Insulation board and manufacturing method thereof

A technology for thermal insulation boards and wood chips, applied in the field of thermal insulation board preparation technology, can solve the problems of flammability, high water absorption, low compressive strength, etc., and achieve superior toughness and rigidity, good thermal insulation performance, and good compressive strength. Effect

Inactive Publication Date: 2021-05-18
上海望实建筑工程有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, EPS (molded polystyrene board), XPS (extruded polystyrene board) and PU (polyurethane), which are popular in the market for building interior and exterior insulation materials in my country, cannot meet the national building regulations due to various indicators such as fire prevention and heat preservation. requirements, but the demand in the building materials market is very large, and the current materials cannot meet the needs of fire protection and heat preservation at the same time. The extruded boards and foamed boards of plastic materials such as polystyrene and polyurethane currently used, although light in weight and heat preservation, However, its low compressive strength and flammability seriously threaten the safety of people's lives and property.
Granular rubber powder mortar made of porous light materials such as perlite solves the problem of fire prevention, but it has a high water absorption rate, is easy to crack, and has poor thermal insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulation board and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021]The method of making a thermal insulation plate proposed by the present invention includes the following steps:

[0022]S1, the mine powder slag, wood chips and straw fibers are placed in the mixer, and the stirred speed is 50 r / s, stirred for 20-28 minutes to obtain the first mixture;

[0023]S2, in the first mixture in S1, an adhesive was added in weight, continued, and the mixer was adjusted to 100 R / S, stirred for 30-40 minutes, and the second mixture was obtained;

[0024]S3, according to the weight of the polystyrene resin and the blowing agent, in place in the generator, heating mixing, the heating temperature is 60-70 ° C, the rotation speed is 30 r / s, then the catalyst is added, and stirring, stirring, stirring for 20 minutes, A third mixture is obtained;

[0025]S4, adding an antioxidant, stabilizer, and fire agent to the third mixture obtained in S3, continuing the stirring, a rotational speed of 30 r / s, and then poured the stirred mixture into the second mixture to con...

Embodiment 2

[0029]The method of making a thermal insulation plate proposed by the present invention includes the following steps:

[0030]S1, the mine powder slag, wood chips and straw fibers are placed in the mixer, and the stirred speed is 50 r / s, stirred for 20-28 minutes to obtain the first mixture;

[0031]S2, in the first mixture in S1, an adhesive was added in weight, continued, and the mixer was adjusted to 100 R / S, stirred for 30-40 minutes, and the second mixture was obtained;

[0032]S3, according to the weight of the polystyrene resin and the blowing agent, in place in the generator, heating mixing, the heating temperature is 60-70 ° C, the rotation speed is 30 r / s, then the catalyst is added, and stirring, stirring, stirring for 20 minutes, A third mixture is obtained;

[0033]S4, adding an antioxidant, stabilizer, and fire agent to the third mixture obtained in S3, continuing the stirring, a rotational speed of 30 r / s, and then poured the stirred mixture into the second mixture to con...

Embodiment 3

[0037]The method of making a thermal insulation plate proposed by the present invention includes the following steps:

[0038]S1, the mine powder slag, wood chips and straw fibers are placed in the mixer, and the stirred speed is 50 r / s, stirred for 20-28 minutes to obtain the first mixture;

[0039]S2, in the first mixture in S1, an adhesive was added in weight, continued, and the mixer was adjusted to 100 R / S, stirred for 30-40 minutes, and the second mixture was obtained;

[0040]S3, according to the weight of the polystyrene resin and the blowing agent, in place in the generator, heating mixing, the heating temperature is 60-70 ° C, the rotation speed is 30 r / s, then the catalyst is added, and stirring, stirring, stirring for 20 minutes, A third mixture is obtained;

[0041]S4, adding an antioxidant, stabilizer, and fire agent to the third mixture obtained in S3, continuing the stirring, a rotational speed of 30 r / s, and then poured the stirred mixture into the second mixture to con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulation board which is prepared from the following raw materials in parts by weight: 25 to 33 parts of slag powder, 20 to 28 parts of sawdust, 18 to 26 parts of straw fiber, 10 to 18 parts of adhesive, 15 to 23 parts of polystyrene resin, 22 to 30 parts of foaming agent, 8 to 16 parts of antioxidant, 5 to 13 parts of stabilizer, 1 to 5 parts of fire retardant and 5 to 13 parts of catalyst. Further, the insulation board comprises the following raw materials in parts by weight: 25 parts of slag powder, 20 parts of sawdust, 18 parts of straw fibers, 10 parts of an adhesive, 15 parts of polystyrene resin, 22 parts of a foaming agent, 8 parts of an antioxidant, 5 parts of a stabilizer, 1 part of a fireproof agent and 5 parts of a catalyst. The prepared heat insulation board is good in heat transfer coefficient, fireproof performance, specific gravity, compressive strength and breaking strength and has low heat conductivity so that better heat insulation performance is guaranteed, and the insulation board has excellent toughness and rigidity.

Description

Technical field[0001]The present invention relates to the field of preparation process of the insulation board, and more particularly to an insulation plate and a method of fabricating it.Background technique[0002]The thermal insulation board is easy to understand is a plate for the building. The insulation plate is a polystyrene resin as a raw material plus other raw materials and polymers, and the hard foam plate produced by heat mixing with the catalyst by heating, then extruding the pressure-out molding, has moisture-proof, waterproof performance, Reduce the thickness of the outer enclosure structure of the building, thereby increasing the indoor use area.[0003]At present, there is an epidemic building in my country, an external thermal temperature material EPS (molded polybenzene sheet) XPS (extruded polybenades) and PU (polyurethane), etc., due to fire, insulation, etc., it is not well to meet the national architectural norm Requirements, but the demand in the building materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/00C04B28/00
CPCC04B26/00C04B28/00C04B2201/32C04B2201/20C04B2201/50
Inventor 候道飞
Owner 上海望实建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com