A kind of casual shoe sole and preparation method thereof

A technology for casual shoes and polyacrylamide, which is applied to shoe soles, footwear, apparel, etc., can solve the problems of shortened service life of soles and insufficient aging resistance, and achieve improved aging resistance, which is beneficial to environmental protection and prolongs service life. Effect

Active Publication Date: 2022-04-01
温州市荣奇鞋业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the related technologies mentioned above, the inventor believes that the aging resistance of the prepared rubber soles under ultraviolet light irradiation is insufficient, and the service life of the soles is shortened after repeated drying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of casual shoe sole and preparation method thereof
  • A kind of casual shoe sole and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A preparation method for casual shoe soles, comprising the following preparation steps:

[0033] S1. Mix 1kg TPR recycled material, 0.3kg polypropylene, 0.2kg thermoplastic styrene-butadiene rubber, 0.001kg cross-linking agent and banbury at 120°C for 15 minutes, then add 0.05kg polyacrylamide and 0.04kg polymethacrylate , 0.01kg amino-modified polyacrylic acid to continue banburying for 5min, and then granulate to obtain pellets;

[0034] S2. Take 0.8 kg of granulated material and heat it to a molten state, then extrude it into a corresponding shoe sole mold and make injection molding to make a casual shoe sole. The injection molding temperature is 180° C., and the mold holding time is 1 second;

[0035] The thermoplastic styrene-butadiene rubber used is a linear structure, the model is LG-604; the polyacrylamide used is anionic polyacrylamide.

Embodiment 2-9

[0037] Embodiments 2-9 are all based on Embodiment 1, and differ from Embodiment 1 only in that the preparation conditions of the soles of casual shoes are different, see Table 2 for details.

Embodiment 1-9

[0038] Table 2. The preparation conditions of embodiment 1-9 casual shoe sole

[0039]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The application relates to the field of sneaker manufacturing technology, and specifically discloses a casual shoe sole and a preparation method thereof. The raw materials for the preparation of casual shoe soles include 80-120 parts of recycled TPR, 20-40 parts of polypropylene, 15-30 parts of thermoplastic styrene-butadiene rubber, 0.05-0.15 parts of crosslinking agent, and 3-7 parts of polyacrylamide in parts by weight. 2-6 parts, 2-6 parts of polymethacrylate, 0.5-1.5 parts of amino-modified polyacrylic acid; its preparation method is: S1, banburying after mixing TPR reclaimed material, polypropylene, thermoplastic styrene-butadiene rubber, and cross-linking agent, and then Add polyacrylamide, polymethacrylate, and amino-modified polyacrylic acid to continue banburying, and granulate to obtain granulated materials; S2, heat the granulated materials to a molten state, and then extrude them into shoe sole molds for injection molding to obtain casual shoes soles. The casual shoe sole of the present application has better aging resistance under ultraviolet light irradiation and is environmentally friendly.

Description

technical field [0001] The present application relates to the field of sneaker manufacturing technology, more specifically, it relates to a casual shoe sole and a preparation method thereof. Background technique [0002] The design concept of casual shoes is mainly simple and comfortable, which can meet the needs of people's daily life. With the continuous development of economy and society, people's living standards are gradually improving, so they begin to pursue higher quality of life and life experience. The shape and connotation of casual shoes can meet people's needs and obtain spiritual satisfaction of aesthetic pleasure. [0003] The soles of casual shoes are mostly rubber soles, which are relatively soft and have high elasticity and impact resistance. my country's casual shoes market is huge, and a large number of casual shoes are produced every year, which also produces a lot of scraps and discarded soles of thermoplastic rubber soles. Thermoplastic rubber is gen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L101/00C08L23/12C08L53/02C08L33/26C08L33/02C08K5/14A43B13/04
CPCC08L101/00A43B13/04C08L2205/025C08L2205/035C08L2205/02C08L2201/08C08L23/12C08L53/02C08L33/26C08L33/02C08K5/14
Inventor 陈金荣
Owner 温州市荣奇鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap