Flame-retardant elastic rubber-plastic wave insulation board and preparation method thereof

A thermal insulation board and wave technology, which is applied in the field of flame-retardant elastic rubber-plastic wave thermal insulation board and its preparation, can solve the problems of low flame-retardant performance, decreased elasticity, low rubber-plastic density, etc., and achieve stable product performance, fine cells, The effect of high cell closure rate

Inactive Publication Date: 2020-05-15
WINCELL INSULATION CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing a flame-retardant elastic rubber-plastic corrugated thermal insulation board with high elasticity and high flame retardancy, which effectively solves the problems of low rubber-plastic density, decreased elasticity and low flame-retardant performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A flame-retardant elastic rubber-plastic wave insulation board, comprising the following raw materials according to the mass ratio: 40 parts of EPDM rubber, 20 parts of styrene-butadiene rubber, 5 parts of high-styrene resin, 10 parts of dioctyl sebacate, vulcanized 3 parts of accelerator, 2 parts of active agent, 0.1 part of antioxidant, 5 parts of light stabilizer, 40 parts of composite flame retardant, 0.2 parts of anti-scorch agent PVI, blowing agent-dinitrosopentamethylenetetramine 15 parts, sulfur 0.1 part. The composite flame retardant is molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and lubricant with a mass ratio of 2:9:1:1:1, molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and For the lubricant, the lubricant is stearic acid, zinc stearate and glyceryl stearate with a mass ratio of 1:1:1, and the active agent is zinc oxide.

[0029] A method for preparing a flame-retardant elastic rubber-plastic wave insulation boar...

Embodiment 2

[0040] A flame-retardant elastic rubber-plastic wave insulation board, comprising the following raw materials according to the mass ratio: 50 parts of EPDM rubber, 25 parts of styrene-butadiene rubber, 6 parts of high-styrene resin, 11 parts of dioctyl sebacate, vulcanized 4 parts of accelerator, 4 parts of active agent, 0.2 part of antioxidant, 5 parts of light stabilizer, 45 parts of composite flame retardant, 0.4 part of anti-scorch agent PVI, foaming agent-dinitrosopentamethylenetetramine 18 parts, 0.3 parts of sulfur. The composite flame retardant is molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and lubricant with a mass ratio of 2:9:1:1:1, molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and For the lubricant, the lubricant is stearic acid, zinc stearate and glyceryl stearate with a mass ratio of 1:1:1, and the active agent is zinc oxide.

[0041] A method for preparing a flame-retardant elastic rubber-plastic wave insulation b...

Embodiment 3

[0052] A flame-retardant elastic rubber-plastic wave insulation board, comprising the following raw materials according to the mass ratio: 60 parts of EPDM rubber, 30 parts of styrene-butadiene rubber, 8 parts of high-styrene resin, 12 parts of dioctyl sebacate, vulcanized 5 parts of accelerator, 5 parts of active agent, 0.2 part of antioxidant, 6 parts of light stabilizer, 50 parts of composite flame retardant, 0.5 part of anti-scorch agent PVI, foaming agent-dinitrosopentamethylenetetramine 20 parts, 0.2 parts of sulfur. The composite flame retardant is molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and lubricant with a mass ratio of 2:9:1:1:1, molybdenum trioxide, aluminum hydroxide, zinc borate, antimony oxide and For the lubricant, the lubricant is stearic acid, zinc stearate and glyceryl stearate with a mass ratio of 1:1:1, and the active agent is zinc oxide.

[0053] A method for preparing a flame-retardant elastic rubber-plastic wave insulation b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a flame-retardant elastic rubber-plastic wave thermal insulation material and a preparation method thereof. The flame-retardant elastic rubber-plastic wave thermal insulationmaterial comprises the following raw materials: an ethylene propylene diene monomer, butadiene styrene rubber, high styrene resin, dioctyl sebacate, a vulcanization accelerator, an active agent, an anti-scorching agent, a foaming agent, sulfur, an antioxidant, a light stabilizer and a composite flame retardant. Ethylene-propylene-diene monomer and a composite flame retardant are added; no polar substituent exists in the molecular structure of the ethylene propylene diene monomer; the molecular cohesion is low, a molecular chain can keep flexibility in a relatively wide range, and the flexibility and elasticity of the material are improved; by adding the composite flame retardant, heat can be absorbed to generate a thermal decomposition reaction, the temperature in a condensed phase can bereduced, the thermal decomposition speed of the material can be reduced, and a large number of active hydroxyl free radicals generated in the combustion process can be isolated, so that the flame retardant effect is achieved, and the elasticity and flame retardant property of rubber and plastic products are effectively improved.

Description

technical field [0001] The invention relates to the technical field of rubber and plastic preparation, in particular to a flame-retardant elastic rubber and plastic wave insulation board and a preparation method thereof. Background technique [0002] Rubber and plastic is the collective name of the rubber and plastic industries. They are all subsidiary products of petroleum. With the demand and application of technology and market becoming more and more extensive, the elasticity of rubber and plastic decreases during the use of rubber and plastic. In addition, rubber and plastic insulation The main components of the material are rubber and plastics, which have the common disadvantage of not being resistant to open flames. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing a flame-retardant elastic rubber-plastic corrugated thermal insulation board with high elasticity and high flame retardan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L9/06C08L61/06C08K13/02C08K5/11C08K3/06C08K3/22C08K3/38C08K5/09C08K5/098C08K5/103C08J9/10
CPCC08J9/107C08J9/0023C08J9/0061C08J9/0066C08K2003/2296C08K2003/2227C08K2003/387C08K3/2279C08K2003/2255C08J2203/04C08J2323/16C08J2409/06C08J2461/06C08K13/02C08K5/11C08K3/06C08K5/09C08K5/098C08K5/103
Inventor 秦伯进张君秦天德刘远斌翟必赢谢存剑曹鑫徐乐
Owner WINCELL INSULATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products