Production process of high-strength Ti80 titanium ring

A production process and high-strength technology, which can be used in manufacturing tools, furnaces, heat treatment equipment, etc., and can solve the problem of insufficient strength of Ti80 titanium rings.

Pending Publication Date: 2021-06-08
陕西茂松科创有限公司
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that the strength of the Ti80 titanium ring obtained by the existing Ti80 titanium ring production process is not high enough, the present invention provides a production process for a high-strength Ti80 titanium ring

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of high-strength Ti80 titanium ring
  • Production process of high-strength Ti80 titanium ring

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A production process for a high-intensity Ti80 titanium ring, comprising the following steps:

[0027] (1) The first fire, billet forging, using 4500T equipment, preheating at 750°C for 2.5 hours, then raising the temperature to 985°C, holding time 385min, the billet after two upsetting and three drawing can be returned to the furnace for billeting, and air-cooled, repaired Grinding and blanking are divided into 95-110kg, 170-195kg, 200-235kg, 320-375, 400-420kg according to the weight of the finished product size and forging size, and the blanking is divided into two pieces of 340-380kg. One piece of 400-420kg, two pieces of blanking 160-190kg, one piece of blanking 200-215kg, one piece of blanking 100-120kg, and the range of remaining material is between 450kg and 500kg, and the remaining material is 475kg in the present invention.

[0028] (2) The second fire, use 2000T equipment, keep warm for 235min at 1000°C, complete three upsetting and three drawing, air cooling...

Embodiment 2

[0034] A production process for a high-intensity Ti80 titanium ring, comprising the following steps:

[0035] (1) The first fire, billet forging, using 4500T equipment, preheating at 780°C for 2.2 hours, then raising the temperature to 1000°C, holding time 370min, after two upsetting and three drawing, the billet can be returned to the furnace for billeting, and air-cooled, repaired Grinding and blanking are divided into 95-110kg, 170-195kg, 200-235kg, 320-375, 400-420kg according to the weight of the finished product size and forging size, and the blanking is divided into two pieces of 340-380kg. One piece of 400-420kg, two pieces of blanking 160-190kg, one piece of blanking 200-215kg, one piece of blanking 100-120kg, and the range of remaining material is between 450kg and 500kg, and the remaining material is 475kg in the present invention.

[0036] (2) The second fire, using 2000T equipment, at 1010°C and holding for 220min, complete three upsetting and three drawing, air c...

Embodiment 3

[0042] A production process for a high-intensity Ti80 titanium ring, comprising the following steps:

[0043] (1) The first fire, billet forging, using 4500T equipment, preheating at 800°C for 2 hours, then raising the temperature to 1050°C, holding time 380min, after two upsetting and three drawing, the billet can be returned to the furnace for billeting, and air-cooled, repaired Grinding and blanking are divided into 95-110kg, 170-195kg, 200-235kg, 320-375, 400-420kg according to the weight of the finished product size and forging size, and the blanking is divided into two pieces of 340-380kg. One piece of 400-420kg, two pieces of blanking 160-190kg, one piece of blanking 200-215kg, one piece of blanking 100-120kg, and the range of remaining material is between 450kg and 500kg, and the remaining material is 475kg in the present invention.

[0044] (2) The second fire, using 2000T equipment, at 1020 ° C and holding for 210 minutes, complete three upsetting and three drawing, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production process of a high-strength Ti80 titanium ring. The production process comprises the following steps: 1, cogging and forging are conducted, 4500T equipment is used, preheating is conducted at 750-845 DEG C for 1.5-2.5 hours, heating to 985-1125 DEG C, and heat preservation is conducted for 385-405 minutes; 2, 2000T equipment is used, and heat preservation is carried out at the temperature of 1000-1065 DEG C for 185-235 minutes; 3, the 2000T equipment is used, and heat preservation is conducted at the temperature of 945-995 DEG C for 185-240 min; 4, the 2000T equipment is used, and heat preservation is conducted at the temperature of 935-985 DEG C for 105-155 min; 5, the 2000T equipment is used to obtain a finished product at the temperature of 925-975 DEG C; and 6, annealing is conducted at the temperature of 755-805 DEG C. Through the production process of the Ti80 titanium ring, the tensile strength, the yield strength, the ductility, the shrinkage rate, the impact strength and the hardness of the Ti80 titanium ring in experimental data are all superior to those of standard requirements after detection and comparison, so that the requirements of various practical applications are met.

Description

technical field [0001] The invention relates to the technical field of nonferrous metal production technology, in particular to a production technology of Ti80 titanium ring. Background technique [0002] Ti80 titanium alloy is a new type of Ti-Al-Nb-Zr-Mo series α+β titanium alloy independently developed in my country. It has comprehensive properties such as high strength, high toughness, weldability, corrosion resistance, good low cycle fatigue and high impact toughness. Compared with the traditional titanium alloy TC4, the plasticity has increased by 3% to 5%, and the impact toughness has increased by nearly 2 times, is widely used in aviation, spaceflight, navigation and other fields, especially in the field of marine engineering has a good application prospect. At present, the field of marine engineering has gradually begun to use large-scale forging billets to prepare pressure vessels, pressure-resistant shells and other components. The larger the size of the forging ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21K1/76C22F1/18C21D1/26C21D9/40
CPCB21K1/761C22F1/183C21D1/26C21D9/40
Inventor 于显群
Owner 陕西茂松科创有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com