Enhanced AES composition for outdoor sound equipment shell and preparation method and application thereof

A composition and sound technology, which are applied in the field of reinforced AES compositions for outdoor audio shells and their preparation, can solve the problems of poor toughness, poor sound quality, etc., and achieve the effects of excellent toughness, not easy to be brittle, and high-quality sound quality.

Active Publication Date: 2021-05-07
KINGFA SCI & TECH CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the defects of poor toughness and poor sound quality described in the above-mentioned prior art, the present invention provides a reinforced AES composition for outdoor audio housings. The reinforced AES composition has a good balance between rigidity and toughness, and the obtained AES product As an outdoor audio enclosure, it can provide good sound quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced AES composition for outdoor sound equipment shell and preparation method and application thereof
  • Enhanced AES composition for outdoor sound equipment shell and preparation method and application thereof
  • Enhanced AES composition for outdoor sound equipment shell and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～18

[0048] The content of each component in the enhanced AES composition of Examples 1-18 is shown in Table 1.

[0049] Its preparation method is: according to Table 1, mix each component except glass fiber evenly and then add it to the main feeding port of the twin-screw extruder, add the glass fiber to the side feeding port of the twin-screw extruder, melt and co- Mixing, extruding and granulating to obtain enhanced AES composition.

[0050] Among them, the feeding speed of the twin-screw extruder is 200-350rpm; the screw temperature from the feeding port to the machine head is 220-250°C in the first zone, 220-240°C in the second zone, 210-220°C in the third zone, and 210-210℃ in the fourth zone. 230°C, five zones 210-230°C, die temperature 220-230°C, host speed 100-500r / min, vacuum degree ≤0.1MPa.

[0051] The component content (parts by weight) of the reinforced AES composition of Table 1 Embodiment 1~18

[0052]

[0053]

[0054]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Flexural modulusaaaaaaaaaa
Melt indexaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an enhanced AES composition for an outdoor sound equipment shell and a preparation method and application thereof. The reinforced AES composition comprises the following components in parts by weight: 40-60 parts of AES resin, 40-50 parts of PBAT resin, 5-30 parts of glass fibers, 0.5-10 parts of a compatilizer, 0.1-5 parts of a coupling agent, 0.1-5 parts of a lubricant and 0-5 parts of an antioxidant, the melt flow rate of the AES resin under the conditions of 220 DEG C and 10 kg is 20-35 g / 10 min, and the intrinsic viscosity of the PBAT resin is 2.0-2.8 dl / g. The enhanced AES composition for the outdoor sound equipment shell is developed by selecting the AES resin with the specific solution flow rate and the PBAT resin with the intrinsic viscosity and mutual cooperation and synergistic interaction of the glass fibers, the compatilizer, the coupling agent and other components, has excellent toughness and is not prone to brittle rupture, and the anti-falling performance of the enhanced AES material is greatly improved; the enhanced AES composition also has appropriate rigidity, and the prepared AES product can provide a high-quality sound quality effect for the sound equipment as a shell of the outdoor sound equipment.

Description

technical field [0001] The invention relates to the field of modification of polymer materials, and more specifically, relates to a reinforced AES composition for outdoor audio housings and its preparation method and application. Background technique [0002] AES resins are ethylene-propylene-diene monomer (EPDM)-acrylonitrile-styrene copolymers with substantially similar physical properties to butadiene rubber-toughened ABS resins. Since the molecular chain of EPDM is mainly composed of ethylene, propylene and a small amount of non-conjugated diene, with very little double bond content, AES resin has better weather resistance and chemical resistance than ABS resin, and is widely used in outdoor audio, household appliances, Electronic appliances and other product fields. [0003] Since AES is usually reinforced and modified with glass fibers, the addition of glass fibers will greatly reduce the toughness of AES materials on the one hand, for example, 20wt.% glass fibers wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/04C08L67/02C08L35/06C08L25/14C08K13/06C08K7/14C08K9/04C08J5/08
CPCC08J5/08C08J2351/04C08J2367/02C08J2451/04C08J2467/02C08J2435/06C08J2425/14C08K13/06C08K9/08C08K7/14
Inventor 李玉虎黄险波叶南飚付锦锋黄宝奎官焕祥唐磊何超雄陈日平林士文
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap