sodium hydroxide and acetic acid are mainly utilized to react to generate sodium acetate and water, and a large amount of neutralization heat is released; wherein the reaction product sodium acetate has a good ice melting effect, the freezing point is reduced, the ice melting efficiency is improved, and the sodium acetate is small in erosion and corrosivity to soil and metal, easy to biodegrade, free of damage to a surface coating of the wind turbine blade and friendly to the surrounding environment.

Description

technical field [0001] The invention belongs to the technical field of wind power generation, and in particular relates to an ice-melting and deicing agent for wind power blades based on exothermic reaction and a preparation method thereof. Background technique [0002] Wind turbines are usually located in areas that are prone to freezing, such as high mountains or frontiers. Because the average annual temperature in these areas is low, it is common for outdoor temperatures to be below zero, which makes the blade surfaces of wind turbines very easy to freeze. However, at an altitude of 1000 In high-altitude areas of ~1800m and in forested areas, wind turbine blades freeze more seriously in winter. Winter is precisely the time when wind resources are relatively abundant. Once the surface of the blades freezes, it will not only have a direct impact on wind power revenue, but also pose a safety risk to share the operation of the unit. Therefore, anti-icing of wind power blades...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/18
CPCC09K3/185
Inventor 郭中旭杨嵩郑天帅程广文姚明宇赵瀚辰杨成龙蔡铭
Owner XIAN THERMAL POWER RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com