Engineering inner tube made of nano material and production method thereof

A technology of nanomaterials and production methods, applied in special tires, tire parts, transportation and packaging, etc., can solve problems affecting the bonding strength of inner tube joints and valves, high heat generation in the extrusion process, and heavy weight of engineering inner tubes, etc. , to achieve the effects of forming vulcanization, reducing material costs and increasing dosage

Inactive Publication Date: 2020-07-17
威海市润通橡胶有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The inner tube is an important part of the tire. The special carbon black reinforcing agent for the traditional inner tube formula is expensive, and the mixing and extrusion process generates a lot of heat. The self-adhesiveness of the rubber is poor, which affects the bonding strength of the inner tube joint and the valve. Engineering inner tubes have problems such as heavy weight and high cost, and the main reason for these problems is the limitation of production technology and raw materials; in recent years, with the emergence of new varieties of raw materials, it has created the possibility for the improvement of the processability and physical and mechanical properties of the rubber compound. Therefore, what kind of nanomaterials to use and how to apply nanomaterials to improve the manufacturability and physical and mechanical properties of the rubber compound, reduce material costs, and reduce the weight of the inner tube are technical problems that need to be solved by those skilled in the art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Engineering inner tube made of nano material and production method thereof
  • Engineering inner tube made of nano material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Such as Figure 1-2 As shown, the inventive point of the present application is that the components of the inner tube are: 70 parts of natural rubber, 30 parts of styrene-butadiene rubber, 3 parts of nano-zinc oxide, 45 parts of nano-calcium carbonate, 15 parts of carbon black, 6 parts of carbon nanotube 1.9 parts of stearic acid, 1.9 parts of vulcanization accelerator, 1.8 parts of accelerator, 3.2 parts of antioxidant, 0.2 part of peptizer, 14 parts of softener, 5 parts of tackifier;

[0035] The manufacturing technological process of described inner tube of a tube is:

[0036] Step 1. Use an internal mixer for mixing, and mix the rubber materials according to the mixing process regulations. The rubber discharge temperature of the first stage of mixing is 145-150 ° C, and the temperature of the second stage of mixing and adding vulcanizing agent is 90- 95°C.

[0037] Step 2. Use an extruder to extrude the compounded rubber into a tire tube according to the construct...

Embodiment 2

[0049] The components of the inner tube are: 80 parts of natural rubber, 20 parts of styrene-butadiene rubber, 3 parts of nano-zinc oxide, 50 parts of nano-calcium carbonate, 15 parts of carbon black, 8 parts of carbon nanotubes, 1.9 parts of stearic acid, vulcanization accelerator 2 parts, accelerator 1.5, anti-aging agent 3.4 parts, peptizer 0.25 parts, softener 12 parts, tackifier 4 parts. Others are the same as in Example 1.

Embodiment 3

[0051] 65 parts of natural rubber, 35 parts of styrene-butadiene rubber, 3.2 parts of nano-zinc oxide, 47 parts of nano-calcium carbonate, 22 parts of carbon black, 5 parts of carbon nanotubes, 1.9 parts of stearic acid, 1.8 parts of vulcanization accelerator, 2.1 parts of accelerator, anti-aging 2.9 parts of agent, 0.2 parts of peptizer, 15 parts of softener, and 6 parts of tackifier. Wherein, the model of the natural rubber is SCR L or SCR 5, the model of styrene-butadiene rubber is SBR 1500 or SBR1502, the carbon black is N220, and the resin is E1102. Others are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an engineering inner tube made of a nano material and a production method of the engineering inner tube. The inner tube comprises the following components: 65 to 80 parts of natural rubber, 20 to 35 parts of butadiene-styrene rubber, 2.5 to 3.5 parts of nano zinc oxide, 40-50 parts of nano calcium carbonate, 15-22 parts of carbon black, 5-10 parts of carbon nanotubes, 1.7-2.5 parts of stearic acid, 1.8-2.2 parts of a vulcanization accelerator, 1.2-1.8 parts of an accelerator, 2.5-3.5 parts of an anti-aging agent, 0.2-0.3 part of a peptizer, 12-18 parts of a softener and4-7 parts of a tackifier. The engineering inner tube has the beneficial effects that the inner tube is light in weight and low in production cost.

Description

technical field [0001] The invention relates to the production technical field of engineering inner tubes, in particular to an engineering inner tube made of nanometer materials and a production method thereof. Background technique [0002] The inner tube is an important part of the tire. The special carbon black reinforcing agent for the traditional inner tube formula is expensive, and the mixing and extrusion process generates a lot of heat. The self-adhesiveness of the rubber is poor, which affects the bonding strength of the inner tube joint and the valve. Engineering inner tubes have problems such as heavy weight and high cost, and the main reason for these problems is the limitation of production technology and raw materials; in recent years, with the emergence of new varieties of raw materials, it has created the possibility for the improvement of the processability and physical and mechanical properties of the rubber compound. , Therefore, what kind of nanomaterials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08K13/02C08K3/22C08K3/26C08K3/04C08K5/09B60C1/00
CPCB60C1/0041C08K2003/2296C08K2003/265C08K2201/011C08L7/00C08L9/06C08K13/02C08K3/22C08K3/26C08K3/041C08K5/09
Inventor 蒋延伟何长军
Owner 威海市润通橡胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com