Preparation method of emulsion for low-solid-content high-quality interior wall latex paint

A high-quality technology for interior wall latex paint, applied in the field of latex paint, can solve the problem of high cost, achieve moderate price, improve user experience, and better effect

Pending Publication Date: 2021-11-19
江苏日出化工有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to meet the national qualified product standard, the formula of the existing interior wall latex paint will ensure that the critical value of the emulsion dosage is about 10%. At this time, the solid content of the emulsion is generally about 47%, and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of emulsion for low-solid-content high-quality interior wall latex paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] S1: Add 20 parts of deionized water, 0.5 parts of emulsifier, and 0.1 part of sodium bicarbonate into the reaction bottle device, start stirring, and start to raise the temperature to 86°C.

[0022] S2: Preparation of emulsion: follow the order of 12 parts of water, 1.5 parts of emulsifier, 0.4 parts of completely dissolved sodium bicarbonate, 2 parts of acrylamide, 1 part of acrylic acid, 10 parts of butyl acrylate, 50 parts of styrene, and rinse water Add to the emulsification tank for emulsification.

[0023] S3: Preparation of the first initiator and the second initiator: the first initiator is prepared by adding 0.05 parts of sodium persulfate and 1 part of water into the oxidation bottle, and the second initiator is prepared by adding 5 parts of water and persulfuric acid into the oxidation bottle Prepared with 0.15 parts of sodium.

[0024] S4: When the temperature of the reactor rises to 86°C, add the first initiator. After the temperature is stable, add the em...

Embodiment 2

[0028] S1: Add 35 parts of deionized water, 1.5 parts of emulsifier, and 1 part of sodium bicarbonate into the reaction bottle device, start stirring, and start to heat up to 86°C.

[0029] S2: Preparation of emulsion: follow the order of 15 parts of water, 3.5 parts of emulsifier, 1.5 parts of completely dissolved sodium bicarbonate, 8 parts of acrylamide, 5 parts of acrylic acid, 20 parts of butyl acrylate, 30 parts of styrene, and rinse water Add to the emulsification tank for emulsification.

[0030] S3: Preparation of the first initiator and the second initiator: the first initiator is prepared by adding 0.2 parts of sodium persulfate and 1 part of water into the oxidation bottle, and the second initiator is prepared by adding 7 parts of water into the oxidation bottle Parts, 0.4 parts of sodium persulfate prepared.

[0031] S4: When the temperature of the reactor rises to 86°C, add the first initiator. After the temperature is stable, add the emulsion and the second ini...

Embodiment 3

[0035] S1: Add 25 parts of deionized water, 1 part of emulsifier, and 0.5 parts of sodium bicarbonate into the reaction bottle device, start stirring, and start to heat up to 86 °C.

[0036] S2: Preparation of emulsion: follow the order of 15 parts of water, 2 parts of emulsifier, 1 part of completely dissolved sodium bicarbonate, 6 parts of acrylamide, 4 parts of acrylic acid, 15 parts of butyl acrylate, 40 parts of styrene, and rinse water Add to the emulsification tank for emulsification.

[0037] S3: Preparation of the first initiator and the second initiator: the first initiator is prepared by adding 0.1 parts of sodium persulfate and 1 part of water into the oxidation bottle, and the second initiator is prepared by adding 7 parts of water and persulfuric acid into the oxidation bottle Prepared with 0.3 parts of sodium.

[0038] S4: When the temperature of the reactor rises to 86°C, add the first initiator. After the temperature is stable, add the emulsion and the second...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of emulsion for low-solid-content high-quality interior wall latex paint. The emulsion for the low-solid-content high-quality interior wall latex paint is prepared from an emulsifying liquid and an initiator, wherein the initiator comprises a first initiator and a second initiator. The preparation method comprises the following steps: S1, sequentially adding water, an emulsifying agent, completely dissolved sodium bicarbonate, acrylamide, acrylic acid, butyl acrylate, styrene and flushing water into an emulsifying tank, and emulsifying for later use to obtain the emulsifier. According to the invention, the solid content in the emulsion is reduced to about 43% from about 47% in the prior art, the national qualified product standard is met, the cost is reduced, and the market competitiveness is enhanced.

Description

technical field [0001] The invention relates to the technical field of latex paint, in particular to a method for preparing an emulsion for interior wall latex paint with low solid content and high quality. Background technique [0002] Emulsion paint is a common name for emulsion paint. It was born in the middle and late seventies of the 20th century. It is a large class of synthetic resin emulsion paint represented by acrylate copolymer emulsion. Latex paint is a water-dispersible paint. It is based on synthetic resin emulsion, and the filler is refined by adding various additives after grinding and dispersing. Latex paint has many advantages that are different from traditional wall paints, such as easy to paint, fast drying, water-resistant paint film, and good scrub resistance. The interior wall latex paint is a classification of latex paint, which is a kind of paint for interior decoration. [0003] Existing interior wall latex paint formulas interior wall latex paint...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F212/08C08F220/56C08F220/06C08F220/18C08F230/08C08F2/38C09D125/14C09D5/02
CPCC08F212/08C09D125/14C09D5/02C08F220/56C08F220/06C08F220/1804C08F230/085C08F2/38
Inventor 景国洪夏林存王海泉缪正军
Owner 江苏日出化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap