Method for reducing corner cracks of medium-carbon boron-containing steel continuous casting sheet billet

A corner crack and slab technology is applied in the field of reducing corner cracks of medium carbon and boron-containing steel continuous casting slabs, which can solve the problems of difficult control of corner crack defects, and achieve the reduction of stress weak points, reduction of embrittlement, and nitrogen fixation. powerful effect

Inactive Publication Date: 2021-06-08
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a method for reducing the corner cracks of medium-carbon boron-containing steel continuous casting slabs, mainly to solve the technical problem that the existing medium-carbon boron-containing steel continuous casting slab corner crack defects are difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for reducing corner cracks of medium-carbon boron-containing steel continuous casting sheet billet
  • Method for reducing corner cracks of medium-carbon boron-containing steel continuous casting sheet billet
  • Method for reducing corner cracks of medium-carbon boron-containing steel continuous casting sheet billet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further illustrated below in conjunction with specific embodiments, and it should be understood that the following specific embodiments are only used to illustrate the present invention and are not intended to limit the scope of the present invention.

[0024]In the embodiment of the present invention, medium-carbon boron-containing molten steel is smelted in a 250-ton top-bottom double-blown converter, wherein the grade of the steel in Embodiment 1 is AR4160C2, and the grade of the steel in Embodiment 2 is DT4360B1.

[0025] The bottom blowing gas in the converter smelting process of the embodiment of the present invention is argon, and the production method includes: converter smelting, LF furnace molten steel treatment; straight arc continuous casting machine casting slab. The control parameters of molten steel production in the embodiment of the present invention are shown in Table 1 to Table 7, and the main control parameters are shown ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for reducing corner cracks of a medium-carbon boron-containing steel continuous casting sheet billet. The method mainly solves the technical problem that the corner crack defect of an existing medium-carbon boron-containing steel continuous casting sheet billet is difficult to control. The method for reducing the corner cracks of the medium-carbon boron-containing steel continuous casting sheet billet comprises the following steps of 1) adjusting the equipment precision of a straight arc-shaped continuous casting machine, and ensuring that the arc alignment precision of a crystallizer foot roller and a bent section is less than or equal to 0.15 mm; and (2) pouring the continuous casting sheet billet, specifically, adopting the straight arc-shaped continuous casting machine for pouring the sheet billet, enabling the superheat degree of tundish molten steel to be 15-25 DEG C, increasing the corner temperature in a weak cooling manner, enabling the water amount of the wide face of a crystallizer to be 3650-3850 L / min, enabling the water amount of the narrow face of the crystallizer to be 460-480 L / min, and controlling the temperature of the corners of the sheet billet before straightening to be 900 DEG C. By means of the method, titanium is adopted as an optimized alloy element, the equipment precision of the continuous casting machine is controlled, and the corner crack rate of the continuous casting sheet billet is smaller than or equal to 0.05%.

Description

technical field [0001] The invention relates to a production method of a medium-carbon boron-containing steel continuous casting slab, in particular to a method for reducing cracks at the corners of a medium-carbon boron-containing steel continuous casting slab, and belongs to the technical field of steelmaking and continuous casting. Background technique [0002] During the production process of continuous casting slabs with a boron content in the range of 0.0010-0.0030%, corner cracks are likely to occur, and the cracks are generally transverse. On the arc caster, the corner transverse cracks are usually formed on the inner arc side, while on the straight arc continuous casting machine, the corner transverse cracks may occur on the inner and outer arcs of the slab, and the length of the severe corner transverse cracks exceeds 10mm. Cracks extend from the wide face of the slab to the narrow face of the slab. There are some small cracks around the larger cracks. These small...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/14C22C38/06C22C38/04C22C38/02B22D11/043B22D11/16
CPCB22D11/001B22D11/043B22D11/16C22C38/002C22C38/02C22C38/04C22C38/06C22C38/14
Inventor 王慧娟孙明军郭园园唐洪乐殷胜
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com