Low-temperature-resistant leather ink and preparation method thereof

A technology of low temperature resistance and ink, which is applied in leather surface treatment, small raw leather/big raw leather/leather/fur treatment, small raw leather/big raw leather/leather skin/fur chemical treatment, etc., and can solve the problem of ink weatherability that cannot withstand low temperature conditions The test, cumbersome process, and various raw materials have achieved the effect of excellent low temperature resistance, convenient process, and easy-to-obtain raw materials.

Active Publication Date: 2021-06-18
广州市宝墨光固化科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method requires a lot of raw materials, and the process is cumbersome, and the finished product cannot withstand the test of the ink's weather resistance under low temperature conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature-resistant leather ink and preparation method thereof
  • Low-temperature-resistant leather ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment provides a low-temperature leather ink, according to weight percent, its raw material includes 76% acrylate, 5% pyrrolidone, 4% photoinitiator, 0.5% of the leveling agent, 0.3% dispersant, coupling 0.5% of the agent, an antioxidant 0.3%, and the slurry replenishing margin.

[0047] The acrylate is an isothersteric, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate.

[0048] The weight ratio of lysate of acrylate, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate is 3.6: 12.5: 2.5.

[0049] The pyrrolidone is a vinylpyrrolidone, and the unsaturation of vinylpyrrolidone is 3, and the CAS number is 88-12-0.

[0050] The photoinitiator is 2,4,6-trimethylbenzoyl-diphenyl phosphine, CAS number 75980-60-8.

[0051] The level of the leveling agent is BYK-333. [Not retrieved to BASF 333, please check if BASF 3033 or byk (Bik) 333; if it is determined to be BASF 333, please provide a purchase manufacturer】

[0052] The amine value of the di...

Embodiment 2

[0058] This example provides a low-temperature leather ink, according to weight percent, its raw material includes 78% acrylate, 6% pyrrolidone, 4% photoinitiator, 0.6%, dispersant 0.3%, coupling 0.5% of the agent, an antioxidant 0.3%, and the slurry replenishing margin.

[0059] The acrylate is an isothersteric, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate.

[0060] The weight ratio of lysate of acrylate, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate is 3.6: 12.5: 2.5.

[0061] The pyrrolidone is a vinylpyrrolidone, and the unsaturation of vinylpyrrolidone is 3, and the CAS number is 88-12-0.

[0062] The photoinitiator is 2,4,6-trimethylbenzoyl-diphenyl phosphine, CAS number 75980-60-8.

[0063] The level of the leveling agent is BYK-333.

[0064] The amine value of the dispersant is 17 mg kOH / g, purchases from Shanghai Guangye Chemical Co., Ltd., model is the UK Ka Card Uniqchem Uniqjet9510.

[0065] The antioxidant is a terzphenol, and th...

Embodiment 3

[0070] This example provides a low-temperature leather ink, according to the weight percentage, the raw material includes 72% acrylate, 4% pyrrolidone, 4% photoinitiator, 0.3% of the leveling agent, 0.3% dispersant, coupling 0.5% of the agent, an antioxidant 0.3%, and the slurry replenishing margin.

[0071] The acrylate is an isothersteric, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate.

[0072] The weight ratio of lysate of acrylate, tetrahydrofuranacrylate, and polyethylene glycol 600 diacrylate is 3.6: 12.5: 2.5.

[0073] The pyrrolidone is a vinylpyrrolidone, and the unsaturation of vinylpyrrolidone is 3, and the CAS number is 88-12-0.

[0074] The photoinitiator is 2,4,6-trimethylbenzoyl-diphenyl phosphine, CAS number 75980-60-8.

[0075] The level of the leveling agent is BYK-333.

[0076] The amine value of the dispersant is 17 mg kOH / g, purchases from Shanghai Guangye Chemical Co., Ltd., model is the UK Ka Card Uniqchem Uniqjet9510.

[0077] The antiox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
amine valueaaaaaaaaaa
amine valueaaaaaaaaaa
degree of unsaturationaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of UV printing, in particular to low-temperature-resistant leather ink and a preparation method thereof. The low-temperature-resistant leather ink comprises the following raw materials in percentage by weight: 66-80% of acrylic ester, 4-6% of pyrrolidone, 4-10% of a photoinitiator, 8-20% of color paste, 0.1-1% of a flatting agent, 0.2-0.6% of a dispersing agent, 0.2-1% of a coupling agent and 0.05-0.3% of an antioxidant. The low-temperature-resistant leather ink provided by the invention has the following advantages: (1) the low-temperature-resistant leather ink has excellent low-temperature resistance and folding-resistant flexibility, and the folding-resistant times at -20 DEG C after the low-temperature-resistant leather ink is jet-printed on the surface of a leather soft material can reach 300,000 or more, which is far away from the level of products of the same type in supermarkets; (2) the appearance weather resistance is strong, and cracking and fading are not easy to occur; and (3) the raw materials are easily available, the process is convenient, and the application prospect is wide.

Description

Technical field [0001] The present invention relates to the field of UV printing techniques, and more particularly to low-temperature leather-resistant inks and preparation methods thereof. Background technique [0002] UV inkjet printing is a new type of printing technique, which is characterized by ultraviolet light, printing UV cured ink on the base; the technique can print the ink over the base of various materials, which can be molded once, No topped. UV inkjet printing technology The perfect combination of UV cured ink and digital printing technology, through computer direct typography, approval, production, simple operation, high efficiency, no pollution, low input, high return, etc., it has quickly obtained The broad recognition of the market. At the same time, more and more social resources are gathered in this area, making UV printing techniques constantly improve, new technologies are constantly applying to UV printers, thereby forming a benign loop, UV printing has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/30C14C11/00
CPCC09D11/30C14C11/003Y02P70/62
Inventor 赵宝元
Owner 广州市宝墨光固化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap