Preparation method of reactive branched polyurethane polymeric dispersant

A polymer dispersant and branched polyurethane technology, which can be used in dyeing, textiles and papermaking, and can solve the problems of poor fiber feel

Inactive Publication Date: 2021-05-11
JIANGNAN UNIV
View PDF17 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above polyurethane dispersants all have good dispersion properties, but after printing, it is still necessary to add an adhesive to fix the fabric on the fiber, resulting in poor fiber feel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of reactive branched polyurethane polymeric dispersant
  • Preparation method of reactive branched polyurethane polymeric dispersant
  • Preparation method of reactive branched polyurethane polymeric dispersant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037](1) 10.5 g of isofluorone diisocyanate 30g solvent tetrahydrofuran was added in three flasks, and the temperature was raised to 70 ° C, and 30 g of polyethylene glycol 1000 was slowly added to prepolymerize 2 h at 70 ° C. Synthetic waterborne polyurethane prepolymer. This process adds 3 to 4 drops of DBTDL as a reaction catalyst.

[0038](2) The temperature was further increased to 80 ° C, and 1.6 g of trimethylolpropane is suck 20 g of tetrahydrofuran, and in the reaction system, the branched reaction is carried out with the polyurethane prepolymer.

[0039](3) The system was then cooled to 60 ° C, weighing 2.5 g of 1- (3-aminopropyl) morpholine as an anchoring group reaction 2 h under 70 ° C for 2 h grafted to the branched urethane end.

[0040](4) Reactive group epoxopropanol 1 g was grafted to a polyurethane end, and the reactive branched polyurethane dispersant is synthesized, and its state is a micro-yellow solution.

[0041]The synthetic polyurethane dispersant vacuum was vacuum, a...

Embodiment 2

[0043](1) In the three flask, 13.3 g of isofluorone diisocyanate was added to 30 g of solvent tetrahydrofuran, and the temperature was raised to 70 ° C, and 2 g of polyethylene glycol 400 was slowly added to prepolymers at 70 ° C for 2 h. .

[0044](2) After the reaction was completed, the hydrophilic chain extender 2,2-dihydroxymethyl propacionic acid was added to the chain-chain reaction, the synthesis of aqueous polyurethane prepolymer, which was added 3 to 4 drops DBTDL as the reaction catalyst.

[0045](3) The temperature was further increased to 80 ° C, and 1.2 g of trihydroxymethane is weighed in 20 g of tetrahydrofuran, and in the reaction system, the reaction was branched with a polyurethane concentration.

[0046](4) The system was then cooled to 50 ° C, and 2.5 g of 1- (3-aminopropyl) morpholine was weighed as an anchoring group to react 2 h under 70 ° C for 2 h into the end of the branched urethane.

[0047](5) Finally, the reactive pentaerythritol trisatyl acrylate 4.0 g was grafte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a reactive branched polyurethane polymeric dispersant, which comprises the steps of (1) putting phorone diisocyanate into a three-neck flask, heating to the temperature of 65-75 DEG C in an oil bath pan, and adding polyethylene glycol to react to synthesize a polyurethane prepolymer; (2) raising the temperature to 75-85 DEG C, and adding 2,2-dimethylolpropionic acid to carry out chain extension reaction; (3) after the chain extension reaction is completed, adding a branched structural monomer, keeping the temperature at 75-85 DEG C, and carrying out a branching reaction; (4) after the branching reaction is finished, reducing the temperature to 50-60 DEG C, grafting an anchoring group at the tail end of the polyurethane, and keeping the end capping rate at 50-75%; and (5) controlling the temperature at 50 DEG C, further grafting a reactive group, and completely blocking the isocyanate group. According to the invention, the polyurethane dispersant is designed into a branched structure on the basis of the polyurethane dispersant, and then a reactive group is introduced to the tail end, so that the self-crosslinking effect can be realized, and the color fixation effect can be achieved without adding an adhesive.

Description

Technical field[0001]The present invention is a technical field of functional polyurethane aid, and more particularly to a method of preparing a reactive branched polyurethane polymer dispersant.Background technique[0002]The organic pigment has the advantages of good photosensitive, high transparency, high color saturation, and strong fiber applicability, and has been widely used in the textile printing industry. However, when the discrete performance of the organic pigment, the solubility is poor, when the solid particles are introduced into the aqueous medium, due to the toner, Van Dehua, hydrogen bonding force, the pigment particles are prone to agglomeration, so in order to improve the efficiency of solid particles in water, The stability of reinforcing dispersion is usually introduced into the dispersant. The polymer dispersant has received wide attention in the past few decades due to its prominent dispersibility and stability. With respect to the small molecule dispersant, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08G18/34C08G18/28C08G18/67C08G18/10D06P1/52D06P3/60
CPCC08G18/10C08G18/2845C08G18/3206C08G18/3246C08G18/3281C08G18/348C08G18/4833C08G18/6677C08G18/673D06P1/5285D06P3/60
Inventor 王潮霞曾腾超殷允杰
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com