Quantum energy multifunctional interior wall coating and preparation method thereof

A quantum energy, interior wall paint technology, applied in the field of paint, can solve the problems of poor stain resistance, limited release of negative ions, easy cracking of interior wall latex paint, etc., to achieve the effect of strong adhesion and simple production process

Pending Publication Date: 2020-09-22
吉林省家森林量子科技有限公司
View PDF15 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the technical problems that the existing interior wall latex paint is easy to crack, has poor stain resistance, and the effect of releasing negative ions is limited, and provides a kind of quantum energy multifunctional interior wall paint and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quantum energy multifunctional interior wall coating and preparation method thereof
  • Quantum energy multifunctional interior wall coating and preparation method thereof
  • Quantum energy multifunctional interior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The preparation method of quantum energy multifunctional interior wall paint of the present invention, the steps are as follows:

[0047] Step 1, weighing each raw material according to composition and parts by weight;

[0048] Step 2. Stir and mix the propylene glycol and dimethylsiloxane evenly;

[0049] Step 3, continue to add deionized water to the reaction kettle, stir and mix evenly;

[0050] Step 4, continue to add 1,2-benzisothiazol-3-one, zinc oxide, perhydropolysilazane, water-based dispersant, nonionic surfactant, titanium dioxide, pigments and fillers to the reactor, and stir well mixed;

[0051] Step 5, continue to add quantum dots to the reaction kettle, stir and mix evenly;

[0052] Step 6, continue to add nano-titanium dioxide and porous cellulose microspheres in the reactor, stir and mix;

[0053] Step 7. Continue to add styrene-acrylic emulsion, styrene-acrylic emulsion thickener and water-based defoamer to the reaction kettle, stir and mix evenly ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a quantum energy multifunctional interior wall coating and a preparation method thereof, belongs to the technical field of coatings, and solves the problems that existing interior wall latex paint is prone to cracking, poor in stain resistance and limited in negative ion release effect. The coating is prepared from the following components in parts by weight: 20-30 parts of styrene-acrylic emulsion, 1.5-2.5 parts of styrene-acrylic emulsion thickener, 0.8-1.5 parts of simethicone, 0.5-1 part of propylene glycol, 1-2 parts of quantum dots, 3-5 parts of nano titanium dioxide, 1-3 parts of porous cellulose microspheres, 1-2 parts of 1, 2-benzoisothiazole-3-ketone, 0.2-0.5 part of zinc oxide, 1-1.2 parts of perhydropolysilazane, 3-8 parts of a water-based dispersing agent, 2-4 parts of a water-based defoaming agent, 2-4 parts of a nonionic surfactant, 2-5 parts of titanium dioxide and the like. The coating is high in adhesive force, resistant to scrubbing and contamination, not prone to cracking, resistant to bacteria and mildew and capable of releasing negative ions and purifying air.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a quantum energy multifunctional interior wall coating and a preparation method thereof. Background technique [0002] Latex paint is a kind of water-based paint prepared by adding pigments, fillers and various additives to synthetic resin emulsion as the base material. It is also called synthetic resin emulsion paint and is a kind of organic paint. According to different production materials, latex paint mainly includes polyvinyl acetate latex paint, ethylene-propylene latex paint, pure acrylic latex paint and other varieties. According to different product application environments, it can be divided into two types: interior wall and exterior wall latex paint. Gloss effect can be divided into flat, matte, semi-gloss, mercerized and glossy and other types. [0003] Latex paint is widely used in housing construction environmental protection coatings because of its advantages suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D5/14C09D5/16C09D7/61C09D7/65
CPCC08K2003/2241C08K2003/2296C08K2201/011C08K2201/014C08L2205/02C08L2205/035C08L2205/18C09D5/14C09D5/1687C09D125/14C09D7/67C08L83/04C08L1/02C08L83/16C08K13/02C08K3/22C08K5/47C08K3/04C08K3/30
Inventor 朱丙仪
Owner 吉林省家森林量子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products