A high-stiffness, low-viscosity tire compound and its preparation method, and a semi-steel radial tire

A low-viscosity, mixed rubber technology, applied in special tires, tire parts, transportation and packaging, etc., can solve the problems of mixed rubber tear strength and elongation at break, etc., to achieve easy processing and improve processing Sexuality, viscosity-reducing effect

Active Publication Date: 2022-07-15
ZHONGCE RUBBER GRP CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, after adding trans-isoprene rubber TPI or eucommia rubber, the tear strength and elongation of the mixed rubber decrease insufficiently, which makes trans-isoprene rubber used in the crown of semi-steel radial tires Restricted when carrying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-stiffness, low-viscosity tire compound and its preparation method, and a semi-steel radial tire
  • A high-stiffness, low-viscosity tire compound and its preparation method, and a semi-steel radial tire
  • A high-stiffness, low-viscosity tire compound and its preparation method, and a semi-steel radial tire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 to 8

[0029] Examples 1 to 8 are as shown in Table 1 (parts by weight).

[0030] Table 1

[0031]

[0032]

[0033] Table 1 Footnotes

[0034] *1: Vietnam 10# natural rubber mixture;

[0035] *2: Synthesis of 1,4-trans polyisoprene rubber, Wuhan Yuancheng Gongchuang Technology Co., Ltd.;

[0036] *3: SBR1500, product of PetroChina Lanzhou Petrochemical Company;

[0037] *4: N326 carbon black, product of Cabot (China) Investment Co., Ltd.;

[0038] *5: Hydrazide Substance Modifier DC-02, Otsuka Material Technology Co., Ltd.;

[0039] *6: Zinc oxide (indirect method), product of Shijiazhuang Zhiyi Zinc Industry Co., Ltd.;

[0040] *7: Stearic acid 1808, Baili Co., Ltd.;

[0041] *8: Anti-aging agent 4020, Sennics Technology Co., Ltd.;

[0042] *9: Resin SL3020, Huaqi Chemical Co., Ltd.;

[0043] *10: Plasticizer A, Wuhan Jinghe Chemical Co., Ltd.;

[0044] *11: OKERIN 1987, Bai Rui Mei Special Chemicals Co., Ltd.;

[0045] *12: Oil-extended sulfur powder S200-10S, Wuxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The present application relates to the field of new tire materials, in particular to a high-stiffness, low-viscosity tire compound, a preparation method thereof, and a semi-steel radial tire using the compound. A high-stiffness, low-viscosity tire compounded rubber, based on 100 parts by mass of the rubber component, the rubber component of the compounded rubber comprising synthetic trans-1,4-polyisoprene (TPI) and / or Or natural eucommia gum (EUG) 1.0-30.0 parts, and adding 0.1-2.0 parts of hydrazide-type material modifiers to prepare, the mixed rubber of the application can significantly improve the stiffness of the rubber compound and improve the viscosity of the rubber compound, but it is not easy to Causes the cap to bloom, which is especially suitable for the manufacture of semi-finished tire caps with high stiffness, low viscosity and low heat generation.

Description

technical field [0001] The present application relates to the field of new tire materials, in particular to a high-stiffness, low-viscosity tire compound, a preparation method thereof, and a semi-steel radial tire using the compound, which can significantly improve the stiffness and stiffness of the compound. Viscosity, reducing tire rolling resistance, especially suitable for improving the stiffness and viscosity of tire semi-finished products during processing. Background technique [0002] With the rapid development of tires and the continuous improvement of tire processing and service performance, the stiffness and viscosity of rubber compounds used in tire semi-finished products have attracted more and more attention from tire manufacturers. [0003] Natural rubber or synthetic rubber and compounding agent are mixed in a certain proportion by a rubber mixer in an uncrosslinked state, which is called mixed rubber. The stiffness of the rubber compound is expressed by sti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/06C08L9/00C08L91/06C08K13/02C08K3/04C08K3/22C08K5/09C08K5/25C08K3/06B60C1/00
CPCC08L7/00C08L9/06B60C1/00C08L2205/035C08L2205/02B60C2001/0066C08L9/00C08L91/06C08K13/02C08K3/04C08K3/22C08K5/09C08K5/25C08K3/06
Inventor 刘辉徐从升董兴旺王丹灵任福君
Owner ZHONGCE RUBBER GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com