A kind of two-component nano-sol type liquid curing agent and preparation method thereof

A nano-sol and hardener technology, applied in the field of building materials, can solve the problems that there are no two-component combined use, synergistic reinforcement of the base surface, inability to change and further change the direction of subsequent reactions, inability to improve concrete hardness, wear resistance, etc. To achieve the effect of improving the overall aesthetics, increasing the service life and improving performance

Active Publication Date: 2022-04-12
ZHEJIANG UNIV HANGZHOU GLOBAL SCI & TECH INNOVATION CENT
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although these formulas can effectively improve and enhance concrete hardness, wear resistance and other properties, they are all based on a single component to strengthen the hardened ground, and there is no product that uses two components together to synergistically strengthen the base surface.
The defect of single-component products is: since the addition is completed at one time during use, the subsequent reaction direction cannot be further changed according to the material reaction process and microstructure changes, so it is impossible to further improve concrete hardness, wear resistance and other properties on the basis of conventional levels
In addition, there are also nominally two-component hardeners, but they need to be mixed before use. In fact, they are also single-component for concrete and other base surfaces, and cannot react according to the concrete base surface. Changes in the situation adjust the amount of the last component material to achieve the effect of synergistic reinforcement and hardening of the base surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of two-component nano-sol type liquid curing agent and preparation method thereof
  • A kind of two-component nano-sol type liquid curing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The present invention will be further described in detail below in conjunction with the examples, but those skilled in the art will understand that the following examples are only for illustrating the present invention, and should not be regarded as limiting the scope of the present invention.

[0040]The two-component nano-sol type liquid curing agent provided by the present invention is composed of a component A solution and a component B solution. Among them, the component A solution is mixed with the following components: 15-30% silicon tetrafluoride solution with a concentration of 0.05-0.8mol / l, 10-35% silica sol with a solid content of 15%-35%, surface active Agent 0.6-1%, distilled water; component B solution is mixed with the following components: pseudo-boehmite 5-25%, ammonia water with a mass fraction of 5%-28% 1-4%, silane coupling agent 0.1- 0.5%, distilled water; the percentages of each component in the described component solutions are mass ratios, which...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building materials and aims to provide a two-component nano-sol type liquid hardener and a preparation method thereof. The liquid hardener is composed of A component solution and B component solution; A component solution is made by mixing silicon tetrafluoride solution, silica sol, surfactant and distilled water; Stone, ammonia water, silane coupling agent and distilled water are mixed. The two single-component solutions of the present invention do not undergo internal reactions and can be preserved for a long time. The ingredients used can have an irreversible chemical reaction with concrete, fill and compact the holes, and firmly fill and form an overall structure; the product has a simple preparation process, no pollution to the environment, simple raw materials, low cost, and can be directly rolled or sprayed on a large area To the concrete surface for construction, especially suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the field of building materials, and specifically relates to a two-component nano-sol type liquid hardener and a preparation method thereof. Background technique [0002] At present, the infrastructure and industrial plants that have been concreted have poor wear resistance and short service life. After long-term use, potholes, weathering, dust, sand, and peeling will appear on the surface; they can no longer meet the needs of modern production environments. In desperate need of a makeover. In order to solve this problem, many scholars have developed a variety of hardeners specially used for concrete floors in recent years, which can greatly increase its service life. [0003] At present, there are two types of ground hardener materials that are used most in the domestic and foreign markets: one is silicate products, such as CN200910055825 and CN201110083155. Lithium silicate, etc.) as the main component, and magnesium fluoro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/70C04B41/91
CPCC04B41/52C04B41/70C04B41/53C04B41/91C04B41/009C04B28/00C04B41/5089C04B41/4556C04B41/4933C04B41/46C04B41/50C04B41/495
Inventor 张继张启龙夏晨林伟峰陈盈盈杨辉
Owner ZHEJIANG UNIV HANGZHOU GLOBAL SCI & TECH INNOVATION CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products