Phosphorescence Aggregation-Induced Luminescent Materials of Platinum(ii) Complexes Containing Nitrogen-Containing Monodentate Ligands and C^n Bidentate Ligands

A technology of aggregation-induced luminescence and monodentate ligands, which is applied in the direction of luminescent materials, platinum-based organic compounds, platinum-group organic compounds, etc., can solve problems such as the gap in electroluminescent efficiency and achieve important application value effects

Active Publication Date: 2021-07-30
山西绿普光电新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, there are few studies on phosphorescent AIE luminescent materials, and there is still a significant gap between the electroluminescent efficiency and traditional phosphorescent materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorescence Aggregation-Induced Luminescent Materials of Platinum(ii) Complexes Containing Nitrogen-Containing Monodentate Ligands and C^n Bidentate Ligands
  • Phosphorescence Aggregation-Induced Luminescent Materials of Platinum(ii) Complexes Containing Nitrogen-Containing Monodentate Ligands and C^n Bidentate Ligands
  • Phosphorescence Aggregation-Induced Luminescent Materials of Platinum(ii) Complexes Containing Nitrogen-Containing Monodentate Ligands and C^n Bidentate Ligands

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Phosphorescence aggregation-induced luminescent material Pt1 of the platinum (II) complex of the nitrogen-containing monodentate ligand and the C^N bidentate ligand of the present embodiment, the chemical formula is C 20 h 15 ClN 2 Pt, the molecular structure formula is:

[0025]

[0026] refer to figure 1 , the synthesis steps are as follows:

[0027] The first step: 0.2g organic ligand with 0.39g K 2 PtCl 4 Put it into the reaction container, add 24mL of a mixed solvent of ethylene glycol ether and water in a nitrogen atmosphere, the volume ratio of ethylene glycol ether and water in the mixed solvent is 3:1, heat to 85°C in a nitrogen atmosphere, and stir for 8 hours Cool to room temperature, add 50mL deionized water to the reaction tube to precipitate solids, filter, take the filter cake and dry to obtain the intermediate product;

[0028] The second step: put the intermediate product and 0.07g of pyridine into the reaction tube, add 15mL of chloroform un...

Embodiment 2

[0032] The phosphorescent aggregation-induced luminescent material Pt2 of the platinum (II) complex of nitrogen-containing monodentate ligand and C^N bidentate ligand of the present embodiment, chemical formula is C 32 h 23 ClN 2 Pt, the molecular structure formula is:

[0033]

[0034] refer to figure 2 , the synthesis steps are as follows:

[0035] The first step: 0.2g organic ligand with 0.39g K 2 PtCl 4 Put it into the reaction container, add 24mL of a mixed solvent of ethylene glycol ether and water in a nitrogen atmosphere, the volume ratio of ethylene glycol ether and water in the mixed solvent is 3:1, heat to 85°C in a nitrogen atmosphere, and stir for 8 hours Cool to room temperature, add 50mL deionized water to the reaction tube to precipitate solids, filter, take the filter cake and dry to obtain the intermediate product;

[0036] The second step: the intermediate product and Put 0.2g into the reaction tube, add 20mL chloroform under nitrogen atmospher...

Embodiment 3

[0040]Phosphorescence aggregation-induced luminescent material Pt3 of the platinum (II) complex of nitrogen-containing monodentate ligand and C^N bidentate ligand of the present embodiment, chemical formula is C 45 h 36 ClN 3 Pt, the molecular structure formula is:

[0041]

[0042] refer to image 3 , the synthesis steps are as follows:

[0043] The first step: 0.2g organic ligand with 0.31g K 2 PtCl 4 Put it into the reaction container, add 24mL of a mixed solvent of ethylene glycol ether and water in a nitrogen atmosphere, the volume ratio of ethylene glycol ether and water in the mixed solvent is 3:1, heat to 85°C in a nitrogen atmosphere, and stir for 8 hours Cool to room temperature, add 50mL deionized water to the reaction tube to precipitate solids, filter, take the filter cake and dry to obtain the intermediate product;

[0044] The second step: the intermediate product and Put 0.23g into the reaction tube, add 20mL chloroform under nitrogen atmosphere, h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Phosphorescence aggregation-induced luminescent material of nitrogen-containing monodentate ligand and C^N bidentate ligand platinum (II) complex, the general formula of the molecular structure is: the present invention is based on a planar configuration platinum (II) complex, designed Synthesize Pt(C^N)NCl-type phosphorescent AIE molecules, where C^N is a 2‑phenylpyridine bidentate ligand, N is a nitrogen-containing monodentate ligand, and Cl is a chlorine monodentate ligand; on this basis On top of that, adjusting the size of C^N bidentate ligands and nitrogen-containing monodentate ligands can regulate their phosphorescent AIE behavior, and realize new phosphorescent AIE characteristics by using the hindered transition from the planar coordination structure in the ground state to the tetrahedral structure in the excited state in the aggregated state. ; In addition, through the intermolecular interaction, hindering the rotation of the group on the ligand can also inhibit the non-radiative decay of the excited state of the phosphorescent complex and increase the luminescent ability of the aggregated state, thereby achieving the realization of the AIE property. Functional modification, thereby significantly improving the space for performance regulation of platinum (II) complex AIE.

Description

technical field [0001] The invention relates to the technical field of organometallic complex luminescent materials, in particular to phosphorescent aggregation-induced luminescent materials based on platinum (II) complexes of nitrogen-containing monodentate ligands and C^N bidentate ligands of different sizes. Background technique [0002] In 2001, Tang Benzhong and others discovered the aggregation-induced emission (AIE) phenomenon of organic molecules. This kind of organic luminescent molecules exhibits enhanced luminescence characteristics in the solid state, which largely solves the problem of luminescent aggregation quenching that plagues luminescent molecules. Organic light-emitting diode devices require organic light-emitting molecules to have strong light-emitting properties in the solid state. Therefore, aggregation-induced light-emitting organic molecules show great advantages in OLEDs. However, most of the organic light-emitting molecules are fluorescent materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07F15/00C09K11/06
CPCC07F15/0086C09K11/06C09K2211/1007C09K2211/1011C09K2211/1029C09K2211/185
Inventor 周桂江杨华杨晓龙
Owner 山西绿普光电新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap