A kind of hot-rolled pickled steel strip for 450mpa grade oil well pipe and its manufacturing method

A technology of hot-rolled pickling and manufacturing methods, applied in the direction of manufacturing tools, metal rolling, metal rolling, etc., can solve problems affecting production line production efficiency, reduce production control difficulty, stabilize performance, improve surface finish and Effect of Thickness Dimensional Accuracy

Active Publication Date: 2021-06-15
MAANSHAN IRON & STEEL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, when the invention is pickling a steel strip with a thickness > 3.0mm, the speed is less than 60m / min, which affects the production efficiency of the production line

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hot-rolled pickled steel strip for 450mpa grade oil well pipe and its manufacturing method
  • A kind of hot-rolled pickled steel strip for 450mpa grade oil well pipe and its manufacturing method
  • A kind of hot-rolled pickled steel strip for 450mpa grade oil well pipe and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A method for manufacturing hot-rolled pickled steel strip for 450MPa grade oil well pipes, including slab production, hot rolling and pickling production processes, specifically: converter smelting, LF furnace refining, RH vacuum degassing, continuous casting, heating, high pressure Water descaling, rolling, laminar cooling, coiling, coil uncoiling, welding, loop storage, tension levelling, continuous pickling, rinsing, drying, skin-leveling, trimming, oiling and coiling.

[0038] Among them, the RH vacuum degassing, the end target [H] ≤ 2ppm, the static cycle time ≥ 6min, open the ladle bottom blowing argon for weak stirring after breaking the air, the weak stirring argon flow rate is 10-30NL / min, the weak stirring holding time ≥10min;

[0039]In the continuous casting, the temperature of the tundish is controlled at 15-30° C. above the liquidus line, and the process of light reduction and electromagnetic stirring is adopted. Among them, the reduction position and red...

Embodiment 2- Embodiment 4

[0047] A method for manufacturing a hot-rolled pickled steel strip for 450MPa oil well pipes, except that the process parameters listed in Table 3 and Table 4 are different from those in Example 1, and the rest of the process is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a hot-rolled pickling steel strip for 450MPa grade oil well pipes and its manufacturing method. Through the design of reasonable smelting, continuous casting, hot rolling and pickling processes, three acid pickling strips are designed based on the continuous pickling production unit. The temperature of the acid solution in the tank is uniform, adopting the process of pickling first and then smoothing, the pickling speed can be controlled in a large range, and the production efficiency is high, which can reduce the production preparation time and reduce the difficulty of production control, and the produced tissue is ferrite +Pearlite, hot-rolled pickled steel strip for tubing with stable coil performance and good formability.

Description

technical field [0001] The invention belongs to the technical field of steel production technology for oil well pipes, and in particular relates to a hot-rolled pickling steel strip for 450MPa grade oil well pipes and a manufacturing method thereof. Background technique [0002] The purpose of pickling is to remove the oxide scale on the surface of the strip, trim the edge, and coil to provide raw materials with smooth surface and high dimensional accuracy for the subsequent process. Some continuous pickling production lines are also equipped with a skin pass unit, which can be used to replace the cooling process in some cases. Rolled products, and its energy consumption is much lower than that of cold-rolled products, which meets the requirements of low-carbon and energy-saving, and has a relatively broad space for development. [0003] The patent CN 106862270 A "A production process for thick-gauge hot-rolled pickling plate" published on June 20, 2017 discloses a method fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C21D8/02C21D9/52C21D6/00C22C38/02C22C38/04C22C38/42C22C38/48C23G3/02B21B1/22B21B37/00B21B37/74
CPCB21B1/22B21B37/00B21B37/74B21B2001/225B21B2201/06C21D6/004C21D6/005C21D6/008C21D8/0221C21D9/52C22C33/04C22C38/002C22C38/02C22C38/04C22C38/42C22C38/48C23G3/02
Inventor 杨森胡学文朱涛孙照阳余宣洵王海波游慧超李忠义杨德伦彭正波殷明张杨饶添荣
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com