A kind of self-foaming plant fiber modified polypropylene material and preparation method thereof

A polypropylene material and plant fiber technology, which is applied in the field of self-foaming plant fiber modified polypropylene material and its preparation, can solve the problems of defective products, foaming agent decomposition speed blocks, small cells, etc., and achieve improved mechanical properties , The operation process is simple, the effect of uniform bubbles

Active Publication Date: 2022-08-05
WANHUA CHEMICAL (NINGBO) CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Patent CN101538387A discloses a polypropylene foam material and its production method, by feeding high-pressure supercritical N into the twin-screw extruder 2 or CO 2 , when the polypropylene melt and high-pressure gas are evenly mixed and extruded from the machine head, due to the instantaneous drop in pressure, the high-pressure gas expands rapidly to form a cell structure. This method has high foaming efficiency and fine and uniform cells. Pressing high-pressure inert gas into the extruder requires a very complicated inflation and pressurization system, and requires extremely high airtightness of the extruder
[0004] Patent CN109575448A discloses a micro-foamed polypropylene material and its preparation method, using a chemical foaming agent as the gas source and molecular sieves as a foaming stabilizer to obtain a high expansion ratio and smaller and more uniform cells, but this The foaming agent used in the method usually decomposes faster, and it is easy to generate air marks on the surface of the molded part, resulting in defective products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-foaming plant fiber modified polypropylene material and preparation method thereof
  • A kind of self-foaming plant fiber modified polypropylene material and preparation method thereof
  • A kind of self-foaming plant fiber modified polypropylene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The technical solutions of the present application are further described below through specific embodiments. It should be understood by those skilled in the art that the embodiments are only for helping the understanding of the present application, and should not be regarded as a specific limitation of the present application.

[0034] Source of raw materials:

[0035] EP5175, LyondellBasell, polypropylene copolymer, melt index 3.5g / 10min (test condition 230℃, 2.16Kg);

[0036] 6012, Tianjin Zhongsha Petrochemical, homopolypropylene, melt index 11g / 10min (test condition 230℃, 2.16Kg);

[0037] Hemp fiber, Hangzhou Gaoke Composite Materials Co., Ltd., 5mm chopped hemp fiber;

[0038] Hemp fiber (pretreatment), Hangzhou Hi-Tech Composite Materials Co., Ltd. Hemp fiber was soaked in 7.5% sodium hydroxide aqueous solution for 12 hours, soaking temperature was 60°C, and then washed, dried and chopped, and the fiber length was 5mm;

[0039] Bamboo fiber, Hangzhou Gaoke Com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-foaming plant fiber-modified polypropylene bead and a preparation method thereof. The self-foaming plant fiber-modified polypropylene and the preparation method thereof are as follows: polypropylene, plant fiber, strong alkali, compatibilizer, Antioxidants, light stabilizers and other additives are combined according to a specific process. Compared with the traditional foamed polypropylene, the product of the present invention does not need to use additional foaming agent, utilizes the decomposition of the plant fiber itself to generate a cell structure, and at the same time improves the mechanical properties of the material.

Description

Technical field: [0001] The invention relates to polypropylene and a composition thereof, in particular to a self-foaming plant fiber modified polypropylene material and a preparation method thereof. technical background: [0002] Foamed polypropylene is widely used in automobiles, product packaging, sporting goods, toys and many other industries because of its low density, high strength, high heat resistance and good energy absorption and shock absorption properties. At present, there are two main foaming methods, including chemical foaming and physical foaming. Chemical foaming means adding a chemical foaming agent during injection molding of polypropylene, and the foaming agent decomposes in a high-temperature melt to generate a cell structure; chemical foaming agents are usually sodium bicarbonate and other chemical substances that can decompose gas. This kind of substance can usually be decomposed quickly under the action of high temperature. If the generated gas canno...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/14C08L23/12C08L97/02C08L1/02C08J9/00
CPCC08J9/0066C08J9/0061C08J2323/14C08J2401/02C08J2323/12C08J2497/02C08J2205/052
Inventor 张文勇陈连清姚威宇祁先勇
Owner WANHUA CHEMICAL (NINGBO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com