A Vacuum Sintering Process of Cemented Carbide Sawtooth

A cemented carbide and vacuum sintering technology, which is applied in the field of cemented carbide, can solve the problems affecting the performance of cemented carbide sawtooth products, and the sintering filler is not stable enough, so as to achieve good sintering effect, small porosity and stable components.

Active Publication Date: 2022-03-11
OKE PRECISION CUTTING TOOLS CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the mixed powder of alumina and carbon black is usually used as the sintered filler. This sintered filler is not stable enough under vacuum conditions, and it is easy to react with the cemented carbide, which affects the performance of the final cemented carbide saw tooth product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Vacuum Sintering Process of Cemented Carbide Sawtooth
  • A Vacuum Sintering Process of Cemented Carbide Sawtooth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment provides a cemented carbide sawtooth vacuum sintering process, which specifically includes the following steps;

[0030] S1. Mix the tungsten carbide sawtooth blank and the sintered filler with a particle size of 80 mesh evenly. The sintered filler used is obtained by mixing the following components: titanium carbide powder: 89%, zirconia powder: 5%, alumina powder 5%, carbon Black: 1%. After mixing evenly, each cemented carbide sawtooth blank is wrapped by sintered material without contact with each other, and then put into a graphite boat, and the cemented carbide sawtooth blank is not in contact with the graphite boat;

[0031] S2. Put the graphite boat containing the mixed material into a vacuum sintering furnace for sintering. The sintering process parameters are as follows: the temperature is 1400° C., and the time is 120 minutes;

[0032] S3. Sieve the sintered material in the graphite boat through a 20-mesh vibrating sieve to obtain cemented carb...

Embodiment 2

[0034] This embodiment provides a cemented carbide sawtooth vacuum sintering process, which specifically includes the following steps;

[0035] S1. Mix the tungsten carbide sawtooth blank and the sintered filler with a particle size of 60 mesh evenly. The sintered filler used is obtained by mixing the following components: titanium carbide powder: 89%, zirconia powder: 1%, alumina powder 9%, carbon Black: 1%. After mixing evenly, each cemented carbide sawtooth blank is wrapped by sintered material without contact with each other, and then put into a graphite boat, and the cemented carbide sawtooth blank is not in contact with the graphite boat;

[0036] S2. Put the graphite boat containing the mixed material into a vacuum sintering furnace for sintering. The sintering process parameters are as follows: the temperature is 1450° C., and the time is 60 minutes;

[0037] S3. Sieve the sintered material in the graphite boat through a 20-mesh vibrating sieve to obtain cemented carbi...

Embodiment 3

[0039] This embodiment provides a cemented carbide sawtooth vacuum sintering process, which specifically includes the following steps;

[0040] S1. Mix the cemented carbide sawtooth blank and sintered filler with a particle size of 40 mesh evenly. The sintered filler used is obtained by mixing the following components: titanium carbide powder: 89%, zirconia powder: 9%, alumina powder 1%, carbon Black: 1%. After mixing evenly, each cemented carbide sawtooth blank is wrapped by sintered material without contact with each other, and then put into a graphite boat, and the cemented carbide sawtooth blank is not in contact with the graphite boat;

[0041] S2. Put the graphite boat containing the mixed material into a vacuum sintering furnace for sintering. The sintering process parameters are as follows: the temperature is 1400° C., and the time is 80 minutes;

[0042] S3. Sieve the sintered material in the graphite boat through a 20-mesh vibrating sieve to obtain cemented carbide s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a cemented carbide sawtooth vacuum sintering process. By wrapping cemented carbide sawtooth blanks with sintering fillers, sintering fillers are filled between the cemented carbide sawtooth blanks and between the cemented carbide blanks and graphite boats. It can avoid sticking and improve the sintering yield. The sintering filler used in the invention has stable properties and will not react with the cemented carbide blank during vacuum sintering. During vacuum sintering, there is no need to set up a sintering tank, the accommodation space of the boat can be fully utilized, and as many carbide sawtooth blanks and sintering fillers can be loaded as possible, the production efficiency is high, and it is easy to popularize. The cemented carbide sawtooth product prepared by the invention has high hardness and good bending strength, and can well meet cutting requirements.

Description

technical field [0001] The invention relates to the technical field of cemented carbide, and more particularly, relates to a cemented carbide sawtooth vacuum sintering process. Background technique [0002] Tungsten carbide sawtooth, as a cemented carbide tool product, is specially made for cutting and grooving metal materials, and is a common cutting tool for processing. For cemented carbide sawtooth, its cutting performance mainly depends on the quality of cemented carbide. [0003] The manufacturing process of cemented carbide sawtooth mainly includes the steps of mixture preparation, molding and sintering. The sintering process is sintered in a vacuum sintering furnace. In order to prevent cemented carbide sawtooth blanks from sticking to each other during sintering, the pressed hard alloy sawtooth blanks are usually placed on a sintering boat provided with sintering grooves for sintering. For example, a utility model patent with the publication number CN207035826U disc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F3/10B22F5/08
CPCB22F3/1003B22F5/08
Inventor 苏振华黄法袁美和
Owner OKE PRECISION CUTTING TOOLS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com