A top-loaded coke blend coal

A technology for blending coal and top-loading coke, applied in the field of metallurgy, can solve the problems of high cost, low content of lean coal and high content of fat coal, and achieve the effects of optimizing coal blending structure, improving coke quality and reducing costs.

Active Publication Date: 2021-11-09
SICHUAN DAZHOU IRON & STEEL GROUP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to ensure the quality of blast furnace coke and the melting efficiency, the conventional coal blending structure has high content of fat coal, low content of lean coal, high content of high-priced low-sulfur main coke, and low content of low-priced high-sulfur main coke. Although this coal blending structure can guarantee the quality of blast furnace coke, the cost is very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A top-loaded coke blend coal
  • A top-loaded coke blend coal
  • A top-loaded coke blend coal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment provides a top-loaded coke blend coal, which is composed of the following components in terms of mass percentage:

[0026] High-sulfur No. 25 coking coal: 19%; low-sulfur No. 25 coking coal: 15%; No. 35 coal I: 16%; No. 35 coal II: 25%; No. 35 coal III: 10%; lean coal: 8%; fat coal : 7%. Among them, the requirements for each component are as follows:

[0027] (1) No. 35 coal:

[0028] The caking index G value of No. 35 coal I is 80%; the caking index G value of No. 35 coal II is 75%; the caking index G value of No. 35 coal III is 65%.

[0029] (2) High sulfur No. 25 coking coal:

[0030] High sulfur No. 25 coking coal, in terms of mass percentage, each component satisfies the following relationship: the content of low metamorphic coal is 0.4%, and the low metamorphic coal is lignite and long-flame coal with a mass ratio of 1:2 Mixed coal; the content of high metamorphic coal is 0.8%, and the high metamorphic coal is a mixed coal of anthracite, lean c...

Embodiment 2

[0042] This embodiment provides a top-loaded coke blend coal, which is composed of the following components in terms of mass percentage:

[0043] High-sulfur No. 25 coking coal: 19%; low-sulfur No. 25 coking coal: 15%; No. 35 coal I: 16%; No. 35 coal II: 25%; No. 35 coal III: 10%; lean coal: 8%; fat coal : 7%. Among them, the requirements for each component are as follows:

[0044] (1) No. 35 coal:

[0045] The caking index G value of No. 35 coal I is 75%; the caking index G value of No. 35 coal II is 70%; the caking index G value of No. 35 coal III is 68%.

[0046] (2) High sulfur No. 25 coking coal:

[0047] High-sulfur No. 25 coking coal, in terms of mass percentage, each component satisfies the following relationship: the low metamorphic degree coal content is 0.5%, and the low metamorphic degree coal is a mixed coal of lignite and long-flame coal in a mass ratio of 1:1; The content of high metamorphic coal is 0.8%. The high metamorphic coal is a mixture of anthracite,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
cohesion indexaaaaaaaaaa
cohesion indexaaaaaaaaaa
cohesion indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a top-loaded coke blended coal, which comprises the following components in terms of mass percentage: No. 25 high-sulfur coking coal: 19%; No. 25 low-sulfur coking coal: 15%; No. 35 coal I: 16%; No. 35 Coal II: 25%; No. 35 Coal III: 10%; Lean Coal: 8%; The caking index G value of coal III is ≥ 70%, and the caking index G value of No. 35 coal III is ≥ 65%. The present invention controls the distribution ratio of each component of the top-loaded coke, optimizes the composition of each component and the corresponding parameter index, ensures the good thermal strength of the top-loaded coke, reduces the amount of high-priced fat coal and low-sulfur main coking coal, and improves the The proportion of low-priced lean coal and high-sulfur main coking coal optimizes the coal blending structure, effectively reduces the cost of coal blending, stabilizes the quality of coke, and creates good conditions for the stable operation of the blast furnace.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a top-loaded coke blended coal. Background technique [0002] As blast furnaces have higher and higher requirements for coke quality stability, higher requirements have been put forward for the stability of incoming coal quality. How to make full use of coal rock analysis to control incoming coal quality, optimize coal blending structure, and reduce coal blending costs has become an important issue. A major research topic facing the coking industry. [0003] In order to ensure the quality of blast furnace coke and ensure the melting efficiency, the conventional coal blending structure has high content of fat coal, low content of lean coal, high content of high-priced low-sulfur main coke, and low content of low-priced high-sulfur main coke. Although this coal blending structure can guarantee the quality of blast furnace coke, the cost is very high. Contents of the invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10B53/04
CPCC10B53/04
Inventor 龙素安李元廷杜国权吴映忠熊江君何德军
Owner SICHUAN DAZHOU IRON & STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com