Preparation method and application of polypyrrole photo-thermal film for intercepting volatile organic compounds (VOCs) in water pollution

A technology for volatile organic compounds and water pollution, applied in water pollutants, water/sewage treatment, general water supply conservation, etc., can solve problems such as separation of volatile organic compounds and volatile organic compounds, and increase light absorption Area, improvement of light-to-heat conversion rate, effect of high light-to-heat conversion rate

Active Publication Date: 2021-02-19
HARBIN INST OF TECH
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problem that existing photothermal materials cannot separate volatile organic compounds existing in the form of synthetic organic compounds in water, nor can they separate volatile organic compounds produced by microbial metabolism in natural water, and provide Preparation method and application of polypyrrole photothermal film for intercepting volatile organic compounds in water pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of polypyrrole photo-thermal film for intercepting volatile organic compounds (VOCs) in water pollution
  • Preparation method and application of polypyrrole photo-thermal film for intercepting volatile organic compounds (VOCs) in water pollution
  • Preparation method and application of polypyrrole photo-thermal film for intercepting volatile organic compounds (VOCs) in water pollution

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0043] Embodiment 1: A method for preparing a polypyrrole photothermal film for intercepting volatile organics in water body pollution according to this embodiment is carried out in the following steps:

[0044] Step 1. Spin-coat photoresist positive resist on the surface of the silicon wafer with a 1 μm oxide layer on the surface;

[0045] Step 2, preparing a square grid array structure with a side length of 5 μm by photolithography;

[0046] Step 3. Soak and elute the silicon wafer after photolithography in step 2 in a mixed solution composed of hydrogen fluoride and ammonium fluoride for 5 minutes to remove exposed silicon dioxide; wherein the volume ratio of hydrogen fluoride to ammonium fluoride is 7:1, so The mass concentration of hydrogen fluoride is 49%, and the mass concentration of ammonium fluoride is 40%;

[0047]Step 4, placing the silicon wafer after step 3 in a KOH solution with a mass concentration of 35% for treatment, the treatment temperature is 70° C. and ...

specific Embodiment approach 2

[0050] Specific embodiment two: the application of the polypyrrole photothermal film prepared by specific embodiment one is as follows:

[0051] The polypyrrole photothermal film prepared in Embodiment 1 is used to intercept phenol in water pollution. The specific process is: in the process of evaporating the phenol solution, the polypyrrole cone film prepared in Embodiment 1 is attached to an open glass container Seal the open end of the open end, and then buckle it upside down on the surface of the phenol solution to ensure that the phenol solution and the polypyrrole cone membrane are fully infiltrated and in contact. Light is injected from the bottom of the glass container and reaches the polypyrrole membrane to heat the evaporated water, which condenses on the wall of the glass container for recovery detection.

[0052] Comparative experiment; use different photothermal materials to carry out barrier test on the phenol solution with an initial concentration of 5 mg / L conf...

specific Embodiment approach 3

[0055] Specific Embodiment Three: A method for preparing a polypyrrole photothermal film for intercepting volatile organics in water body pollution according to this embodiment is carried out in the following steps:

[0056] Step 1. Spin-coat photoresist positive resist on the surface of the silicon wafer with a 1 μm oxide layer on the surface;

[0057] Step 2, preparing a square grid array structure with a side length of 20 μm by photolithography;

[0058] Step 3. Soak and elute the silicon wafer after photolithography in step 2 in a mixed solution composed of hydrogen fluoride and ammonium fluoride for 5 minutes to remove exposed silicon dioxide; wherein the volume ratio of hydrogen fluoride to ammonium fluoride is 7:1, so The mass concentration of hydrogen fluoride is 49%, and the mass concentration of ammonium fluoride is 40%;

[0059] Step 4, placing the silicon wafer after step 3 in a KOH solution with a mass concentration of 35% for treatment, the treatment temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and application of a polypyrrole photo-thermal film for intercepting VOCs in water pollution. The invention belongs to the field of water resource purification materials. The invention aims to solve the technical problems that an existing photo-thermal material can not separate VOCs existing in the form of synthetic organic matters in water and can notseparate volatile biological organic compounds generated by microbial metabolism in natural water. The method comprises the following steps: 1, spin-coating photoresist on the surface of a silicon wafer with a surface oxide layer; 2, photo-etching to prepare a micron-sized grid array structure; 3, soaking and eluting in a silicon dioxide removal solution; 4, treating in a KOH solution; and 5, electro-depositing polypyrrole, and removing the template to obtain the polypyrrole film with the micron silicon cone structure on the surface; or directly etching the silicon wafer without an oxide layerby using a KOH solution, and then electro-depositing polypyrrole to obtain the polypyrrole film. The photo-thermal material disclosed by the invention has the advantages of high photo-thermal conversion rate, good water quality purification effect and simple preparation process.

Description

technical field [0001] The invention belongs to the field of water resource purification materials, and in particular relates to a preparation method and application of a polypyrrole photothermal film for intercepting volatile organic matter in water body pollution. Background technique [0002] China is a country with severe water shortage. The seven major river systems of Haihe River, Liaohe River, Huaihe River, Yellow River, Songhua River, Yangtze River and Pearl River are all polluted to varying degrees. The regeneration of usable fresh water resources is the main challenge my country currently faces in the field of water purification. As a green, environmentally friendly and sustainable technology, solar water purification technology has broad application prospects in seawater desalination, water quality sterilization, freshwater regeneration and other fields. [0003] The process of purifying water by solar energy is actually a process of converting the sun's light en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/14C02F101/30
CPCC02F1/14C02F2101/30Y02A20/212
Inventor 刘妍齐殿鹏王威徐洪波
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com