High-viscosity modified asphalt for water-permeable pavement and preparation method thereof

A water-permeable pavement and modified asphalt technology, which is applied in the field of asphalt materials, can solve the problems of unsatisfactory asphalt, achieve the effects of weight reduction, high structural strength, improvement of high temperature stability and anti-aging performance

Active Publication Date: 2021-06-29
无锡市城市道桥科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Permeable pavement requires Yonggao high viscosity modified asphalt, currently there is no asphalt that meets this requirement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-viscosity modified asphalt for water-permeable pavement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056]The first component is prepared, the asphalt is mixed with UV absorber and dispersant, then heated to 180°C through a heat exchanger, transferred to the mixing production tank, and transferred to the mixing production tank; the second component is prepared, using the existing concrete Block preparation of raw materials, specifically: select waste concrete blocks, add them to a high-temperature furnace, and continue to process them at 130°C for 35 minutes; put the waste concrete blocks treated in the previous steps into a mixer, and continuously feed them into the mixer High-pressure air is used to crush the waste concrete blocks inside to obtain waste gas concrete powder; the preparation of permeable concrete is specifically: according to the weight fraction, 40 parts of waste gas concrete powder, 8 parts of water glass, and 8 parts of fine aluminum powder 8 parts, 8 parts of bentonite, 8 parts of gypsum, 8 parts of quicklime, and 25 parts of fine river sand are put into ...

Embodiment 2

[0058] The first component preparation, the asphalt is mixed with UV absorber and dispersant, then heated to 170°C through a heat exchanger, transferred to the mixing production tank, and transferred to the mixing production tank; the second component preparation, using the existing concrete Block preparation raw materials, specifically: select waste concrete blocks, add them to a high-temperature furnace, and continue to process them at 120°C for 30 minutes; put the waste concrete blocks treated in the previous steps into a mixer, and continuously feed them into the mixer High-pressure air is used to crush the waste concrete blocks inside to obtain waste gas concrete powder; the preparation of permeable concrete is specifically: according to the weight fraction, 30 parts of waste gas concrete powder, 5 parts of water glass, and 5 parts of fine aluminum powder 5 parts of bentonite, 5 parts of gypsum, 5 parts of quicklime, and 20 parts of fine river sand are put into the mixer a...

Embodiment 3

[0060] The first component is prepared, the asphalt is mixed with UV absorber and dispersant, then heated to 190°C through a heat exchanger, transferred to the mixing production tank, and transferred to the mixing production tank; the second component is prepared, using the existing concrete Block preparation raw materials, specifically: select waste concrete blocks, add them to a high-temperature furnace, and continue to process them at 150°C for 45 minutes; put the waste concrete blocks treated in the previous steps into a mixer, and continuously feed them into the mixer High-pressure air is used to crush the waste concrete blocks inside to obtain waste gas concrete powder; the preparation of permeable concrete is specifically: according to the weight fraction, 50 parts of waste gas concrete powder, 10 parts of water glass, and 10 parts of fine aluminum powder 10 parts of bentonite, 10 parts of gypsum, 10 parts of quicklime, and 30 parts of fine river sand are put into the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-viscosity modified asphalt for water-permeable pavement, comprising: a first component, the first component is asphalt; a second component, the second component is filled particles with a porous structure; The third component, the third component is a colorless cementing material; the second component and the third component are uniformly mixed and then dispersed into the first component. The technical scheme of the invention modifies the asphalt through the permeable concrete and the colorless cementing material, which can increase the water permeability of the asphalt.

Description

technical field [0001] The invention relates to an asphalt material, in particular to a high-viscosity modified asphalt for water-permeable pavement and a preparation method thereof. Background technique [0002] Bitumen is a viscous, black and highly viscous liquid or semisolid found in most crude oils and some natural sediments. Bitumen can also be obtained by refining, mostly as a carefully refined residue from the breakdown of selected crude oils. [0003] Asphalt binder is a key material for pavement, roofing and waterproofing applications. The main use of asphalt in my country is in road construction. The most common type of flexible pavement pavement in my country is hot mix asphalt. [0004] Due to its physical properties, asphalt generally cannot be used directly and needs to be modified. Modified asphalt is the addition of external additives (modifiers) such as rubber, resin, high molecular polymer, ground rubber powder or other fillers, or taking measures such a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42C04B28/26C04B28/04C04B111/40
CPCC04B28/04C04B28/26C04B40/0039C04B2111/00284C04B2111/40C04B2201/10C04B24/36C04B18/16C04B24/08C04B24/26C04B24/42C04B22/04C04B14/104C04B22/143C04B22/064C04B14/06C04B38/02C04B38/10C04B7/00C04B18/08C04B2103/302
Inventor 钱钧孙浩陶振
Owner 无锡市城市道桥科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com