Thermal transfer printing ink and preparation method thereof

A thermal transfer, ink technology, applied in the direction of ink, household appliances, applications, etc., can solve the problem of low color fixing rate of thermal transfer ink

Active Publication Date: 2021-09-07
铜陵晖闪数码科技有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yet, there is the problem that the fixation rate of thermal transfer printing ink is low in this invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] Another object of the present invention is to provide a preparation method of the thermal transfer ink, which is characterized in that it includes the following steps: proportioning the components, mixing them evenly and then filtering to obtain the thermal transfer ink.

[0025] Due to the application of the above technical solutions, the present invention has the following advantages compared with the prior art: the present invention provides a thermal transfer ink with high color fixation rate, antibacterial, good storage stability, high printing fluency, and color reproduction Excellent, waterproof, scratch-resistant and light-resistant, safe and environmentally friendly, not easy to age, and will not produce white smoke and odor when the ink is colored.

Embodiment 1

[0028] This example provides a thermal transfer ink, characterized in that it is made of the following components in parts by weight: 15 parts of thermal transfer disperse dyes, 1 part of rosin polyether sulfonate, 0.1 part of graphene, 10 parts of betaine, 1 part of rose extract, 15 parts of hyperbranched polyglycerol, 1 part of water-soluble chitosan, 0.1 part of preservative, 0.3 part of polymer surfactant, 30 parts of water, 10 parts of alcohol solvent.

[0029] Described alcohol solvent is ethylene glycol; Described macromolecule surfactant is 752W; the preservative is Proxel GXL; the hyperbranched polyglycerol is the 4th generation product, and it is made by the disclosed method of CN105209520A; the particle diameter of the graphene is 300nm; the rosin polyether sulfonate is Made according to the method of Example 1 in CN10817326A; the thermal transfer disperse dye is disperse dye brown 27.

[0030] A method for preparing the thermal transfer ink is characterized in th...

Embodiment 2

[0032] This example provides a thermal transfer ink, its formula and preparation method are basically the same as in Example 1, the difference is that it is made from the following components in parts by weight: 17 parts of thermal transfer disperse dyes, rosin polymer 2 parts of ether sulfonate, 0.2 parts of graphene, 11 parts of betaine, 1.5 parts of rose flower extract, 17 parts of hyperbranched polyglycerol, 1.2 parts of water-soluble chitosan, 0.2 parts of preservative, 0.4 parts of polymer surfactant Parts, 32 parts of water, 13 parts of alcohol solvent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses thermal transfer printing ink and a preparation method thereof. The thermal transfer printing ink is prepared from the following components in parts by weight: 15 to 25 parts of heat transfer printing disperse dye, 1 to 4 parts of rosin polyether sulfonate, 0.1 to 0.5 part of graphene, 10 to 15 parts of betaine, 1 to 3 parts of rose extract, 15 to 20 parts of hyperbranched polyglycerol, 1 to 2 parts of water-soluble chitosan, 0.1 to 0.5 part of preservative, 0.3 to 0.6 part of macromolecular surfactant, 30 to 40 parts of water and 10 to 20 parts of alcohol solvent. The invention also discloses a preparation method of the thermal transfer printing ink. The thermal transfer printing ink is high in fixation rate, antibacterial, good in storage stability, high in printing fluency, excellent in color reducibility, remarkable in waterproof, scratch-resistant and sun-proof effects, safe and environment-friendly to use and not liable to age, and white smoke and odor cannot be generated during color development of the ink.

Description

technical field [0001] The invention relates to the technical fields of fine chemical industry and light chemical industry, in particular to a thermal transfer printing ink and a preparation method thereof. Background technique [0002] Thermal transfer ink is also called sublimation ink, which is mainly used for heating transfer printing products. Thermal transfer ink can clearly print patterns and characters on other products after being heated by a thermal transfer machine, so it is a thermal transfer ink. One of the essential materials in the transfer printing industry. Compared with other dye inks, pigment inks and water-based inks, thermal transfer inks are bright and thick in color and high in density. After being heated and transferred by a thermal transfer machine, The image is clear and the color reproduction is high. Its appearance has aroused people's extensive attention, and the development of thermal transfer ink with excellent comprehensive performance has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D11/102C09D11/037C09D11/03
CPCC09D11/102C09D11/037C09D11/03
Inventor 王艳艳徐正华
Owner 铜陵晖闪数码科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com