Composite wear-resistant steel plate and preparation method thereof

A wear-resistant steel plate and a wear-resistant plate technology are applied in the field of composite wear-resistant steel plates and their preparation, which can solve the problems of poor wear-resistant performance of composite steel plates, and achieve the effects of good wear-resistant performance, low price, and improved compactness.

Active Publication Date: 2021-01-22
北京华锦源耐磨材料有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, due to defects in material selection, the current clad steel plates have poor wear resistance, making it difficult to meet the needs of applying clad steel plates in scenes where friction often occurs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] A composite wear-resistant steel plate, including a wear-resistant plate and a Q235B steel plate, the wear-resistant plate is composed of the following components:

[0062] Cr 3000g;

[0063] Mn 80g;

[0064] Al 50g;

[0065] V 75g;

[0066] C 310g;

[0067] Zr 20g;

[0068] TiB 2 135g;

[0069] MoSi 2 75g;

[0070] Fe 6255g;

[0071]where TiB 2 The particle size range of 200~250nm, MoSi 2 The particle size range is 20~30μm.

[0072] Preparation method of wear-resistant plate:

[0073] S1. Mix Cr, Fe, Al, Mn, C, V, Zr, and 5kg of ethanol, and put it into a ball mill for ball milling for 1 hour, and put the slurry obtained after ball milling into a 70°C oven for 1 hour to dry to obtain the first primary mixture material;

[0074] S2. TiB 2 and MoSi 2 Mix and put into a melting furnace, heat to 890°C, keep warm for 30min to obtain the second primary mixture;

[0075] S3. Add the first primary mixture to the second primary mixture, heat to 1360°C at a he...

Embodiment 2

[0079] A composite wear-resistant steel plate, including a wear-resistant plate and a Q235B steel plate, the wear-resistant plate is composed of the following components:

[0080] Cr 4000g;

[0081] Mn 1300g;

[0082] Al 25g;

[0083] V 45g;

[0084] C 780g;

[0085] Zr 60g;

[0086] TiB 2 170g;

[0087] MoSi 2 95g;

[0088] Fe 4695g;

[0089] where TiB 2 The particle size range of 200~250nm, MoSi 2 The particle size range is 20~30μm.

[0090] Preparation method of wear-resistant plate:

[0091] S1. Mix Cr, Fe, Al, Mn, C, V, Zr, and 5kg of ethanol, and put it into a ball mill for ball milling for 2 hours, and put the slurry obtained after ball milling into a 70°C oven for 1 hour to dry to obtain the first primary mix material;

[0092] S2. TiB 2 and MoSi 2 Mix and put into the melting furnace, heat to 820°C, keep warm for 40min to get the second primary mixture;

[0093] S3. Add the first primary mixture to the second primary mixture, heat to 1380°C at a hea...

Embodiment 3

[0097] A composite wear-resistant steel plate, including a wear-resistant plate and a Q235B steel plate, the wear-resistant plate is composed of the following components:

[0098] Cr 3800g;

[0099] Mn 110g;

[0100] Al 30g;

[0101] V 60g;

[0102] C 590g;

[0103] Zr 25g;

[0104] TiB 2 160g;

[0105] MoSi 2 80g;

[0106] Fe 5145g;

[0107] where TiB 2 The particle size range of 200~250nm, MoSi 2 The particle size range is 20~30μm.

[0108] Preparation method of wear-resistant plate:

[0109] S1. Mix Cr, Fe, Al, Mn, C, V, Zr, and 5kg of ethanol, and put it into a ball mill for ball milling for 1 hour, and put the slurry obtained after ball milling into a 70°C oven for 1 hour to dry to obtain the first primary mixture material;

[0110] S2. TiB 2 and MoSi 2 Mix and put into the melting furnace, heat to 850°C, keep warm for 40min to obtain the second primary mixture;

[0111] S3. Add the first primary mixture to the second primary mixture, heat to 1400°C at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of composite steel plates, and particularly discloses a composite wear-resistant steel plate and a preparation method thereof. The composite wear-resistant steel plate comprises a base plate and a wear-resistant plate, wherein the wear-resistant plate is composed of the following components: Cr, Mn, Al, V, C, Zr, TiB2, MoSi2 and the balance Fe and inevitable impurities. The preparation method comprises the steps that Cr, Fe, Al, Mn, V, Zr and ethyl alcohol are mixed to form a first primary mixture; TiB2, MoSi2 and C are mixed to form a second primary mixture;the first primary mixture and the second primary mixture are mixed, heated, melted, pressed into a blank, annealed, cooled and ground to obtain a wear-resistant plate; and then the wear-resistant plate and the base plate are subjected to heating pressure welding to obtain the composite wear-resistant steel plate. The composite wear-resistant steel plate provided by the invention has the advantageof being good in wear resistance.

Description

technical field [0001] The application relates to the field of composite steel plates, more specifically, it relates to a composite wear-resistant steel plate and a preparation method thereof. Background technique [0002] Steel plate is a common steel in industrial production. With the continuous acceleration of industrial development, people have higher and higher requirements for steel plate. Steel plate needs to have better mechanical properties and mechanical strength, so that the steel plate can be used in the application process. play a greater role. [0003] In order to further enhance the performance of steel plates, people produce composite steel plates. On the basis of ordinary steel plates, ordinary steel plates are combined with another or more steel plates with better performance to improve the overall mechanical properties of the composite steel plates, so that they can be used At the same time as the ordinary steel plate, the mechanical properties of the ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/28C22C38/36C21D8/02C22C33/04
CPCC22C38/04C22C38/06C22C38/28C22C38/36C22C38/02C22C33/04C21D8/0205
Inventor 朱华忠
Owner 北京华锦源耐磨材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com