A kind of self-sharpening structure tungsten alloy material and its preparation method and application

A tungsten alloy and peeling technology, which is applied in the field of peeling self-sharpening structure tungsten alloy materials and its preparation, can solve the problems of limited control level of adiabatic shear performance

Active Publication Date: 2022-05-17
SHENZHEN QIANYAN EQUIP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing methods such as pressureless liquid phase sintering, hot pressing sintering, two-step sintering, and simple plastic deformation have limited control over the adiabatic shear properties of tungsten alloy materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-sharpening structure tungsten alloy material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The invention provides a method for preparing a layer-peeling self-sharpening structure tungsten alloy material, comprising the following steps:

[0021] The mixed powder obtained by mixing tungsten oxide powder, nickel oxide powder and iron oxide powder is subjected to pulse reduction plasma jet treatment and cooling treatment to obtain tungsten-nickel-iron pre-alloyed powder;

[0022] The tungsten-nickel-iron pre-alloyed powder is subjected to four-stage roller forming treatment to obtain plate-shaped tungsten-nickel-iron alloy;

[0023] performing roll bending deformation treatment on the plate-shaped tungsten-nickel-iron alloy to obtain deformed tungsten-nickel-iron alloy;

[0024] The deformed tungsten-nickel-iron alloy is subjected to warm-pressing and densification treatment to obtain a tungsten alloy material with exfoliated self-sharpening structure.

[0025] In the present invention, unless otherwise specified, the raw materials and equipment used are commerc...

Embodiment 1

[0035] (1) In terms of mass percentage, take 92.70% tungsten oxide powder (with a particle size of 2-6 μm), 5.33% nickel oxide powder (with a particle size of 2-6 μm) and 1.97% iron oxide powder (with a particle size of 2-6 μm) and mix evenly, The obtained mixed powder is subjected to pulse reduction plasma jet treatment and cooling treatment to obtain tungsten-nickel-iron pre-alloyed powder; wherein, the operating conditions include: the plasma source is a mixture of argon and hydrogen, and the volume ratio of argon and hydrogen is 6 : 4; the pulse current is 2.3A, and the pulse frequency is 6.8Hz; based on the mass of the mixed powder, the treatment efficiency of the pulse reduction plasma jet treatment is 7s / g; the cooling medium is 3°C circulating water;

[0036] (2) Send the tungsten-nickel-iron pre-alloyed powder into a four-stage roller forming integrated device for forming to obtain a plate-shaped tungsten-nickel-iron alloy; wherein, the operating conditions include: th...

Embodiment 2～8

[0040] According to the method of Example 1, the peeled self-sharpening structure tungsten alloy material is prepared, and the ratio of raw materials and the operating parameters of each step are shown in Table 1 (the operating conditions or parameters not listed in Table 1 are the same as Example 1).

[0041] Raw material proportioning and the operation parameter of each step in the embodiment 1~8 of table 1

[0042]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a layer-peeling self-sharpening structure tungsten alloy material and its preparation method and application, belonging to the technical field of tungsten alloy preparation. In the present invention, the mixed powder obtained by mixing tungsten oxide powder, nickel oxide powder and iron oxide powder is subjected to pulse reduction plasma jet treatment and cooling treatment to obtain tungsten-nickel-iron pre-alloyed powder; the tungsten-nickel-iron pre-alloyed powder is subjected to four-stage Roll forming treatment to obtain plate-shaped tungsten-nickel-iron alloy; rolling deformation of the plate-shaped tungsten-nickel-iron alloy to obtain deformed tungsten-nickel-iron alloy; subjecting the deformed tungsten-nickel-iron alloy to temperature-pressing and densification treatment to obtain a self-sharpening structure Tungsten alloy material. The present invention fully exerts the technical advantages of chemical reduction and plastic deformation by adopting pulse reduction plasma jet technology, four-stage roller forming treatment, roll bending deformation treatment and warm-pressing densification treatment, and can optimize the matching of the strength and plasticity of tungsten alloy materials. The obtained peeled self-sharpening structure tungsten alloy material has better adiabatic shear performance.

Description

technical field [0001] The invention relates to the technical field of tungsten alloy preparation, in particular to a layer-peeling self-sharpening structure tungsten alloy material and its preparation method and application. Background technique [0002] As a structural material, high-density tungsten alloy is mainly used in military fields such as the core of armor-piercing projectiles. The matching of strength and plasticity (adiabatic shear performance) is the key condition for determining the armor-piercing performance of bullets. If the strength is too high and the plasticity is low, it will be brittle during the armor-piercing process. On the contrary, if the strength is low and the plasticity is too high, a "mushroom"-shaped bullet will easily appear, and the bullet will lose its self-sharpening and armor-piercing properties. The existing methods such as pressureless liquid phase sintering, hot pressing sintering, two-step sintering, and simple plastic deformation ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/22B22F3/18B22F3/14C22C27/04
CPCB22F9/22B22F3/18B22F3/14C22C27/04B22F2003/145Y02P10/25
Inventor 董洪峰艾桃桃李文虎
Owner SHENZHEN QIANYAN EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com