Diffusion bonding agent for brazing of aluminum alloy honeycomb plate and diffusion brazing method

A technology of diffusion connection and brazing method, which is applied in the direction of welding medium, welding equipment, welding equipment, etc., can solve the problems of non-corrosive properties of materials, reduction of joint strength, intergranular corrosion of solder joints, etc., and achieve the suppression of penetration and diffusion depth , high density, good metallurgical bonding effect

Active Publication Date: 2020-06-09
ZHENGZHOU RES INST OF MECHANICAL ENG CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the self-flux has the following problems: (1) The self-flux material contains ZnCL 2 and SnCL 2 These two strong corrosive components, the material does not have non-corrosive properties; (2) The self-flux material relies on mass transfer with Al at high temperature to precipitate a small amount of Zn, Sn, Ge, etc. to form eutectic Zn-Al solder , to realize the brazing connection of aluminum alloy, the temperature of the connection process is high, and the welding needs to be realized at 570 °C; (3) there is Sn in the connection process, and Sn is easy to cause intergranular corrosion of the solder joints, and reduce the strength of the joint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diffusion bonding agent for brazing of aluminum alloy honeycomb plate and diffusion brazing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A diffusion bonding agent for aluminum alloy honeycomb plate brazing, the mass percentage of each component is: 10% of Si powder with a purity of 99% and a particle size range of 300-400 mesh, and 90% of Ga-In eutectic liquid alloy . Add Si powder into Ga-In eutectic liquid alloy and stir evenly to make a paste-like diffusion bonding agent.

[0024] The preparation method of Ga-In eutectic liquid alloy: prepare Ga and In according to the eutectic composition, slowly add In to Ga in the plastic cup, Ga and In react, and prepare Ga-In eutectic liquid alloy.

Embodiment 2

[0026] A diffusion bonding agent for aluminum alloy honeycomb plate brazing, the mass percentage of each component is: 12% of Si powder with a purity of 99% and a particle size range of 300-400 mesh, and 88% of Ga-In eutectic liquid alloy . Add Si powder into Ga-In eutectic liquid alloy and stir evenly to make a paste-like diffusion bonding agent.

Embodiment 3

[0028] A diffusion bonding agent for aluminum alloy honeycomb plate brazing, the mass percentage of each component is: 15% of Si powder with a purity of 99% and a particle size range of 300-400 mesh, and 85% of Ga-In eutectic liquid alloy . Add Si powder into Ga-In eutectic liquid alloy and stir evenly to make a paste-like diffusion bonding agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
purityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a diffusion bonding agent for brazing of an aluminum alloy honeycomb plate and a diffusion brazing method. The diffusion bonding agent comprises the following components of, by mass, 80%-90% of Ga-In eutectic liquid alloy and 10%-20% of Si powder. The diffusion brazing method comprises the steps of coating the diffusion bonding agent on the to-be-welded surface of a honeycomb core strip and the to-be-welded surfaces of an upper panel and a lower panel, and placing the honeycomb core strip, the upper panel and the lower panel in a mesh belt type continuous brazing furnace for heating after assembling to obtain the aluminum alloy honeycomb plate. By means of the active bonding agent, high-reliability, high-compactness, brazing-filler-free and brazing-flux-free connection between the aluminum alloy honeycomb plates can be achieved.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy honeycomb plate brazing, in particular to a diffusion bonding agent for aluminum alloy honeycomb plate brazing and a diffusion brazing method. Background technique [0002] Aluminum honeycomb panels have the characteristics of low density, high rigidity, good stability, and good sound and heat insulation properties, and are widely used in aerospace, transportation, and architectural decoration. The traditional aluminum honeycomb structure generally adopts the organic colloid bonding process, and the joints can only form a physical bond, so that the performance of the aluminum honeycomb structure is generally restricted by the adhesive, and its application field, working environment and service life are also limited; while the aluminum alloy honeycomb panel Brazing can form a metallurgical bond at the joint, with small deformation and high precision, and the performance of the joint is also ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K20/02B23K35/36
CPCB23K20/026B23K35/3601
Inventor 龙伟民程亚芳张雷丁天然秦建董宏伟黄俊兰刘全明
Owner ZHENGZHOU RES INST OF MECHANICAL ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products