Treatment agent for polyolefin-based synthetic fibers, and polyolefin-based synthetic fiber

A synthetic fiber, polyolefin-based technology, applied in the field of polyolefin-based synthetic fibers, to achieve the effects of excellent initial hydrophilicity and excellent carding machine passability

Active Publication Date: 2020-06-05
TAKEMOTO YUSHI KK
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when polyolefin-based synthetic fibers are produced by a dry process using card rolls (cards) using non-woven fabrics, etc., card passability becomes indispensable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment agent for polyolefin-based synthetic fibers, and polyolefin-based synthetic fiber
  • Treatment agent for polyolefin-based synthetic fibers, and polyolefin-based synthetic fiber

Examples

Experimental program
Comparison scheme
Effect test

no. 1 Embodiment approach

[0025] Hereinafter, 1st Embodiment of the polyolefin-type synthetic fiber processing agent (henceforth a processing agent) which actualized this invention is demonstrated. The processing agent of this embodiment contains the following polyoxyalkylene derivative and the following linear hydrocarbon.

[0026] The polyoxyalkylene derivative is one in which at least one selected from ethylene oxide and propylene oxide is added in a ratio of 5 to 100 moles with respect to 1 mole of aliphatic monohydric alcohol having 24 to 60 carbon atoms. compound.

[0027] The straight-chain hydrocarbon is a straight-chain hydrocarbon having 10 to 100 carbon atoms.

[0028] The polyoxyalkylene derivative used in the treatment agent of this embodiment is a polyoxyalkylene derivative selected from ethylene oxide and A compound of at least one kind of propylene oxide. The aliphatic monohydric alcohol having 24 to 60 carbon atoms is not particularly limited, and examples thereof include tetracosan...

no. 2 Embodiment approach

[0038]Next, a second embodiment of a polyolefin-based synthetic fiber (hereinafter referred to as a synthetic fiber) which is an embodiment of the present invention will be described. The synthetic fiber of this embodiment is a polyolefin type synthetic fiber to which the processing agent of 1st Embodiment adhered. Polyolefin-based synthetic fibers are not particularly limited, and examples thereof include polyolefin-based fibers such as polyethylene fibers, polypropylene fibers, and polybutene fibers. These may be used individually by 1 type, and may use it in combination of 2 or more types. In addition, it is a composite fiber having a core-sheath structure, and either or both of the core and the sheath are polyolefin-based fibers, such as polyethylene / polypropylene composite fibers in which the sheath is polyethylene fibers, polyethylene / polyester Composite fibers, etc.

[0039] The ratio of the treatment agent (excluding the solvent) of the first embodiment to the above-...

Embodiment

[0045] Examples and the like are given below in order to more specifically describe the configuration and effects of the present invention, but the present invention is not limited to these Examples. In addition, in description of a following Example and a comparative example, a part shows a mass part, and % shows a mass %.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

A treatment agent for polyolefin-based synthetic fibers according to the present invention is characterized by comprising a polyoxyalkylene derivative as mentioned below and a linear hydrocarbon compound as mentioned below. The polyoxyalkylene derivative is a compound in which at least one oxide selected from ethylene oxide and propylene oxide is added at a ratio of 5 to 100 moles relative to 1 mole of a monovalent aliphatic alcohol having 24 to 60 carbon atoms. The linear hydrocarbon compound is a linear hydrocarbon compound having 10 to 100 carbon atoms. A polyolefin-based synthetic fiber according to the present invention is characterized by having, attached thereto, the treatment agent for polyolefin-based synthetic fibers.

Description

technical field [0001] The present invention relates to a treatment agent for polyolefin-based synthetic fibers and polyolefin-based synthetic fibers attached with the treatment agent. The treatment agent for polyolefin-based synthetic fibers endows polyolefin-based synthetic fibers with excellent The carded web made of olefin-based synthetic fibers has excellent initial hydrophilicity, durable hydrophilicity, and anti-wetting properties. Background technique [0002] In general, sanitary products such as disposable diapers are known in which polyolefin-based synthetic fibers are coated on the surface of a superabsorbent polymer in order to absorb body fluids. Synthetic fibers coated on the surface of superabsorbent polymers are particularly required: initial hydrophilicity to quickly absorb body fluids, durable hydrophilicity to repeatedly absorb body fluids quickly, and anti-leakage properties to prevent water retained in the superabsorbent polymers from leaking out. Hygr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/53D06M13/17D06M13/184D06M13/224D06M13/256D06M13/262D06M13/292D06M101/20
CPCD06M13/02D06M13/165D06M13/17D06M13/184D06M13/224D06M13/256D06M13/262D06M13/292D06M15/227D06M15/53
Inventor 木村裕森田昌武小室利广
Owner TAKEMOTO YUSHI KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com