White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof

A technology of tourmaline and textiles, which is applied in the preparation of industrialized production of fast-heating and warming textiles, and in the field of fast-heating and warming textiles, which can solve problems such as limiting the application scenarios of mineral composite textiles, reducing the flexibility of textiles, and affecting wearing comfort. Enhance the far-infrared performance of minerals, good washing resistance, and reduce energy consumption

Pending Publication Date: 2021-12-21
YUYUE HOME TEXTILE +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, conventional mineral composite textiles, due to the addition of mineral components, will significantly reduce the flexibility of the textiles, affecting the comfort of wearing
Moreover, the firmness and color of mineral particles will limit the application scenarios of mineral composite textiles, especially in the prior art, textiles with mineral components are generally darker in color, which is not conducive to later color printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof
  • White tourmaline mineral compounded quick-heating warm-feeling textile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of white tourmaline mineral composite quick-heat warm-sensing textile, comprising the following steps:

[0046] (1) Water-based slurry preparation: 20ml of deionized water was used to dissolve the aid, including 0.4g of water-resistant dispersant CX003 and 0.03g of AMP-95 regulator. Then put 20g of white tourmaline powder with a particle size of 10 μm and 10g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0047] (2) Printing slurry preparation: add SHW binder accounting for 60g of printing slurry and 100g thickener accounting for printing slurry in turn, stir evenly;

[0048] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 22m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain the white ...

Embodiment 2

[0050] A kind of white tourmaline mineral composite quick-heat warm-sensing textile, comprising the following steps:

[0051] (1) Water-based slurry preparation: 30ml of deionized water was used to dissolve the auxiliary agent, including 0.4g of water-resistant dispersant CX003 and 0.03g of AMP-95 regulator. Then put 20g of white tourmaline powder with a particle size of 10 μm and 10g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0052] (2) Preparation of printing paste: add 50g of SHW binder and 100g of thickener in printing paste in sequence, and stir evenly;

[0053] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 10m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain the white tourmaline compound...

Embodiment 3

[0055] A kind of white tourmaline mineral composite quick-heat warm-sensing textile, comprising the following steps:

[0056] (1) Water-based slurry preparation: 30ml of deionized water was used to dissolve the auxiliary agent, including 0.4g of water-resistant dispersant CX003 and 0.03g of AMP-95 regulator. Then put 20g of white tourmaline powder with a particle size of 10 μm and 5g of black tourmaline powder with a particle size of 10 μm, 5g of SiO 2 , 5g ZrO 2 Powder with a particle size of 30nm, then stir evenly;

[0057] (2) Preparation of printing paste: add SHW binder accounting for 50g of printing paste and 100g thickener accounting for printing paste in turn, stir evenly;

[0058] (3) Printing and dyeing: the post-processing parameters of the pure fiber cloth are set as follows: the magnetic force is 5V, and the speed is 22m / min. Dry in an oven at 80°C after printing and dyeing. After drying, carry out secondary printing and dyeing and then dry, and finally obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thermal resistanceaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention generally relates to the technical field of functional textiles, in particular to a white tourmaline mineral compounded quick-heating warm-feeling textile and a preparation method of the industrially produced quick-heating warm-feeling textile. According to the white tourmaline mineral compounded quick-heating warm-feeling textile, white tourmaline and schorlite which can increase the surface temperature after absorbing light energy and have a far infrared ray emission function are used as main components, a metal oxide is used as an auxiliary agent, and a dispersing agent and a conditioning agent are added to prepare water-based slurry; then, an adhesive and a printing thickening agent are added for preparing printing paste; and finally, printing and dyeing are carried out, so that the textile is obtained. The whole preparation method is simple and suitable for large-scale industrial production and preparation, large-scale continuous production can be achieved, and the prepared white tourmaline mineral compounded quick-heating warm-feeling textile is white gray and can be directly converted into an actual commercial product by simply spraying patterns in the later period.

Description

technical field [0001] The present invention generally relates to the technical field of functional textiles, in particular to a quick-heating warm-sensing textile compounded with white tourmaline minerals, and a preparation method for industrially producing the quick-heating warm-sensing textile. Background technique [0002] With the development of society and the continuous improvement of people's quality of life, people's requirements for clothing are no longer shelter from the cold, nor is it just fashionable and beautiful. In addition to basic convenience (easy to wash, quick-drying, no fading, non-ironing, shrink-proof, etc.), comfort (soft fit, moisture absorption, skin-friendly and breathable), people's clothing health care (anti-ultraviolet, antibacterial, etc.) , antistatic, deodorant, insect-proof) also have requirements. [0003] Functional textiles refer to textiles that, in addition to their own basic use value, also have other additional special functions, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/52D06P1/673
CPCD06P1/67383D06P1/6735D06P1/5257Y02B30/00
Inventor 张以河张国清张磊田娜高路周博文高彩霞陈宇王兰心李兴娜文洪杰路明磊
Owner YUYUE HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com