Metal polishing solution and preparation method and application thereof

A polishing liquid and metal technology, applied in the field of metal polishing liquid and its preparation, can solve the problems of low cutting efficiency, cost reduction, unfavorable environmental protection, etc., and achieve the effects of excellent suspension stability, excellent polishing quality, and reduced formula cost

Pending Publication Date: 2021-12-07
DEMETER SUZHOU ELECTRONICS ENVIRONMENTAL MATERIALS CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, some commonly used metal polishing liquids still have problems such as easy scratches and low cutting efficiency when polishing 314L and 316L, and the preparation of these metal polishing liquids usually requires the addition of suspension stabilizers to facilitate long-term storage. These suspension stabilizers are usually chemicals containing organic matter, which are not conducive to subsequent water treatment and are not conducive to environmental protection. Especially when preparing polishing liquid, it takes a lot of time to screen different types of suspension stabilizers for specific polishing powders. In order to meet the excellent suspension stability of the specific polishing powder, it is time-consuming and labor-intensive. At the same time, some suspension stabilizers with better suspension stability are more expensive, which is not conducive to reducing costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal polishing solution and preparation method and application thereof
  • Metal polishing solution and preparation method and application thereof
  • Metal polishing solution and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The present embodiment provides a metal polishing liquid and a preparation method thereof, and the preparation method of the metal polishing liquid comprises the following steps:

[0052] 1) Select commercially available common pseudo-boehmite (Na content is about 0.37%, purchased from Shandong Aluminum Industry) as raw material; put the pseudo-boehmite into a kiln for calcination, the calcination temperature is 1280 ° C, and monitor the particles The specific surface area of ​​the material, and monitor the grain size with HSEM, the specific surface area of ​​the material after calcination is 4.05m 2 / g, the grain size is 98nm;

[0053] The calcined material is wet-milled with a stirring mill (stirring milling beads: spherical, φ=3mm) to control the solid content to about 43.8%, monitored by a laser particle size analyzer, and ball milled to a particle size of D 50 About 1.3μm;

[0054] 2) Commercially available common pseudo-boehmite (Na content 0.37%) is wet-milled ...

Embodiment 2

[0058] The present embodiment provides a metal polishing liquid and a preparation method thereof, and the preparation method of the metal polishing liquid comprises the following steps:

[0059] 1) Select commercially available high-purity aluminum hydroxide (purity > 99.9%, purchased from Shandong Aluminum Industry) as raw material; put high-purity aluminum hydroxide into a kiln for calcination, the calcination temperature is 1250 ° C, monitor the specific surface area of ​​the particles, and use HSEM to monitor Grain size, the specific surface area of ​​the material after calcination is 5.74m 2 / g, the grain size is 92nm;

[0060] The calcined material is wet-milled by stirring mill (stirring milling beads: spherical, φ=3mm), the solid content is controlled to be about 44.0%, monitored by laser particle size analyzer, and ball milled to particle size D 50 About 1.1 μm;

[0061] 2) Commercially available common pseudo-boehmite (Na content 0.37%) is wet-milled with a vibrati...

Embodiment 3

[0065] The present embodiment provides a metal polishing liquid and a preparation method thereof, and the preparation method of the metal polishing liquid comprises the following steps:

[0066] 1) select commercially available common pseudo-boehmite (Na content is about 0.37%) as raw material; put the pseudo-boehmite into the kiln for calcination, the calcination temperature is 1180°C, monitor the specific surface area of ​​the particles, and use HSEM Monitor the grain size, the specific surface area of ​​the calcined material is 7.43m 2 / g, the grain size is 90.9nm;

[0067] The calcined material is wet-milled with a stirring mill (stirring milling beads: spherical, φ=3mm), and the solid content is controlled to be about 40.2%, monitored by a laser particle size analyzer, and the ball is milled to a particle size of D 50 About 0.93μm;

[0068] 2) Commercially available common pseudo-boehmite (Na content 0.37%) is wet-milled with a vibration mill (milling beads: cylindrical...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Grain sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a metal polishing solution and a preparation method and application thereof. The preparation method comprises the steps that a first aluminum oxide precursor serves as a raw material and is calcined, the calcined material is subjected to wet ball milling, and the solid content of ball milling slurry is 30-55% till the particle size D<50> is 0.8-4 <mu>m; wet ball milling is carried out on a second aluminum oxide precursor until the solid content of the ball milling slurry is 30-70% until the particle size D<50> is 3-6 <mu>m; and the ball milling slurry obtained through calcination after-treatment, the ball milling slurry obtained through direct ball milling of the precursor, a surfactant, a defoaming agent, a corrosion inhibitor and a pH value regulator are mixed, and the metal polishing solution is prepared. According to the metal polishing solution, the prepared metal polishing solution can still have excellent suspension stability under the condition that a commercially available suspension stabilizer is not added, and the metal polishing solution is high in polishing efficiency, good in polishing quality and low in cost when being used for polishing stainless steel materials with the mark of 314L or 316L.

Description

technical field [0001] The invention relates to the technical field of polishing stainless steel materials, in particular to polishing media for polishing stainless steel materials such as grades 314L and 316L, and in particular to a metal polishing liquid and its preparation method and application. Background technique [0002] 314L and 316L are respectively a grade of stainless steel, which are widely used in metal products, mainly including other mechanical parts and structural parts such as furniture, bicycles, automobiles, and solenoid valves. Especially in recent years, because 314L and 316L are It has the characteristics of acid resistance, alkali resistance, and no bubbles. It is more and more used in precision daily necessities such as various watch cases, watch strap bottom covers, and mobile phone frames. However, with the further pursuit of product quality, the requirements for the surface of 314L and 316L are getting higher and higher, such as good surface brigh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F3/04C23F3/06
CPCC23F3/04C23F3/06
Inventor 周利虎郭倩倩
Owner DEMETER SUZHOU ELECTRONICS ENVIRONMENTAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap