Degradable EVA foam material and preparation method thereof

A foaming material, ethylene technology, applied in the field of foaming materials, can solve the problems of poor mechanical strength and other comprehensive use performance, poor anti-slip effect, poor wear resistance, etc., to achieve good anti-slip effect, high elasticity, and improved quality Effect

Active Publication Date: 2020-07-03
福建安达福新材料科技有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. Poor wear resistance;
[0006] 2. Poor elasticity;
[0007] 3. Poor anti-slip effect;
[0008] 4. Non-degradable, not environmentally friendly, poor mechanical strength and other comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable EVA foam material and preparation method thereof
  • Degradable EVA foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A kind of degradable EVA foaming material, is made of the raw material that comprises following parts by weight:

[0056] 35-45 parts of ethylene-vinyl acetate copolymer,

[0057] 15-20 parts of POE elastomer,

[0058] 8 to 12 parts of rubber,

[0059] 6-10 parts of bio-based polypentamethylene adipate polymer,

[0060] 20-30 parts of degradable organic matter,

[0061] 1 to 1.5 parts of stearic acid,

[0062] 1 to 1.2 parts of zinc oxide,

[0063] 1 to 1.5 parts of peroxide,

[0064] 1-5 parts of AC blowing agent.

[0065] In this embodiment, the degradable organic matter is preferably tapioca flour or cornstarch.

[0066] In this embodiment, the vinyl acetate content in the ethylene-vinyl acetate copolymer is preferably 32.5-36.5%.

[0067] In this embodiment, the POE elastomer is preferably a mixture of ethylene-octene copolymer and ethylene-hexene copolymer.

[0068] In this embodiment, the bio-based polypentamethylene adipate polymer is preferably made of ...

Embodiment 2

[0088] A kind of degradable EVA foaming material, is made of the raw material that comprises following parts by weight:

[0089] 35 parts of ethylene-vinyl acetate copolymer,

[0090] POE elastomer 15 parts,

[0091] 8 parts of rubber,

[0092] Bio-based polypentamethylene adipate polymer 6 parts,

[0093] 20 parts of degradable organic matter,

[0094] 1 part stearic acid,

[0095] Zinc oxide 1 part,

[0096] 1 part peroxide,

[0097] 1 part of AC foaming agent.

[0098] In this embodiment, the degradable organic matter is tapioca flour or corn starch.

[0099] In this embodiment, the content of vinyl acetate in the ethylene-vinyl acetate copolymer is 32.5%.

[0100] In this embodiment, the POE elastomer is a mixture of ethylene-octene copolymer and ethylene-hexene copolymer.

[0101] In this example, the bio-based polypentamethylene adipate polymer is made from petroleum-based adipic acid and bio-based pentamethylene adipate.

[0102] In this embodiment, the peroxi...

Embodiment 3

[0111] A kind of degradable EVA foaming material, is made of the raw material that comprises following parts by weight:

[0112] 45 parts of ethylene-vinyl acetate copolymer,

[0113] POE elastomer 20 parts,

[0114] 12 parts of rubber,

[0115] 10 parts of bio-based polypentamethylene adipate polymer,

[0116] 30 parts of degradable organic matter,

[0117] 1.5 parts of stearic acid,

[0118] Zinc oxide 1.2 parts,

[0119] 1.5 parts peroxide,

[0120] AC blowing agent 5 parts.

[0121] In this embodiment, the degradable organic matter is tapioca flour or corn starch.

[0122] In this embodiment, the content of vinyl acetate in the ethylene-vinyl acetate copolymer is 36.5%.

[0123] In this embodiment, the POE elastomer is a mixture of ethylene-octene copolymer and ethylene-hexene copolymer.

[0124] In this example, the bio-based polypentamethylene adipate polymer is made from petroleum-based adipic acid and bio-based pentamethylene adipate.

[0125] In this embodim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a degradable EVA foam material and a preparation method thereof. The degradable EVA foaming material is prepared from the following raw materials in parts by weight: 35-45 parts of an ethylene-vinyl acetate copolymer, 15-20 parts of a POE elastomer, 8-12 parts of rubber, 6-10 parts of a bio-based polypentamethylene diamine adipate polymer, 20-30 parts of a degradable organic matter, 1-1.5 parts of stearic acid, 1-1.2 parts of zinc oxide, 1-1.5 parts of peroxide and 1-5 parts of an AC foaming agent, wherein the degradable organic matter is tapioca flour or corn starch; the content of vinyl acetate in the ethylene-vinyl acetate copolymer is 32.5%-36.5%; and the POE elastomer is a mixture of an ethylene-octene copolymer and an ethylene-hexene copolymer. The degradableEVA foaming material disclosed by the invention has good wear resistance, high elasticity, good portability, good anti-slip effect, good mechanical properties, favorable comprehensive performance andgood application prospects.

Description

technical field [0001] The invention relates to the technical field of foaming materials, in particular to a degradable EVA foaming material and a preparation method thereof. Background technique [0002] Ethylene-vinyl acetate copolymer (EVA) is a rubber-like thermoplastic. Compared with polyethylene, it has excellent flexibility, low temperature brain flexibility, elasticity, stress crack resistance, good plasticity and processability, so it is widely used. Applications. EVA cross-linked foaming material is a non-toxic foaming material with excellent physical properties. Due to the existence of gas phase, it has the advantages of low density, high specific strength, and ability to absorb loads. However, the EVA foam material has the disadvantages of large deformation, insufficient wear resistance, slipping, and hardening at low temperature, which limit its application. [0003] In recent years, there have been many researches on EVA cross-linked foaming materials at home...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L77/06C08L3/02C08L7/00C08K13/02C08K3/22C08K3/18C08K5/14C08K5/09C08J9/10
CPCC08J9/103C08J9/0095C08J9/0066C08J9/0061C08J9/0023C08J2323/08C08J2423/08C08J2477/06C08J2403/02C08J2407/00C08K13/02C08K2003/2296C08K3/18C08K5/14C08K5/09C08J2203/04
Inventor 丁尤权丁星懿丁雪峰吕方舟林清锴杨文华
Owner 福建安达福新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap