High-grade magnesium household porcelain and manufacturing method thereof

A manufacturing method and technology of daily-use porcelain, applied in the field of ceramics, can solve the problems of narrow firing range, poor process performance, late aging and so on

Pending Publication Date: 2021-10-12
上饶市广丰区方正非矿开发有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its poor process performance, narrow firing range, and late aging, the three major technical problems are difficult to overcome, and it has not been able to achieve industrialized mass production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The ratio of each component in a high-grade magnesia daily-use porcelain blank is as follows:

[0030] Calcined white talc 45%, Guangfeng black talc 30%, kaolin 15%, petalite feldspar 7%, zirconium silicate 3%.

[0031] The composition ratio of the glaze is as follows: 47% feldspar, 20% quartz, 15% calcite, 7% burnt talc, 5% ZnO and 6% kaolin.

[0032] The manufacturing method includes the following steps:

[0033] Step 1: Calcined white talc, Guangfeng black talc, kaolin, lithium petalite and zirconium silicate are weighed and batched according to the above ratio.

[0034] Step 2: After ball milling, stirring, sieving, iron removal, mud squeezing, aging and vacuum refining, the qualified mud material is obtained. The fineness of the ball mill mud is 250 mesh; the stale time of the mud cake is 7 days; the moisture content of the mud is 23%

[0035] Step 3: weighing according to the proportion of the glaze components, adding to a ball mill, grinding to 325 meshes, sie...

Embodiment 2

[0039] The ratio of each component in a high-grade magnesia daily-use porcelain blank is as follows:

[0040] Calcined white talc 50%, Guangfeng black talc 25%, kaolin 15%, petalite feldspar 7%, zirconium silicate 3%.

[0041] The composition ratio of the glaze is as follows: 45% feldspar, 22% quartz, 12% calcite, 9% burnt talc, 7% ZnO and 5% kaolin.

[0042] The manufacturing method includes the following steps:

[0043] Step 1: Calcined white talc, Guangfeng black talc, kaolin, lithium petalite and zirconium silicate are weighed and batched according to the above ratio.

[0044] Step 2: After ball milling, stirring, sieving, iron removal, mud squeezing, aging and vacuum refining, the qualified mud material is obtained. The fineness of the ball mill mud is 250 meshes; the stale time of the mud cake is 7 days; the moisture content of the mud is 24%.

[0045] Step 3: weighing according to the proportion of the glaze components, adding to a ball mill, grinding to 325 meshes, ...

Embodiment 3

[0049] The ratio of each component in a high-grade magnesia daily-use porcelain blank is as follows:

[0050] Calcined white talc 40%, Guangfeng black talc 30%, kaolin 15%, petalite feldspar 10%, zirconium silicate 5%.

[0051] The composition ratio of the glaze is as follows: 40% feldspar, 20% quartz, 15% calcite, 7% burnt talc, 8% ZnO and 10% kaolin.

[0052] The manufacturing method includes the following steps:

[0053] Step 1: Calcined white talc, Guangfeng black talc, kaolin, lithium petalite and zirconium silicate are weighed and batched according to the above ratio.

[0054] Step 2: After ball milling, stirring, sieving, iron removal, mud squeezing, aging and vacuum refining, the qualified mud material is obtained. The fineness of the ball mill mud is 250 mesh; the stale time of the mud cake is 7 days; the moisture content of the mud is 22%.

[0055] Step 3: weighing according to the proportion of the glaze components, adding to a ball mill, grinding to 325 meshes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-grade magnesium household porcelain, which relates to the technical field of ceramics. The blank of the household porcelain comprises the following components in percentage by weight: 30-50% of calcined white talc, 20-40% of Guangfeng black talc, 10-20% of kaolin, 5-10% of petalite and 2-5% of zirconium silicate. The glaze of the household porcelain comprises the following components in percentage by weight: 40-55% of feldspar, 15-22% of quartz, 10-15% of calcite, 5-10% of calcined talc, 3-8% of ZnO and 5-10% of kaolin. The appearance quality and the performance of the high-grade magnesium household porcelain are superior to those of bone china and reinforced porcelain, and the high-grade magnesium household porcelain reaches and exceeds various standards of the high-grade household porcelain. The performance indexes are as follows: the breaking strength is more than or equal to 200MPa, the whiteness is more than or equal to 84%, the light transmittance is more than or equal to 80%, and the water absorption is less than or equal to 0.1%. And the heat stability is as follows: cracking is avoided after three times of heat exchange at 20-200 DEG C.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a high-grade magnesia daily-use porcelain and a manufacturing method thereof. Background technique [0002] As early as the end of the 18th century, Britain used talc as the main raw material to make magnesia porcelain, also known as talc porcelain. Steatite porcelain is often used to make porcelain for high-frequency insulating devices because of its low dielectric loss, high mechanical strength, and electromechanical properties between high-alumina porcelain and ordinary porcelain. [0003] In the 1980s, Shandong, my country developed a kind of talc porcelain that can be applied to daily-use ceramics. It has excellent characteristics such as high whiteness, high strength, and high transparency. However, due to its poor process performance, narrow firing range, and late aging, three major technical problems are difficult to overcome, and it has not been able to achieve industr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/20C04B35/195C04B35/622C03C8/00
CPCC04B35/20C04B35/195C04B35/622C03C8/00C04B2235/349C04B2235/3472C04B2235/3427C04B2235/96C04B2235/9646C04B2235/9607
Inventor 梅尚侠梅端杰索广宇程慧玲纪旭滨
Owner 上饶市广丰区方正非矿开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com