Building environment-friendly coating and preparation method thereof

An environmentally friendly coating and construction technology, applied in the direction of antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve problems such as damage, volatile human body, low wear resistance, etc., to reduce damage and improve gloss , conducive to the effect of promotion

Inactive Publication Date: 2021-03-19
陕西天赟轩越科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing paint gas is easy to volatilize and cause damage to the human body, and the degree of wear resistance is not high, which has certain adverse effects. Therefore, the present invention provides a kind of architectural environmental protection paint and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An architectural environmental protection coating and a preparation method thereof, the architectural environmental protection coating is composed of the following raw materials: 30 parts of titanium dioxide, 8 parts of precipitated barium, 5 parts of cellulose, 20 parts of kaolin, 15 parts of heavy calcium powder, 20 parts of emulsion, 3 parts of deodorizing film-forming aids, 2 parts of propylene glycol, 6 parts of fungicides, 12 parts of multifunctional additives, 1 part of glass beads, 7 parts of polyethylene wax, 11 parts of pigments, 3000ml of deionized water.

[0026] A kind of building environmental protection paint and preparation method thereof, concrete preparation steps are as follows:

[0027] (1), 30 parts of titanium dioxide, 8 parts of precipitated barium, 5 parts of cellulose, 20 parts of kaolin, 15 parts of heavy calcium powder, 20 parts of emulsion, 3 parts of net odor film-forming aids, 2 parts of propylene glycol, and 6 parts of fungicide 12 parts o...

Embodiment 2

[0033] An architectural environmental protection coating and a preparation method thereof, wherein the architectural environmental protection coating is composed of the following raw materials: 35 parts of titanium dioxide, 9 parts of precipitated barium, 6 parts of cellulose, and 25 parts of kaolin , 17 parts of heavy calcium powder, 23 parts of emulsion, 4 parts of deodorizing film-forming aids, 3 parts of propylene glycol, 7 parts of fungicides, 14 parts of multifunctional additives, 2 parts of glass beads, 8 parts of polyethylene wax, and 12 parts of pigments , 4000ml deionized water.

[0034] A kind of building environmental protection paint and preparation method thereof, concrete preparation steps are as follows:

[0035] (1), 35 parts of titanium dioxide, 9 parts of precipitated barium, 6 parts of cellulose, 25 parts of kaolin, 17 parts of heavy calcium powder, 23 parts of emulsion, 4 parts of net odor film-forming aid, 3 parts of propylene glycol, 7 parts of fungicide...

Embodiment 3

[0041] An architectural environmental protection coating and a preparation method thereof, wherein the architectural environmental protection coating is composed of the following raw materials: 40 parts of titanium dioxide, 10 parts of precipitated barium, 7 parts of cellulose, and 30 parts of kaolin , 20 parts of heavy calcium powder, 25 parts of emulsion, 5 parts of deodorizing film-forming aids, 4 parts of propylene glycol, 8 parts of fungicides, 15 parts of multifunctional additives, 3 parts of glass beads, 9 parts of polyethylene wax, and 13 parts of pigments , 5000ml deionized water.

[0042] A kind of building environmental protection paint and preparation method thereof, concrete preparation steps are as follows:

[0043] (1), 40 parts of titanium dioxide, 10 parts of precipitated barium, 7 parts of cellulose, 30 parts of kaolin, 20 parts of heavy calcium powder, 25 parts of emulsion, 5 parts of net odor film-forming aids, 4 parts of propylene glycol, and 8 parts of fu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of building industry, and discloses an environment-friendly building coating and a preparation method thereof. The environment-friendly building coating is preparedfrom the following raw materials in parts by weight: 30-40 parts of titanium dioxide, 8-10 parts of precipitated barium, 5-7 parts of cellulose, 20-30 parts of kaolin, 15-20 parts of coarse whiting powder, 20-25 parts of emulsion, 3-5 parts of odorless coalescing agent, 2-4 parts of propylene glycol, 6-8 parts of bactericide, 12-15 parts of multifunctional additive, 1-3 parts of glass beads, 7-9 parts of polyethylene wax, 11-13 parts of pigment and a proper amount of water. According to the environment-friendly building coating prepared by the invention, through the combination of the coarse whiting, the bactericide, the odorless coalescing agent and the bactericide, the color retention of light-color paint can be improved, the mould resistance can be increased, the harm of harmful gas tohuman bodies can be reduced, the gloss of the coating can be improved; and the polyethylene wax can achieve the effects of scratch resistance and wear resistance; The building environment-friendly coating has a bright market prospect and can be favorably popularized.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to an architectural environmental protection coating and a preparation method thereof. Background technique [0002] With the development of society, more and more buildings rise from the ground. After the buildings are built, in order to prevent the walls from being corroded, they need to be painted, so as to prevent erosion and look beautiful. Therefore, it is necessary to use architectural Eco-friendly paint. [0003] At present, the existing paint gas is easy to volatilize and cause damage to the human body, and the degree of wear resistance is not high, which has certain adverse effects. Therefore, the present invention provides an architectural environmental protection paint and a preparation method thereof. Contents of the invention [0004] Technical issues resolved [0005] Aiming at the deficiencies of the prior art, the invention provides a building environmental...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/14C09D201/00C09D123/06C09D7/61
CPCC08K2003/2241C08K2003/265C08L2205/03C09D5/14C09D201/00C09D7/61C09D7/70C08L23/06C08L1/02C08K13/04C08K7/20C08K3/26C08K3/22C08K3/346
Inventor 秦碧龙
Owner 陕西天赟轩越科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com