Water-based ceramic material for inner tank of stainless steel thermos cup and preparation method thereof

A ceramic coating, water-based technology, applied in the direction of coating, etc., can solve the problems that the environmental protection and health of the cup cannot be guaranteed, and achieve the effects of avoiding health problems, delaying heat conduction, and increasing adhesion

Active Publication Date: 2021-09-17
SHANGHAI EXCILON NEW MATERIALS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The Chinese invention patent with the publication number CN201610226583.9 discloses a water-based transparent weather-resistant coating for a thermos cup. The coating uses fluorocarbon emulsion, styrene-acrylic emulsion, hydroxyl acrylic resin and epoxy soybean oil as film-forming substances, and amino resin as The curing agent and film-forming substances are all organic resins, so the environmental protection and health of the cup cannot be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based ceramic material for inner tank of stainless steel thermos cup and preparation method thereof
  • Water-based ceramic material for inner tank of stainless steel thermos cup and preparation method thereof
  • Water-based ceramic material for inner tank of stainless steel thermos cup and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0047] Examples 1 to 3 respectively relate to a water-based ceramic coating for the inner tank of a stainless steel thermos cup, and its composition and dosage by weight are shown in Table 1;

[0048] The preparation process is as follows:

[0049] (1) Grinding color paste: After mixing sol, inorganic pigments, fillers, and deionized water, grind at 1300 rpm to a fineness below 18 μm, control the pH value to >8.2, then add acrylic resin, reduce the speed to 170rmp, and React under alkaline conditions for 45 minutes to obtain the color paste;

[0050] (2) Add acetic acid to the color paste, stir evenly, and control the pH value between 3.9-4.3;

[0051] (3) Continue to add methyltrimethoxysilane, dimethyldiethoxysilane, aminopropyltrimethoxysilane, and hydroxyl silicone oil, react at 180rmp for 6 hours, and let it stand; the water-based ceramic coating is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based ceramic material for the inner tank of a stainless steel thermos cup and a preparation method thereof; 4‑5 parts of methyldiethoxysilane, 2‑3 parts of aminopropyltrimethoxysilane, 16‑18 parts of acrylic resin, 17‑19 parts of inorganic pigments, 6‑7 parts of filler, 0.2‑0.3 parts of hydroxy silicone oil , 2.6-2.9 parts of acetic acid, the balance of deionized water; the sol is a mixture of silica sol and zirconium sol with a mass ratio of 2:1 to 3:1. The ceramic coating of the present invention is sprayed on the inner surface of the stainless steel thermos cup, and the coating thickness is 35-40 μm, which can significantly improve the heat preservation effect of the thermos cup. After pouring boiling water for 6 hours, the water temperature can be kept above 65°C; and the ceramic coating Good adhesion to the substrate, even if the stainless steel substrate is not sandblasted, it can achieve a good adhesion effect only after simple grinding.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based ceramic material for a stainless steel thermos cup inner tank and a preparation method thereof. Background technique [0002] Along with the raising of people's living standard, daily drinking water mode and drinking water cup are also changing. It has developed from traditional enamel jars, glass cups, ceramic cups, purple sand cups and other utensils to stainless steel thermos cups with thermal insulation properties. The stainless steel thermos cup is mainly produced by a combination of inner and outer double-layer stainless steel materials through vacuum technology. The vacuum structure of the stainless steel thermos cup can effectively control the three heat transfer methods of heat conduction, heat convection and heat radiation, so as to achieve the purpose of heat preservation, cold preservation and fresh preservation. It can be used to hold water, tea, cof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D183/08C09D133/04C09D7/63C09D7/61
CPCC08K5/544C08K7/26C09D1/00C09D4/00C09D133/04C09D183/08C09D7/61C09D7/63C09D7/70
Inventor 李力锋陈德义
Owner SHANGHAI EXCILON NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com