Lithium iron phosphate positive plate and environment-friendly low-temperature-resistant lithium battery comprising same

A technology of lithium iron phosphate and positive electrode, which is applied in the field of environment-friendly low-temperature resistant lithium batteries, can solve the problems that limit the wide application of lithium iron phosphate batteries, low energy density of lithium-ion batteries, low tap density and compaction density, and achieve Conducive to conduction and diffusion, improve electrical and thermal conductivity, and high compaction density

Inactive Publication Date: 2020-06-09
广西卓能新能源科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, there are some performance defects in existing iron-lithium lithium-ion batteries, such as very low tap density and compaction density, resulting in low energy density of lithium-ion batteries; poor low-temperature performance, which cannot Make electric vehicles drive; unstable processing performance: The production and processing of lithium iron phosphate requires high humidity in the production environment, and the slurry is prone to thickening after water absorption, resulting in unstable coating surface density, which leads to more problems. For example, the qualified rate of the produced products is lower than 90%, the product consistency is poor, the proportion of safety hazards is high, the cycle performance of 0.5C / 1C is less than 1000 cycles, the weight specific energy is low, and the volume power density is low.
The above problems seriously limit the wide application of lithium iron phosphate batteries in new energy vehicles and other fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium iron phosphate positive plate and environment-friendly low-temperature-resistant lithium battery comprising same
  • Lithium iron phosphate positive plate and environment-friendly low-temperature-resistant lithium battery comprising same
  • Lithium iron phosphate positive plate and environment-friendly low-temperature-resistant lithium battery comprising same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The above-mentioned positive electrode sheet is prepared by the following methods, including:

[0043] 1) Add the formulated amount of aqueous positive electrode slurry and deionized water to the double planetary beater, and stir for 2 hours at a revolution speed of 40-50 revolutions / min and a rotation speed of 1300-1500 revolutions / min to make the first Aqueous cathode slurry;

[0044] 2) Add the above-mentioned first aqueous positive electrode slurry to a high-speed disperser, and disperse it to a viscosity of 5000-8000 mPa.s under the conditions of 3500-4500 revolutions / min to obtain the aqueous positive electrode slurry;

[0045] 3) Coat the water-based positive electrode slurry on aluminum foil with a thickness of 12-16μm, dry it until the moisture content is ≤1%, then roll compaction, and cut according to the width required by the process to obtain the positive electrode sheet;

[0046] An environmentally friendly low-temperature resistant lithium battery, comprising the ...

Embodiment 1-4

[0065] The components were weighed according to the proportions in Table 1, and the positive electrode plates were prepared according to the preparation methods of Examples 1-4.

[0066] Table 1 Example 1-4 Positive electrode composition

[0067]

[0068] Among them, the particle size of lithium iron phosphate is 4-10 μm, and the average particle size is 6 μm.

Embodiment 1

[0071] 1) Add the aqueous cathode slurry and deionized water of the formula in Table 1 into the double planetary beater, and stir for 2 hours under the conditions of revolution speed of 48 revolutions / min and rotation speed of 1400 revolutions / min to make the first aqueous cathode Slurry

[0072] 2) Add the above-mentioned first aqueous positive electrode slurry to a high-speed disperser, and disperse it to a viscosity of 5000 mPa.s under the condition of 3500 revolutions / min to obtain the aqueous positive electrode slurry;

[0073] 3) Coat the water-based positive electrode slurry on a 14μm thick aluminum foil according to the areal density of 300g / ㎡, and dry it until the water content is ≤1%, and then the active material is 2.6g / mm 3 The compaction density is rolled and finally cut into 57mm wide positive electrode sheet.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lithium iron phosphate positive plate. The lithium iron phosphate positive plate comprises an aluminum foil and water-based positive slurry which coats the aluminum foil; thewater-based positive slurry comprises lithium iron phosphate, carbon nanotubes, graphene, chitosan, butadiene styrene rubber, sodium carboxymethyl cellulose, sodium alginate and amino silicone oil; and the particle size of the lithium iron phosphate is 4-10 microns. According to the lithium iron phosphate positive plate of the invention, a positive electrode active substance with large particle size and small specific surface area is adopted, so that the low-temperature performance of the lithium iron phosphate positive plate is good; the environment-friendly water-based positive electrode slurry is adopted, so that the positive electrode plate is environment-friendly, non-toxic, good in processing environment adaptability and stable in processing performance, and the obtained positive electrode plate is high in compaction density, high in specific energy and excellent in low-temperature property. The invention further discloses an environment-friendly low-temperature-resistant lithium battery which comprises the lithium iron phosphate positive plate and is combined with a negative plate with high cost performance, large capacity and high activity, and the obtained lithium iron phosphate battery is good in safety performance, high in energy density, excellent in low-temperature performance, stable in processing performance, free of pollution in the production process and low in battery cost.

Description

Technical field [0001] The present invention relates to the technical field of lithium batteries, in particular to a lithium iron phosphate positive electrode sheet and an environmentally friendly low-temperature resistant lithium battery containing the positive electrode sheet. Background technique [0002] With the development of mobile electronic devices, the demand for batteries is increasing, and higher requirements are put forward for the capacity, voltage, service life and use cost of the batteries. Lithium-ion battery is a kind of secondary battery (rechargeable battery). It mainly relies on the movement of lithium ions between the positive and negative electrodes to work. However, the lithium-ion batteries on the market often have poor safety performance and poor low-temperature performance. There are many shortcomings of low capacity, low capacity per unit volume, low power, and poor cycle performance. Among them, the lithium iron phosphate lithium ion battery is a lit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/136H01M4/58H01M4/62H01M4/1397H01M10/0525
CPCH01M4/136H01M4/1397H01M4/5825H01M4/62H01M4/622H01M4/625H01M10/0525H01M2004/021H01M2004/028Y02E60/10
Inventor 刘国壮邓鸿华许欣凡黄定东江利金
Owner 广西卓能新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products