Preparation method and application of carbon fluoride material

A fluorinated carbon and fluorinated technology, applied in the field of electrochemical energy storage of power supply technology, to achieve the effect of high specific energy and high specific power

Active Publication Date: 2020-05-19
XIAMEN INST OF RARE EARTH MATERIALS
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these methods are difficult to achieve the optimal specific capacity and rate performance of carbon fluoride materials at the same time. How to achieve high specific energy properties while obtaining high specific power performance puts forward requirements for the structural design of carbon fluoride materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of carbon fluoride material
  • Preparation method and application of carbon fluoride material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of carbon fluoride material, comprising the steps of:

[0024] Step 1: According to the mass ratio of the hard carbon raw material sucrose and the soft carbon raw material non-graphitized mesocarbon microspheres as 90%:10%, the non-graphitized mesocarbon microspheres and the non-graphitized mesocarbon microspheres are placed in the Mix in deionized water, add a little ethanol solution, stir evenly, and then sinter in a protective atmosphere at 2500 °C for 24 hours to obtain a pretreated material.

[0025] Step 2: Grinding the pretreated product obtained in step 1 until the particle size reaches below 60 microns, passing through 200 mesh, 400 mesh, and 800 mesh sieve successively to obtain a powdery product.

[0026] Step 3: Put the powder material obtained in Step 2 into the fluorination equipment, pass in fluorinated gas NF3, keep the pressure at 120kPa, and react at 400°C for 8 hours to obtain fluorine containing graphite carbon in the bulk phase ...

Embodiment 2

[0030] A preparation method of carbon fluoride material, comprising the steps of:

[0031] Step 1: According to the mass ratio of the hard carbon raw material sucrose and the soft carbon raw material non-graphitized mesocarbon microspheres as 70%:30%, the non-graphitized mesocarbon microspheres and the non-graphitized mesocarbon microspheres are placed in the Mix in deionized water, add a little ethanol solution, stir evenly, and then sinter in a protective atmosphere at 1500°C for 12 hours to obtain a pretreated material.

[0032] Step 2: Grinding the pretreated product obtained in step 1 until the particle size reaches below 60 microns, passing through 200 mesh, 400 mesh, and 800 mesh sieve successively to obtain a powdery product.

[0033] Step 3: Put the powder material obtained in Step 2 into the fluorination equipment, pass in fluorinated gas NF3, keep the pressure at 90kPa, and react at 350°C for 16 hours to obtain fluorine containing graphite carbon in the bulk phase a...

Embodiment 3

[0036] A preparation method of carbon fluoride material, comprising the steps of:

[0037] Step 1: According to the mass ratio of the hard carbon raw material sucrose and the soft carbon raw material non-graphitized mesocarbon microspheres as 98%: 2%, the non-graphitized mesocarbon microspheres and the non-graphitized mesocarbon microspheres are placed in the Mix in deionized water, add a little ethanol solution, stir evenly, and then sinter in a protective atmosphere at 2800°C for 22 hours to obtain a pretreated material.

[0038] Step 2: Grinding the pretreated product obtained in step 1 until the particle size reaches below 60 microns, passing through 200 mesh, 400 mesh, and 800 mesh sieve successively to obtain a powdery product.

[0039] Step 3: Put the powder material obtained in Step 2 into the fluorination equipment, pass in fluorinated gas NF3, keep the pressure at 100kPa, and react at 450°C for 16 hours to obtain fluorine containing graphite carbon in the bulk phase ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific poweraaaaaaaaaa
Specific poweraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a carbon fluoride material, which comprises the following steps: S1, weighing 70-98 wt% of a hard carbon raw material and 2-30 wt% of a soft carbon rawmaterial, mixing in a solvent, uniformly stirring, and sintering in a protective atmosphere at 1500-2800 DEG C for 1-24 hours to obtain a pretreated material; S2, grinding the pretreated material obtained in the step S1 to prepare a powdery product; and S3, putting the powdery product obtained in the step S2 into fluorination equipment, introducing fluorination gas, keeping the pressure at 90-120kPa, and reacting at 350-450 DEG C for 8-16 hours to obtain the carbon fluoride material. The carbon fluoride material prepared by the invention has high specific power and high specific energy, can realize discharge under the current of 30 A / g, has the specific energy of more than 550 Wh / kg and the specific power of more than 45000 W / kg, and can be applied to a lithium carbon fluoride battery positive electrode material.

Description

technical field [0001] The invention belongs to the field of electrochemical energy storage of power supply technology, and in particular relates to a preparation method and application of a carbon fluoride material. Background technique [0002] When carbon fluoride is used as a cathode material for lithium primary batteries, its theoretical mass specific energy is as high as 2180 Wh kg-1, which is currently the commercial lithium primary battery material with the highest theoretical specific energy. Lithium fluoride batteries are currently widely used in various civilian and military fields such as electronic radio frequency identification systems, cardiac pacemakers, missile ignition systems, small satellites or space weapons, kinetic energy interceptors, and space stations. The specific energy of fluorinated carbon materials is determined by the degree of fluorination of the material. The higher the degree of fluorination, the higher the theoretical specific energy, but ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B32/10H01M4/583H01M6/14
CPCC01P2006/40C01B32/10H01M4/5835H01M6/14
Inventor 岳红军钟贵明陈慧鑫卢灿忠
Owner XIAMEN INST OF RARE EARTH MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com