High-nickel ternary precursor with core-shell structure, preparation method of high-nickel ternary precursor, and hollow doped high-nickel ternary positive electrode material

A core-shell structure and precursor technology, applied in structural parts, electrical components, battery electrodes, etc., can solve the problems of low initial capacity, unstable cycle structure, poor conductivity of high-nickel NCM, etc., to improve the internal structure and easy to design. Assembly and structure regulation, and the effect of facile preparation

Active Publication Date: 2020-08-11
ZHUJI PAWA NEW ENERGY
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems existing in the prior art, the present invention provides a high-nickel ternary precursor with a core-shell structure, which overcomes the problems of high-nickel NCM with poor conductivity, unstable cycle structure, and low initial capacity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-nickel ternary precursor with core-shell structure, preparation method of high-nickel ternary precursor, and hollow doped high-nickel ternary positive electrode material
  • High-nickel ternary precursor with core-shell structure, preparation method of high-nickel ternary precursor, and hollow doped high-nickel ternary positive electrode material
  • High-nickel ternary precursor with core-shell structure, preparation method of high-nickel ternary precursor, and hollow doped high-nickel ternary positive electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The preparation of a high-nickel ternary precursor with a core-shell structure includes the following steps:

[0043] (1) The concentration of zinc nitrate is adjusted and controlled at 2mol / L; the concentration of 2-methylimidazole is adjusted and controlled at 4mol / L;

[0044] (2) Slowly add the uniformly stirred metal salt solution into the 2-methylimidazole solution, stir for 30min, and let stand for 24h;

[0045] (3) The Zn-MOF was washed by centrifugation, dried at 80°C for 8 hours, and then soaked in 0.1mol / L boric acid solution for 6 hours;

[0046] (4) Industrial 28% ammonia water is mixed with deionized water and the concentration is adjusted to be 10mol / L; NaOH is mixed with deionized water to adjust the concentration to be 4mol / L;

[0047] (5) dissolving soluble nickel nitrate, cobalt nitrate, and manganese nitrate with a molar ratio of Ni:Co:Mn=7:2:1 and a total concentration of 2mol / L in hot water at 70°C, and stirring until completely dissolved;

[0048...

Embodiment 2

[0058] The preparation of a high-nickel ternary precursor with a core-shell structure includes the following steps:

[0059] (1) The concentration of zinc nitrate is adjusted and controlled at 2mol / L; the concentration of 2-methylimidazole is adjusted and controlled at 4mol / L;

[0060] (2) Slowly add the uniformly stirred metal salt solution into the 2-methylimidazole solution, stir for 30min, and let stand for 24h;

[0061] (3) The Zn-MOF was washed by centrifugation, dried at 80°C for 12h, and then soaked in 0.05mol / L boric acid solution for 10h;

[0062] (4) Industrial 28% ammonia water is mixed with deionized water and the concentration is adjusted to be 10mol / L; NaOH is mixed with deionized water to adjust the concentration to be 4mol / L;

[0063] (5) dissolving soluble nickel nitrate, cobalt nitrate, and manganese nitrate with a molar ratio of Ni:Co:Mn=6:2:2 and a total concentration of 2mol / L in hot water at 70°C, and stirring until completely dissolved;

[0064] (6) P...

Embodiment 3

[0069] The preparation of a high-nickel ternary precursor with a core-shell structure includes the following steps:

[0070] (1) The concentration of zinc nitrate is adjusted and controlled at 1.5mol / L; the concentration of 2-methylimidazole is adjusted and controlled at 3mol / L;

[0071] (2) Slowly add the uniformly stirred metal salt solution into the 2-methylimidazole solution, stir for 15 minutes, and let stand for 20 hours;

[0072] (3) The Zn-MOF was washed by centrifugation, dried at 100°C for 6h, and then soaked in 0.02mol / L boric acid solution for 24h

[0073] (4) Industrial 28% ammonia water is mixed with deionized water and the concentration is adjusted to be 10mol / L; NaOH is mixed with deionized water to adjust the concentration to be 4mol / L;

[0074] (5) dissolving soluble nickel sulfate, cobalt sulfate, and manganese sulfate with a molar ratio of Ni:Co:Mn=8:1:1 and a total concentration of 2mol / L in hot water at 70°C, and stirring until completely dissolved;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of lithium ion battery materials, in particular to a high-nickel ternary precursor with a core-shell structure, a preparation method of the high-nickel ternary precursor and a hollow doped high-nickel ternary positive electrode material. The precursor is of a core-shell structure, an inner core is of a boron-doped octahedral structure Zn-MOF, and an outer shell is of a nickel-rich ternary precursor NixCoyMnz(OH)2. The preparation method comprises the following two steps: step 1, synthesizing octahedral structure Zn-MOF (metal organic framework) through coprecipitation, and soaking the octahedral structure Zn-MOF in a boric acid solution to obtain boron-doped MOF; and step 2, coating a high-nickel ternary precursor material on the basis to form the high-nickel ternary precursor with the core-shell structure. The high-nickel ternary precursor with the core-shell structure is prepared by adopting a simple and efficient method, and a foundation is laid for a cathode material prepared in the later period to have higher initial capacity and cycling stability; the product synthesized by adopting a coprecipitation method is uniform in component, good in sphericity degree and good in reproducibility, and has good economic value and application prospect.

Description

technical field [0001] The invention relates to the technical field of lithium ion batteries, in particular to a core-shell structure high-nickel ternary precursor and a preparation method thereof, and a hollow-doped high-nickel ternary positive electrode material. Background technique [0002] Lithium-ion batteries (LIBs) with high energy and power density have been widely used in energy storage systems. Electrode materials provided for EVs or HEVs need to fully balance five basic factors: energy density, power density, cost, lifetime, and safety. Nickel-rich (Ni content gradually increases from x=0.33 to x=0.85 and even higher) layered ternary cathode material LiNi with high capacity and high energy density x co y mn 1-x-y o 2 (NCM) and LiNi x co y al 1-x-y o 2 (NCA) has become a very representative material in commercialization. However, detrimental phase transitions inside high-nickel materials can lead to structural instability, as well as surface-active Ni in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/485H01M4/505H01M4/525H01M10/0525
CPCH01M4/366H01M4/485H01M4/505H01M4/525H01M10/0525Y02E60/10
Inventor 张宝王振宇
Owner ZHUJI PAWA NEW ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com