Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polymer, curable resin composition and use thereof

A polymer and cured product technology, applied in the direction of optical filters, etc., can solve the problem of insufficient transparency of the cured film, and achieve the effect of excellent heat resistance and coloring

Active Publication Date: 2022-03-18
NIPPON SHOKUBAI CO LTD
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, for a resin composition containing a polymer derived from maleimide, since the maleimide-based polymer contains nitrogen atoms, there is a problem that the polymer is colored yellow to yellowish-brown during heating and the cured film may be cured. The problem of insufficient transparency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer, curable resin composition and use thereof
  • Polymer, curable resin composition and use thereof
  • Polymer, curable resin composition and use thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0279]

[0280] The method for preparing the curable resin composition is not particularly limited, and a known method may be used. For example, a method of mixing and dispersing the above-mentioned components using various mixers and dispersers is mentioned. The mixing / dispersing step is not particularly limited, and may be performed by a known method. In addition, other generally performed steps may be further included. In addition, when the said curable resin composition contains a coloring material, it is preferable to prepare through the dispersion|distribution treatment process of a coloring material.

[0281] As the dispersion treatment process of the above-mentioned coloring material, for example, the following method can be enumerated: first, weighing each predetermined amount of coloring material (preferably an organic pigment), a dispersant, and a solvent, and using a disperser to disperse the coloring material particles to obtain a liquid Pigment dispersion (als...

Embodiment

[0324] The following examples are given to illustrate the present invention in more detail, but the present invention is not limited to these examples. In addition, unless otherwise stated, "part" means "mass part", and "%" means "mass %".

[0325] In this example, measurement conditions of various physical properties and the like are as follows.

[0326]

[0327] Utilize HLC-8220GPC (manufactured by Tosoh Corporation), use tetrahydrofuran as eluent, use TSK-gelSuperHZM-M (manufactured by Tosoh Corporation) as column, measure by gel permeation chromatography, and calculate by standard polystyrene conversion weight average molecular weight.

[0328]

[0329] Accurately weigh about 1 g of the copolymer solution in an aluminum cup, add about 2 g of acetone to dissolve it, and let it stand at room temperature for about 2 hours to allow it to dry naturally. Then, after drying in vacuum at 140 degreeC for 1.5 hours with the vacuum dryer (made by EYELA company), it cooled natur...

Synthetic example 1

[0349] Preparation of Copolymer Solution 1

[0350] Prepare a detachable flask equipped with a thermometer, a stirrer, a gas inlet tube, a condenser tube, and a drop tank inlet as a reaction tank. On the other hand, as a monomer drop tank, prepare 10.0 parts of dimethyl-2,2 '-[Oxybis(methylene)]bis-2-acrylate (hereinafter referred to as MD), 29.5 parts of tert-butyl methacrylate (hereinafter referred to as "t-BMA"), 15.0 parts of methyl 2-hydroxyethyl acrylate (hereinafter referred to as "HEMA"), 1.0 parts of methyl methacrylate (hereinafter referred to as "MMA"), 44.5 parts of mono(2-acryloyloxyethyl) succinate ( Hereinafter referred to as "HOA-MS"), 2 parts of t-butyl peroxide (2-ethylhexanoate) ("perbutyl (registered trademark) O" manufactured by NOF Corporation; hereinafter referred to as "PBO"), 33 Parts of propylene glycol monomethyl ether acetate (hereinafter referred to as "PGMEA") was fully stirred and mixed, and dropped into the tank as a chain transfer agent, and 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The present invention provides a polymer that can sufficiently suppress yellowing during heating and can be applied to high coloration; and a curable resin composition containing the polymer. The present invention is a polymer characterized in that it has 10 to 60% by mass of a monomer unit represented by the following general formula (I) and 5 to 80% by mass of -COO * R 4 (R 4 is a monovalent organic group, and O * The bonded carbon atom is a tertiary carbon atom) based vinyl-based monomer unit.

Description

technical field [0001] The present invention relates to a new polymer. More specifically, it relates to a polymer excellent in heat-resistant colorability, a curable resin composition containing the polymer, a color filter having a cured product of the curable resin composition, and a display device. Background technique [0002] Polymers curable by heat or active energy rays are used in various applications depending on the properties of the polymers. Examples of such applications include various optical components such as color filters, inks, printing plates, printed circuit boards, semiconductor elements, and photoresists used in liquid crystal display devices and solid-state imaging devices. For electrical / electronic equipment, etc., studies have been made on copolymers suitable for these applications. [0003] In the above-mentioned applications, the color filter is a main part constituting a liquid crystal display device or a solid-state imaging element, etc., and us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/18C08F265/06C08L33/06G02B5/20
CPCC08F265/06C08L33/06G02B5/20C08F220/1804C08F220/282C08F212/04
Inventor 久野美辉松田安弘加藤泰斗
Owner NIPPON SHOKUBAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More