Preparation method and application of magnetic structural color hydrogel microcarrier for bladder cancer protein multi-element analysis
A technology of magnetic structure and multivariate analysis, applied in the field of biomedical materials, can solve the problems of poor repeatability, large steric hindrance, cross-contamination, etc., and achieve the effects of high specificity, good stability and high flexibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] Preparation of magnetic structured color hydrogel microcarriers
[0033] (1) see figure 1 In the preparation process, silica nanoparticles with a particle size of 215nm were selected, and a monodisperse silica nanoparticle suspension with a concentration of 20m / v% was used as the internal phase, and dimethyl fluorinated silicone oil (50cSt) was used as the external phase. , the external phase and the internal phase are injected into the corresponding channels of the microfluidic device, collected in the container through the output channel of the microfluidic device, and at 65 ° C, the droplets of the silica nanoparticles evaporate with the water Self-assembled, solidified and crystallized for 12 hours to form silica photonic crystal microspheres; the temperature was raised to 95°C to solidify the silica photonic crystal microspheres for 2 hours; then the silica photonic crystal microspheres were collected in a crucible and washed with n-hexane The microspheres were cl...
Embodiment 2
[0038] Preparation of magnetic structured color hydrogel microcarriers
[0039] (1) see figure 1In the preparation process, silica nanoparticles with a particle size of 237nm were selected, and a monodisperse silica nanoparticle suspension with a concentration of 20m / v% was used as the internal phase, and dimethyl fluorinated silicone oil (50cSt) was used as the external phase. , the external phase and the internal phase are injected into the corresponding channels of the microfluidic device, collected in the container through the output channel of the microfluidic device, and at 65 ° C, the droplets of the silica nanoparticles evaporate with the water Self-assembled, solidified and crystallized for 12 hours to form silica photonic crystal microspheres; the temperature was raised to 95°C to solidify the silica photonic crystal microspheres for 2 hours; then the silica photonic crystal microspheres were collected in a crucible and washed with n-hexane The microspheres were cle...
Embodiment 3
[0043] Preparation of magnetic structured color hydrogel microcarriers
[0044] (1) see figure 1 In the preparation process, silica nanoparticles with a particle size of 247nm were selected, and a monodisperse silica nanoparticle suspension with a concentration of 20m / v% was used as the internal phase, and dimethyl fluorinated silicone oil (50cSt) was used as the external phase. , the external phase and the internal phase are injected into the corresponding channels of the microfluidic device, collected in the container through the output channel of the microfluidic device, and at 65 ° C, the droplets of the silica nanoparticles evaporate with the water Self-assembled, solidified and crystallized for 12 hours to form silica photonic crystal microspheres; the temperature was raised to 95°C to solidify the silica photonic crystal microspheres for 2 hours; then the silica photonic crystal microspheres were collected in a crucible and washed with n-hexane The microspheres were cl...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com