Preparation method of hydrophobic silica powder
A technology of silicon micropowder and hydrophobicity is applied in the field of preparation of hydrophobic silicon micropowder, which can solve the problems of easy agglomeration and unsatisfactory modification effect, and achieve the effects of improving dispersibility, improving effect and solving poor compatibility.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0035] The 1.5 kg of silicon fine powder was added to a high-speed mixed modifier, and the temperature was provided to 100 ° C, preheating for 30 min, and the atomized pressure was 0.5 MPa, and the Y9669 mixture of pre-water was added (7.5 g coupling agent, 7.5 g of isopropion) Alcohols and 15 g of deionized water, hydrolysis time of 30 min, hydrolyzed pH of 7.5), modified 20 min, resulting in high phase hydrophobic silicon fine powder for epoxy resin.
Embodiment 2
[0037] 1.5kg silicon fine powder was added to a high-speed mixed modifier, and the temperature was set to 110 ° C, preheating for 30 min, and the atomized pressure was 0.5 MPa, and the Y9669 mixture of pre-water was added (7.5 g coupling agent, 7.5 g isopropad Alcohols and 15 g of deionized water, hydrolysis time 30 min, hydrolyzed pH of 7.5), modified 20 min, resulting in high phase hydrophobic silicon fine powder for epoxy resin.
Embodiment 3
[0039] The 1.5 kg of silicon fine powder was added to a high-speed mixed modifier, and the temperature was provided to 100 ° C, preheating for 30 min, and the atomized pressure was 0.5 MPa, and the Y9669 mixture of pre-water was added (7.5 g coupling agent, 7.5 g of isopropion) Alcohols and 15 g of deionized water, hydrolysis time 30 min, hydrolyzed pH 8.5), modified 20 min to obtain a high phase hydrophobic silicon fine powder for epoxy resin.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com