Rock plate with mutton fat jade touch feeling and preparation method thereof

A suet and tactile technology, applied in the field of slate with suet jade touch and its preparation, can solve the problems of many glass phases and insufficient wear resistance, and achieve good wear resistance effect

Active Publication Date: 2021-09-28
GUANGDONG OVERLAND CERAMICS CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The suet jade white porcelain can be used on an open flame, but its wear resistance is insufficient due to too much glass phase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rock plate with mutton fat jade touch feeling and preparation method thereof
  • Rock plate with mutton fat jade touch feeling and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A rock slab with suet jade tactility comprises a body layer and a glaze layer from bottom to top, and the glaze layer is formed by applying suet jade glaze on the body layer and sintering.

[0033] The suet jade glaze is prepared from the following raw materials in parts by weight: 33 parts of potassium-containing minerals, 26 parts of kaolin, 16 parts of quartz sand, 10 parts of modified aluminum borate whiskers, 7 parts of spodumene, and 6 parts of lubricant , 2 parts of calcium silicate.

[0034] Under the formula system with potassium-containing minerals and kaolin as main ingredients, by adding a lubricant, a rock slab with a smooth and delicate touch and a touch similar to suet jade can be obtained.

[0035] The potassium-containing mineral is composed of illite, potassium feldspar and muscovite in a weight ratio of 5:3:2.

[0036] The use of the above-mentioned potassium-containing minerals can improve the wear resistance to a certain extent, and can significant...

Embodiment 2

[0049] A rock slab with suet jade tactility comprises a body layer and a glaze layer from bottom to top, and the glaze layer is formed by applying suet jade glaze on the body layer and sintering.

[0050] The suet jade glaze is prepared from the following raw materials in parts by weight: 34 parts of potassium-containing minerals, 28 parts of kaolin, 20 parts of quartz sand, 6 parts of modified aluminum borate whiskers, 8 parts of spodumene, and 3 parts of lubricant , 1 part calcium silicate.

[0051] The potassium-containing mineral is composed of illite, potassium feldspar and muscovite in a weight ratio of 2:2:1.

[0052] The preparation method of described modified aluminum borate whisker is:

[0053] S1. Add 3 parts by weight of sodium oxalate, 2 parts by weight of sodium lignosulfonate, and 4 parts by weight of glycerin to 30.8 parts by weight of deionized water to prepare a mixed solution, and then add 10 parts by weight of aluminum borate whiskers to the mixed solutio...

Embodiment 3

[0062] A rock slab with suet jade tactility comprises a body layer and a glaze layer from bottom to top, and the glaze layer is formed by applying suet jade glaze on the body layer and sintering.

[0063] The suet jade glaze is prepared from the following raw materials in parts by weight: 31 parts of potassium-containing minerals, 30 parts of kaolin, 15 parts of quartz sand, 9 parts of modified aluminum borate whiskers, 6 parts of spodumene, and 5 parts of lubricant , 4 parts of calcium silicate.

[0064] The potassium-containing minerals are composed of illite, potassium feldspar and muscovite in a weight ratio of 6:3:1.

[0065] The preparation method of described modified aluminum borate whisker is:

[0066] S1. Add 2 parts by weight of sodium oxalate, 1.5 parts by weight of sodium lignosulfonate, and 2.5 parts by weight of glycerin to 33.7 parts by weight of deionized water to prepare a mixed solution, and then add 10 parts by weight of aluminum borate whiskers to the mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of rock plates, and particularly discloses a rock plate with a mutton fat jade touch feeling , the rock plate comprises a green body layer and a glaze layer from bottom to top, and the glaze layer is formed by sintering mutton fat jade glaze on the green body layer; and the mutton fat jade glaze is prepared from the following raw materials in parts by weight: 28-40 parts of potassium-containing minerals, 20-30 parts of kaolin, 15-20 parts of quartz sand, 6-11 parts of modified aluminum borate whiskers, 4-8 parts of spodumene, 3-7 parts of a lubricant and 1-4 parts of calcium silicate. The rock plate disclosed by the invention is oily, smooth and fine in touch feeling, has the touch feeling similar to that of mutton fat jade, and has a good wear-resistant effect. Under the formula system taking the potassium-containing minerals and the kaolin as the main materials, the lubricant is added, so that the rock plate which is oily, smooth and fine in touch feeling and has the touch feeling similar to that of mutton fat jade can be obtained.

Description

technical field [0001] The invention relates to the technical field of rock slabs, in particular to a rock slab with suet jade touch and a preparation method thereof. Background technique [0002] With the integration of building materials and home furnishings, slate has become a new material for kitchen and bathroom decorative panels, replacing some metals, plastics and other materials with its unique corrosion resistance, durability, and ease of cleaning. With the development of society, people's pursuit of slate is not only satisfied with its performance, but also with its touch. [0003] CN108530022A discloses a suet jade white porcelain that can be used in an open flame and a preparation method thereof, comprising a suet jade white porcelain body and a suet jade white porcelain glaze disposed outside the white porcelain body, the suet jade white porcelain glaze The components are as follows: 45-50 parts of transparent glaze, 15-20 parts of calcined spodumene powder, 15...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B35/81C04B35/16C04B41/86
CPCC03C8/00C04B35/80C04B35/16C04B41/009C04B41/5022C04B41/86C04B2235/349C04B2235/3418C04B2235/3472C04B2235/3454C04B2235/5276C04B2235/96
Inventor 石明文黄大泱卢佩玉王礼
Owner GUANGDONG OVERLAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com