Wheel bolt electroplating process

An electroplating process and bolt technology, which is applied in the field of wheel bolt electroplating process, can solve the problems such as the risk of hydrogen embrittlement, and achieve the effects of reducing the risk of hydrogen embrittlement, improving product quality, and reducing production costs

Inactive Publication Date: 2020-04-28
山东九佳紧固件股份有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anticorrosion of the surface of wheel bolts is inseparable from the electroplating process, and the pickling process in electroplating is mainly used to remove oxide skin and oil stains on the surface of parts, which is one of the keys to determine the quality of the coating, but the pickling process will produce hydrogen permeation. risk of hydrogen embrittlement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wheel bolt electroplating process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] In order to clearly illustrate the technical features of the solution, the solution will be described below through specific implementation modes.

[0023] Such as figure 1 As shown, a kind of wheel bolt electroplating process of the present invention comprises the process steps that are carried out in the following order:

[0024] For shot blasting, put the processed and formed bolts into the shot blasting chamber, and the weight of each loading should not exceed 120kg. Too much loading at a time will lead to incomplete removal of the shot blasting scale; the diameter of the steel shot in the shot blasting chamber is 0.1~ 0.2mm, the hardness of the steel shot is 45~50HRC, and the shot blasting time is 5~8min; in the shot blasting process, when the shot blasted bolts are taken out of the shot blasting chamber, the vibration blanking method can be used, and a slope can be set at the blanking port. A vibration motor is installed on the slope. When the vibration motor vib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wheel bolt electroplating process. The process comprises the following process steps of thermal debinding, primary water washing, pre-plating, secondary water washing, electroplating, third water washing, glaring, fourth water washing, passivation, fifth water washing, hot water washing and drying. An electroplated product obtained after shot blasting has the same surface quality and salt fog testing as an electroplated product after acid pickling, a shot blasting product does not need acid pickling, the hydrogen embrittlement risk is reduced, shot blasting does notonly replaces one acid pickling procedure, neutralization and hydrogen removal after acid pickling are not needed, in addition, the production cost can be consumed by waste acid treatment caused by acid pickling, shot blasting is free of the problem, the product quality is improved through process improvement, and in addition, the production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of bolt processing, in particular to the field of bolt electroplating, in particular to a wheel bolt electroplating process. Background technique [0002] Wheel bolts are high-strength bolts used to connect the wheels of vehicles. Generally, they are grade 10.9 for small cars and grade 12.9 for medium and large vehicles. Wheel bolts are the key components connecting the wheels. Once they fail, serious consequences will be caused. Therefore, strict checks must be carried out during the production of bolts. The anticorrosion of the surface of wheel bolts is inseparable from the electroplating process, and the pickling process in electroplating is mainly used to remove oxide skin and oil stains on the surface of parts, which is one of the keys to determine the quality of the coating, but the pickling process will produce hydrogen permeation. There is a risk of hydrogen embrittlement. In order to reduce the ri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D7/00C25D5/36C25D5/10C25D5/48C25D3/22C23C22/06
CPCC23C22/06C25D3/22C25D5/10C25D5/36C25D5/48C25D7/003
Inventor 徐铁成李红梅陈辰
Owner 山东九佳紧固件股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com