A kind of modified thermoplastic starch and preparation method thereof

A thermoplastic starch and modification technology, applied in the field of modified thermoplastic starch and its preparation, can solve the problems of low strength and easy regeneration of thermoplastic starch, and achieve the effects of high mixing uniformity, simple steps and good water resistance

Active Publication Date: 2022-04-26
NINGBO UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to propose a modified thermoplastic starch and a preparation method thereof for the defects of low strength and easy retrogradation of the existing thermoplastic starch. The modified thermoplastic starch not only has good anti-retrograde performance, but also has relatively Excellent mechanical strength, so that the biodegradable polyester composite material filled with modified thermoplastic starch has excellent stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified thermoplastic starch and preparation method thereof
  • A kind of modified thermoplastic starch and preparation method thereof
  • A kind of modified thermoplastic starch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The preparation method of the modified thermoplastic starch of embodiment 1 may further comprise the steps:

[0046] 1) Add cornstarch and hydroxypropyl methylcellulose to a planetary ball mill in a mass-number ratio of 100:2 for dry ball milling. The grinding medium uses zirconia balls at a temperature of 60°C. The revolution speed of the ball mill is 60 rpm, and the rotation speed 120rpm, ball milling time 30min, to obtain refined starch;

[0047] 2) Add the plasticizer to the planetary ball mill equipped with refined starch in step 1) for dry ball milling, wherein the mass / number ratio of the plasticizer to the starch added in step 1) is 10:100, and the grinding medium adopts Zirconia balls, temperature 90°C, ball milling revolution speed 100rpm, rotation speed 200rpm, ball milling time 35min, to obtain plasticized starch;

[0048] 3) adding the basic catalyst, esterifying agent and coupling agent to the planetary ball mill equipped with plasticized starch in step 2...

Embodiment 6

[0058] The preparation method of the modified thermoplastic starch of embodiment 6, comprises the following steps:

[0059] 1) Put cornstarch and cellulose acetate into a planetary ball mill at a ratio of 100:5 by mass to carry out dry ball milling. The grinding medium is ceramic balls, the temperature is 70°C, the revolution speed of the ball mill is 60 rpm, the rotation speed is 110 rpm, and the milling time is 40 min , to obtain refined starch;

[0060] 2) Add the plasticizer to the planetary ball mill equipped with refined starch in step 1) for dry ball milling, wherein the mass / number ratio of the plasticizer to the starch added in step 1) is 5:100, and the grinding medium adopts Ceramic balls, temperature 95°C, ball mill revolution speed 120rpm, rotation speed 220rpm, ball mill time 40min, to obtain plasticized starch;

[0061] 3) adding the basic catalyst, esterifying agent and coupling agent to the planetary ball mill equipped with plasticized starch in step 2) and ca...

Embodiment 11

[0070] The preparation method of the modified thermoplastic starch of embodiment 11, comprises the following steps:

[0071] 1) Put cornstarch and cellulose acetate into a planetary ball mill at a ratio of 100:6 by mass and number for dry ball milling. The grinding medium is zirconia balls at a temperature of 80°C. 30min, obtain refined starch;

[0072] 2) Add the plasticizer to the planetary ball mill equipped with refined starch in step 1) for dry ball milling, wherein the mass / number ratio of the plasticizer to the starch added in step 1) is 15:100, and the grinding medium adopts Zirconia balls, temperature 95°C, ball milling revolution speed 120rpm, rotation speed 210rpm, ball milling time 35min, to obtain plasticized starch;

[0073]3) adding the basic catalyst, esterifying agent and coupling agent to the planetary ball mill equipped with plasticized starch in step 2) and carrying out dry ball milling, wherein the basic catalyst, esterifying agent, coupling agent and ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The mass percentage composition of the modified thermoplastic starch disclosed by the invention is: 100 parts of starch, 2-10 parts of modified cellulose, 5-25 parts of plasticizer, 0.5-5 parts of alkaline catalyst, and 5-10 parts of esterification agent , 1 to 5 parts of coupling agent. The modified thermoplastic starch not only has good anti-retrogradation performance, but also has better mechanical strength, so that the biodegradable polyester composite material filled with the modified thermoplastic starch has excellent stability. The preparation method of the modified thermoplastic starch of the present invention has simple steps, low equipment requirements, strong operability, and less modified raw material consumption, which can improve processing efficiency and efficiently realize the destruction, plasticization, esterification and cellulose particles of starch crystal particles The coupling strengthening of the obtained reinforced modified thermoplastic starch has excellent mechanical properties and good water resistance and anti-retrogradation performance, which expands the application of thermoplastic starch itself as a film material or as a filling material in biodegradable materials.

Description

technical field [0001] The invention relates to the field of modification of biomass materials, in particular to a modified thermoplastic starch and a preparation method thereof. Background technique [0002] Starch is a common natural biopolymer material, which often contains amylose (linked by α-1,4 glycosidic bonds) and amylopectin (linked by α-1,4 and α-1,6 glycosidic bonds). It has the advantages of degradability, low cost, renewable and wide sources, and is a better filling material. With the implementation of the "Plastic Ban and Restriction Order", starch is widely used to fill biodegradable polyesters such as PLA, PBAT, PBS, and PGA, and is prepared into disposable plastic products such as plastic bags, lunch boxes, knives and forks, and straws. The addition of starch greatly reduces the cost of biodegradable polyester products. [0003] Starch crystallizes under the action of hydrogen bonds of polyhydroxy groups, and the direct use of starch is limited and the ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/06C08L1/28C08L1/12C08L1/04
CPCC08L3/06C08L2201/06C08L1/284C08L1/12C08L1/286C08L1/04
Inventor 田佳榕钱少平刘岳侬张家溪阮贇杰
Owner NINGBO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap